Processing technology of bamboo fibers for seedling culture base fabric

A processing technology, bamboo fiber technology, applied in fiber processing, fiber mechanical separation, bast fiber produced by chemical method, etc., can solve the problems of uneven distribution of fiber thickness, poor mechanical properties, poor degumming effect of bamboo fiber, etc., to achieve fiber The effect of uniform pore distribution, reduced strength, and satisfactory mechanical properties

Inactive Publication Date: 2018-11-02
江西创迪科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the above-mentioned problems in the prior art, the present invention provides a processing technology of bamboo fiber for seedling raising base cloth, so as to overcome the disadvantages of poor degumming effect, uneven distribution of fiber thickness and poor mechanical properties of bamboo fiber in the prior art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Present embodiment provides a kind of processing technique of bamboo fiber for seedling raising base cloth, and its technological process is as follows:

[0025](1) Mechanical pretreatment: the bamboo is repeatedly rolled by rollers for 120 times to obtain a rough material, and then washed with water to initially remove part of the hemicellulose and lignin attached to the surface of the fiber;

[0026] (2) Pre-soaking treatment: Soak the crude material obtained in step (1) in a peracetic acid pre-soaking treatment solution, wherein the concentration of peracetic acid is 4%, the temperature is 65° C., the pH value is 6, and the time is 65 minutes; After completing the pre-soaking process, rinse with water again to obtain bamboo fiber;

[0027] (3) Scouring: the bamboo fiber obtained in step (2) is further scoured, rinsed with 80°C hot water after scalding, and then washed with 20°C cold water; wherein, the bath ratio of scoured is 1: 9. The scouring temperature is 60°C,...

Embodiment 2

[0033] Present embodiment provides a kind of processing technique of bamboo fiber for seedling raising base cloth, and its technological process is as follows:

[0034] (1) Mechanical pretreatment: the bamboo is repeatedly rolled by rollers for 150 times to obtain a rough material, and then washed with water to initially remove part of the hemicellulose and lignin attached to the fiber surface;

[0035] (2) Pre-soaking treatment: Soak the crude material obtained in step (1) in a peracetic acid pre-soaking solution, wherein the concentration of peracetic acid is 4%, the temperature is 70° C., the pH value is 7, and the time is 80 minutes; After completing the pre-soaking process, rinse with water again to obtain bamboo fiber;

[0036] (3) Scouring: the bamboo fiber obtained in step (2) is further scoured, rinsed with 90°C hot water after scalding, and then washed with 30°C cold water; wherein, the bath ratio of scoured is 1: 12. The scouring temperature is 70°C, the scouring t...

Embodiment 3

[0043] Present embodiment provides a kind of processing technique of bamboo fiber for seedling raising base cloth, and its technological process is as follows:

[0044] (1) Mechanical pretreatment: The bamboo is repeatedly rolled by rollers for 180 times to obtain a rough material, and then washed with water to initially remove part of the hemicellulose and lignin attached to the surface of the fiber;

[0045] (2) Pre-soaking treatment: Soak the crude material obtained in step (1) in a peracetic acid pre-soaking solution, wherein the concentration of peracetic acid is 5%, the temperature is 75° C., the pH value is 8, and the time is 90 minutes; After completing the pre-soaking process, rinse with water again to obtain bamboo fiber;

[0046] (3) Scouring: the bamboo fiber obtained in step (2) is further scoured, rinsed with 80-100°C hot water after the scoured, and then washed with 35°C cold water; wherein, the bath ratio of scoured is 1:14, the scouring temperature is 80°C, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a processing technology of bamboo fibers for a seedling culture base fabric. A flow of the processing technology comprises the following steps: after mechanically and repeatedly rolling bamboo wood; carrying out pre-impregnation, scouring, softening, dehydration and drying, and mechanical post-treatment to obtain fine bamboo fibers. According to the processing technology provided by the invention, a good degumming effect is realized by utilizing three flow steps including mechanical pre-treatment, the pre-impregnation and the scouring; especially, scouring liquid prepared by matching acid and alkali with a complex enzyme is used for carrying out degumming treatment on the bamboo fibers; the residual gum rate is relatively low and a technological flow is simple; relatively fine fibers are easy to obtain. Softening and mechanical post-treatment are utilized; furthermore, the fine bamboo fibers are obtained through slow-speed carding, the strength of the bamboo fibers is reduced and the fibers are uniformly distributed, so that the prepared seedling culture base fabric has stable quality and the mechanical properties can meet the utilization requirements of seedling culture and rice seedlings culture very well.

Description

technical field [0001] The invention relates to a processing technology of bamboo fiber, in particular to a processing technology of bamboo fiber for seedling raising base cloth. Background technique [0002] Bamboo fiber is a fiber obtained from various bamboo plants, including the bast fiber of the cortex of annual or perennial herbaceous dicotyledonous plants and the leaf fiber of monocotyledonous plants. [0003] The main component of bamboo fiber is cellulose, followed by hemicellulose, pectin and lignin. The outside of bamboo fiber is covered with gum, which makes the fibers glued to each other. It cannot be directly used to prepare the desired product. Therefore, it must be degummed to release the fiber and be in a separated state. Traditional bamboo fiber degumming mainly involves chemical degumming with caustic soda, using strong acid, strong alkali, high temperature and high pressure cooking, to break the fiber molecular chain and improve the crystallinity, but af...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01C1/02D01B1/10
CPCD01C1/02D01B1/10
Inventor 陈杨
Owner 江西创迪科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com