Indoor deodorant as well as preparation method and application thereof
A deodorant and dispersant technology, which is applied in the field of indoor deodorant and its preparation, can solve the problems of inability to release, unstable continuous effect, and ineffective treatment of polluted gas, etc., and achieve a rapid and long-lasting deodorizing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0034] A preparation method for indoor deodorant, specifically comprising the following steps:
[0035] (1) After mixing nano titanium dioxide, nano mica powder, acetic acid and citric acid, stir and react at a speed of 500r / min for 35 minutes, wherein the mass ratio of nano titanium dioxide and nano mica powder is 5:2;
[0036] (2) Add deionized water with 4 times the weight of nano-titanium dioxide, then add dispersant sodium pyrophosphate and sodium lauryl sulfate and surfactant alkyl glucoside while stirring, and adjust the pH of the system to be 6-8;
[0037] (3) Join the cationic polymer urea-formaldehyde resin accounting for 80% of the weight of nano-titanium dioxide into the system of step (2), and stir vigorously for 20min at a rotating speed of 2000r / min;
[0038] (4) Add benzene polyphenols, green tea essential oil, and an enzyme mixture of lysozyme, oxidoreductase, cellulase, protease, and lipase with an enzyme activity ≥ 20,000 in sequence, and the amount of the e...
Embodiment 2
[0041] A preparation method for indoor deodorant, specifically comprising the following steps:
[0042] (1) After mixing nano titanium dioxide, nano mica powder, acetic acid and citric acid, stir and react at a speed of 450r / min for 50min, wherein the mass ratio of nano titanium dioxide and nano mica powder is 5:3;
[0043] (2) Add deionized water with 5 times the weight of nano-titanium dioxide, then add dispersant polyacrylamide and surfactant fatty acid sorbitan while stirring, and adjust the pH value of the system to 6-8;
[0044] (3) The cationic polymer polyamide polyamine epichlorohydrin accounting for 85% of the weight of nano-titanium dioxide is added to the system of step (2), and vigorously stirred for 15 min at a rotating speed of 2500r / min;
[0045] (4) Add benzene polyphenols, green tea essential oil, and an enzyme mixture of lysozyme, oxidoreductase, cellulase, protease, and lipase with an enzyme activity ≥ 20,000 in sequence, and the amount of the enzyme mixtur...
Embodiment 3
[0048] A preparation method for indoor deodorant, specifically comprising the following steps:
[0049] (1) After mixing nano titanium dioxide, nano mica powder, acetic acid and citric acid, stir and react at a speed of 450r / min for 60min, wherein the mass ratio of nano titanium dioxide and nano mica powder is 4:3;
[0050](2) Add deionized water with 6 times the weight of nano-titanium dioxide, then add dispersant triethylhexyl phosphoric acid and cellulose derivatives and surfactant polysorbate while stirring, and adjust the pH of the system to be 6-8;
[0051] (3) join the cationic polymer melamine formaldehyde resin that accounts for 75% of the weight of nano-titanium dioxide in the system of step (2), and stir vigorously for 10min at a rotating speed of 3000r / min;
[0052] (4) Add benzene polyphenols, green tea essential oil, and an enzyme mixture of lysozyme, oxidoreductase, cellulase, protease and lipase with an enzyme activity ≥ 20,000 in sequence, and the amount of th...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com