Electrolytic aluminum ash man-made underfloor heating composite brick and preparation method thereof

An electrolytic aluminum ash system and composite brick technology, which is applied in the fields of manufacturing tools, sustainable waste treatment, solid waste management, etc., can solve the problems of polluting the environment and the lack of comprehensive utilization of useful components, so as to reduce emissions and save energy. Effect

Inactive Publication Date: 2018-09-11
重庆新格有色金属有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the lack of unified technology for social benefits, environmental benefits, and economic benefits, the treatment of aluminum ash in China is still at a relatively primitive stage. The reality is that a considerable part of aluminum ash is buried or discarded without treatment, not only The useful components in aluminum ash cannot be effectively comprehensively utilized, and it also seriously pollutes the environment, which is extremely incompatible with today's concept of green development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrolytic aluminum ash man-made underfloor heating composite brick and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] An electrolytic aluminum ash-based artificial floor heating composite brick of the present invention, the composite brick mainly includes electrolytic aluminum dust collection ash, electrolytic aluminum ash, quartz powder, quartz sand, resin, curing agent, reactant, and silane coupling agent; Wherein electrolytic aluminum dust collection ash accounts for 5% of mass percentage, electrolytic aluminum dust accounts for 32% of mass percentage, quartz powder accounts for 5% of mass percentage, particle diameter is that 10 mesh quartz sand 1 accounts for 12% of mass percentage, particle diameter is The 80-mesh quartz sand II accounts for 16% by mass, the 100-mesh quartz sand III accounts for 10% by mass, the resin accounts for 18% by mass, the curing agent accounts for 0.250% by mass, and the reactant accounts for 10% by mass. 0.25% and the silane coupling agent accounts for 1.5% of the mass percentage.

[0044] The particle size of the electrolytic aluminum dust collecting a...

Embodiment 2

[0071] An electrolytic aluminum ash-based artificial floor heating composite brick of the present invention, the composite brick mainly includes electrolytic aluminum dust collection ash, electrolytic aluminum ash, quartz powder, quartz sand, resin, curing agent, reactant, and silane coupling agent; Wherein electrolytic aluminum dust collection ash accounts for 5% of mass percentage, electrolytic aluminum dust accounts for 32% of mass percentage, quartz powder accounts for 5% of mass percentage, particle diameter is that 10 purpose quartz sand 1 accounts for 10% of mass percentage, particle diameter is The 80-mesh quartz sand II accounts for 18% by mass percentage, the 100-mesh quartz sand III accounts for 10% by mass percentage, the resin accounts for 18% by mass percentage, the curing agent accounts for 0.250% by mass percentage, and the reactant accounts for 10% by mass percentage. 0.25% and the silane coupling agent accounts for 1.5% of the mass percentage.

[0072] The pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses an electrolytic aluminum ash man-made underfloor heating composite brick and a preparation method thereof. The composite brick is mainly prepared from the following componentsin percentage by mass: 0.1-5% of electrolytic aluminum dust collection ash, 18-35% of electrolytic aluminum ash, 1.5-5% of quartz powder, 10-18% of quartz sand I, 16-25% of quartz sand II, 10-25% of quartz sand III, 12-18% of resin, 0.1-0.25% of curing agent, 0.1-0.25% of reaction agent and 0.5-2.5% of silane coupling agent. The prepared composite brick product is green and environmentally friendly, the resources can be recycled, and emission of waste is reduced.

Description

technical field [0001] The invention relates to an artificial composite brick board, in particular to an electrolytic aluminum gray system artificial floor heating composite brick and a manufacturing method thereof. Background technique [0002] Aluminum ash is produced in electrolytic aluminum, secondary aluminum processing and other aluminum processing and production processes. The slag produced in the production process is cooled and processed. It contains aluminum and various valuable elements and is a renewable resource. Its sources can be divided into aluminum ash produced in the process of aluminum electrolytic smelting, aluminum ash in the process of aluminum melting and casting, and aluminum ash in the process of secondary aluminum processing. Aluminum ash is mainly composed of a mixture of metal aluminum, oxides and salt solvents, which contains 10%-30% aluminum and 20%-40% aluminum oxide. If it is not recycled, it will not only waste resources, but also pollute t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/18C04B18/14B28B3/00B28B13/02B28B13/06
CPCB28B3/006B28B13/02B28B13/06C04B18/144C04B26/18C04B2201/50C04B14/06C04B24/42C04B2103/0068Y02W30/91
Inventor 黄耀滨
Owner 重庆新格有色金属有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap