Method for transferring graphene through low liquid level tension wet process

A liquid surface tension, wet transfer technology, applied in the direction of graphene, nano-carbon, etc., can solve the problems of insoluble PMMA, affecting the electron mobility of graphene, and more residues, so as to improve the transfer efficiency, reduce the transfer cost and price. low cost effect

Inactive Publication Date: 2018-08-28
ZHEJIANG UNIV
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The liquid phase corrosion method mainly has the following problems: serious impurities remain, and PMMA will react with the corrosion solution, causing PMMA in some areas to be difficult to be dissolved by organic solvents, resulting in incomplete removal of PMMA and more residues, which seriously affect the electronic properties of graphene. Mobility, which reduces the electrical performance of devices made of graphene

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for transferring graphene through low liquid level tension wet process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] This embodiment is illustrated by transferring a 2*2CM graphene-copper foil sample as an example, so the amount of the etching solution and the selection of the container are all selected according to the specification of 2*2CM. But actually it is not limited to the dimensions described in this embodiment.

[0027] A kind of polymer-free wet transfer graphene method, comprises the following steps:

[0028] Step 1. Use isopropanol to clean the surface impurities of the 2*2CM graphene / copper foil sample, and dry the surface of the sample with isopropanol after cleaning.

[0029] Step 2. Use a glass petri dish with a capacity of 50ml to load 40ml of FeCl with a concentration of 1 mole per liter 3 solution. And float a floating frame, the outer frame size of the floating frame is 3*3cm, the inner frame size of the floating frame is 2.5*2.5cm, and the glass frame with a thickness of 1mm makes the liquid level of the solution inside the frame bulge.

[0030] Step 3. Add 1m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for transferring graphene through a low liquid level tension wet process. The method comprises the following steps: washing a copper foil with the graphene and dryingby blowing; preparing a corrosion solution; adding the corrosion solution into a container, and generating a bulge on a liquid level of the corrosion solution to form a convex liquid level; dropwise adding heptane on a graphene-copper foil and completely covering the surface of the graphene with the heptane; enabling the graphene-copper foil with a heptane layer to float on the convex liquid levelof the corrosion solution, wherein the copper foil and the corrosion solution are located on the liquid level and the graphene is located on the copper foil; dropwise adding the heptane into the corrosion solution; after the copper foil is completely dissolved, horizontally an oxidization layer of a substrate above the graphene; slowly pressing the substrate to the graphene until the graphene isin sufficient contact with the substrate; attaching the graphene on the substrate to form a graphene-substrate; obtaining the graphene-substrate and washing; drying to obtain the clean graphene-substrate. According to the method disclosed by the invention, the graphene can be completely transferred and impurities are not introduced.

Description

technical field [0001] The invention belongs to the field of graphene transfer, in particular to a method for wet transfer of graphene without polymer protection. Background technique [0002] Graphene, a new type of two-dimensional thin-film carbon material, has rapidly set off a wave of graphene research in the world because of its excellent properties beyond many materials. So far, the preparation methods of graphene and the research on its mechanical, electrical, chemical and other aspects have made very good progress. However, if graphene is to be applied to other devices, it is necessary to use the CVD method to grow large-scale continuous graphene films, but the graphene grown by the CVD method cannot be used directly on the copper substrate, so a corresponding transfer method is required to transfer the graphene onto the target substrate. [0003] The traditional transfer method is also called liquid-phase corrosion method, and its specific transfer process is: 1. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B32/184
Inventor 赵沛王宏涛徐晨汪洋尹少骞
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products