Method for producing non-spangle galvanized plate based on sheet billet continuous casting and rolling heat-based raw material and pickling galvanization continuous production line

A thin slab continuous casting and galvanized sheet technology, which is applied in hot-dip coating process, heat treatment furnace, metal rolling, etc., can solve the problems of shortened service life of the load of the roll system, complicated process flow, and easy deviation of the strip, etc. To achieve uniform structure performance, shorten the process flow, and shorten the length of the rolling line

Active Publication Date: 2018-09-04
RIZHAO BAOHUA NEW MATERIAL CO LTD
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The thickness of traditional hot-based galvanizing raw materials below 2.0mm is the limit thin specification for hot rolling, the output is small, it cannot be mass-produced, the shape of the plate is not easy to control, and the thickness is uneven;
[0005] Cold-based products need to be processed by cold rolling and annealing processes. The process is complex and costly, and the cold-based raw materials with a thickness of more than 2.0mm are galvanized. The process speed is slow, the thickness of the zinc layer is not uniform, and there are many quality defects; The difficulty is high, and the strip steel is easy to run off and cause downtime accidents; the thick-gauge strip steel requires high tension in the whole line, and the heavy load of the roller system shortens the service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing non-spangle galvanized plate based on sheet billet continuous casting and rolling heat-based raw material and pickling galvanization continuous production line
  • Method for producing non-spangle galvanized plate based on sheet billet continuous casting and rolling heat-based raw material and pickling galvanization continuous production line
  • Method for producing non-spangle galvanized plate based on sheet billet continuous casting and rolling heat-based raw material and pickling galvanization continuous production line

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] DX51D+Z galvanized sheet

[0049] The process steps are: continuous casting and rolling of full-endless thin slab → pickling → leveling → heating → spangle-free galvanizing → skin pass → passivation → coiling into spangle-free hot-dip galvanized coil

[0050] The composition of the thin slab continuous casting and rolling heat-based raw material is: C≤0.06, Si≤0.044, Mn.08-0.20, P≤0.017, S≤0.006, Alt0.015-0.050, B0.0009-0.0025, thin plate Billet continuous casting and rolling thermal base material thickness: 0.8mm ~ 6.0mm.

[0051] The above steps of continuous casting and rolling of full endless thin slabs are as follows: the continuous casting slab produced by the continuous casting machine directly enters the large-reduction rolling mill, and is rolled to a 12mm intermediate slab, heated to 1150°C by an induction heating furnace, descaled under high pressure, and then Enter the finishing mill for finishing rolling. After finishing rolling, the temperature: 850±20℃, ...

Embodiment 2

[0060] Steel type: SGHC

[0061] The process steps are: continuous casting and rolling of full-endless thin slab → pickling → leveling → heating → spangle-free galvanizing → skin pass → passivation → coiling into spangle-free hot-dip galvanized coil

[0062] The composition of the thin slab continuous casting and rolling heat-based raw material is: C≤0.06, Si≤0.044, Mn.08-0.20, P≤0.017, S≤0.006, Alt0.015-0.050, B0.0009-0.0025, thin plate Billet continuous casting and rolling thermal base material thickness: 0.8mm ~ 6.0mm.

[0063] The above-mentioned steps of continuous casting and rolling of full endless thin slabs are as follows: the continuous casting slab produced by the continuous casting machine directly enters the large-reduction rolling mill, and is rolled to a 15mm intermediate slab, heated to 1200°C by an induction heating furnace, and then descaled under high pressure, and then Enter the finishing mill for finishing rolling. After finishing rolling, the temperature...

Embodiment 3

[0072] S350GD+Z

[0073] The process steps are: continuous casting and rolling of full-endless thin slab → pickling → leveling → heating → spangle-free galvanizing → skin pass → passivation → coiling into spangle-free hot-dip galvanized coil

[0074] The composition of the thin slab continuous casting and rolling heat-based raw material is: C≤0.06, Si≤0.044, Mn.08-0.20, P≤0.017, S≤0.006, Alt0.015-0.050, B0.0009-0.0025, thin plate Billet continuous casting and rolling thermal base material thickness: 0.8mm ~ 6.0mm.

[0075] The above steps of continuous casting and rolling of full endless thin slabs are as follows: the continuous casting slab produced by the continuous casting machine directly enters the large-reduction rolling mill, and is rolled to a 10mm intermediate slab, heated to 1200°C by an induction heating furnace, descaled under high pressure, and then Enter the finishing mill for finishing rolling. After finishing rolling, the temperature: 850±20℃, laminar flow coo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for producing a non-spangle galvanized plate based on sheet billet continuous casting and rolling heat-based raw material and a pickling galvanization continuous production line. The method comprises the following steps of totally-headless sheet billet continuous casting and rolling, pickling, smoothing, heating, non-spangle galvanization, finishing, passivation and coiling to form a non-spangle hot-galvanized roll. By means of the method, the non-spangle continuous pickling hot-galvanized plate with the specification being (0.8-4.0)*(900-1650) mm is producedin a hot rolling manner, the technological process is shortened, energy is saved, a product is good in surface quality, high in size precision and stable in performance, the production cost is lowered, parts of cold-rolling base material galvanized products can be replaced by the product, and the blank of heat-based continuous pickling galvanizing production is filled up.

Description

technical field [0001] The invention relates to the field of galvanized sheet production, and more specifically relates to a method for producing spangle-free galvanized sheets based on thin slab continuous casting and rolling hot-based raw materials and pickling and galvanizing continuous production lines. Background technique [0002] At present, there are more than 600 hot-dip galvanizing medium and wide band production lines in China, with an annual production capacity of more than 100 million tons. Most of the production lines are galvanized products with spangles, and cold-rolled galvanized products are mostly used as the base material for thin-gauge galvanized products. [0003] Hot-dip galvanized sheets are mainly made of hot-based raw materials (above 2.0mm) and cold-based raw materials (below 2.0mm), and the main processes are hot rolling → pickling → heating → galvanizing → passivation → coiling and hot rolling → acid Washing→cold rolling→annealing→galvanizing→pas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21C37/02B21B1/46C23C2/06C23C2/40C23C2/02C23C22/00C21D9/46C22C38/02C22C38/04C22C38/06
CPCB21B1/463B21C37/02C21D9/46C22C38/002C22C38/02C22C38/04C22C38/06C23C2/02C23C2/06C23C2/40C23C22/00
Inventor 王慧凯王学伦张波郑志刚周城连晓磊郭久明徐帅汲广桥胡新杰生西鹏
Owner RIZHAO BAOHUA NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap