A kind of preparation method of fuel cell catalyst with low PT load using MOF as template

A fuel cell and catalyst technology, applied in battery electrodes, circuits, electrical components, etc., can solve the problems of limited application, achieve the effects of reducing growth and migration, slowing down migration and agglomeration, and improving quality and activity

Active Publication Date: 2020-10-16
WUHAN UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although non-noble metal catalysts have high activity and certain stability, there is still a certain gap between the ORR performance of general non-noble metal electrocatalysts and Pt-based catalysts in acidic working environments, which limits the performance of non-noble metal electrocatalysts in acidic environments. Applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of fuel cell catalyst with low PT load using MOF as template
  • A kind of preparation method of fuel cell catalyst with low PT load using MOF as template
  • A kind of preparation method of fuel cell catalyst with low PT load using MOF as template

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of preparation method of the fuel cell catalyst with low Pt loading of MOF as template, comprises the following steps:

[0032] Step 1) Preparation of MOF template: Cobalt nitrate, 2-aminoterephthalic acid and triethylenediamine (concentration ratio=1:0.7:0.7) were dispersed in N,N-dimethylformamide (DMF) to form MOF precursor mixed solution, transfer the above mixed solution to a high-pressure reactor, and use the solvothermal method to stand in an oven at 110-130°C for 24-48 hours, then collect the MOF crystal precipitate, and centrifuge and wash the MOF precipitate three to five times. Vacuum drying to obtain MOF powder for later use;

[0033] Step 2) Pt loading on MOF template: Add MOF powder to 0.01-0.2mol / L sodium chloroplatinate ethanol solution and stir for 20-60min, then let it stand at 0-10℃ for 24h, take it out, and wash it by centrifugation for three After five times, the MOF material impregnated with Pt was obtained by vacuum drying;

[0034] Step ...

Embodiment 2

[0040] A kind of preparation method of the fuel cell catalyst with low Pt loading of MOF as template, comprises the following steps:

[0041] Step 1) Preparation of MOF template: Cobalt nitrate, 2-aminoterephthalic acid and triethylenediamine (concentration ratio=1:1:0.5) were dispersed in N,N-dimethylformamide (DMF) to form MOF precursor mixed solution, transfer the above mixed solution to a high-pressure reactor, and use the solvothermal method to stand in an oven at 110-130°C for 24-48 hours, then collect the MOF crystal precipitate, and centrifuge and wash the MOF precipitate three to five times. Vacuum drying to obtain MOF powder for later use;

[0042] Step 2) Pt loading on MOF template: Add MOF powder to 0.01-0.2mol / L sodium chloroplatinate ethanol solution and stir for 20-60min, then let it stand at 0-10℃ for 24h, take it out, and wash it by centrifugation for three After five times, vacuum dry for later use;

[0043] Step 3) Preparation of catalyst with low Pt loadi...

Embodiment 3

[0045] A kind of preparation method of the fuel cell catalyst with low Pt loading of MOF as template, comprises the following steps:

[0046] Step 1) Preparation of MOF template: Cobalt nitrate, 2-aminoterephthalic acid and triethylenediamine (concentration ratio=1:1:0.7) were dispersed in N,N-dimethylformamide (DMF) to form MOF precursor mixed solution, transfer the above mixed solution to a high-pressure reactor, and use the solvothermal method to stand in an oven at 110-130°C for 24-48 hours, then collect the MOF crystal precipitate, and centrifuge and wash the MOF precipitate three to five times. Vacuum drying to obtain MOF powder for later use;

[0047] Step 2) Pt loading on MOF template: Add MOF powder to 0.01-0.2mol / L sodium chloroplatinate ethanol solution and stir for 20-60min, then let it stand at 0-10℃ for 24h, take it out, and wash it by centrifugation for three After five times, vacuum dry for later use.

[0048] Step 3) Preparation of catalysts with low Pt load...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a low Pt loading capacity type fuel battery catalyst by utilizing MOF as a template. The method comprises the following steps: dispersing cobalt nitrate, 2-aminoterephthalic acid and triethylene diamine in N,N-dimethyl formamide to obtain an MOF precursor mixing solution; preparing MOF according to a solvent heating method; washing; drying to obtainMOF powder; adding to a sodium chloroplatinate or chloroplatinic acid solution; stirring; dissolving; allowing standing still; washing; drying; performing high-temperature treatment and pickling underinsert atmosphere; centrifugally washing and drying the product; grinding to obtain the low Pt loading capacity type fuel battery catalyst. The method has the following advantages and beneficial effects: the Pt content in the catalyst is obviously decreased, so that the problem of high cost of the catalyst of a current fuel battery can be solved; low Pt loading capacity type catalyst is outstanding in catalyzing activity; the quality activity of the Ptd is increased by 2-5 times when being compared with that of the conventional commercial Pt / C catalyst.

Description

technical field [0001] The invention relates to the field of fuel cell catalysts, in particular to a method for preparing a low-Pt-loaded fuel cell catalyst using MOF as a template. Background technique [0002] Hydrogen fuel cell is the use of hydrogen and fuel cells to generate electricity. As a true zero-pollution, zero-emission energy conversion tool, it is an inevitable direction for future new energy vehicles. Fuel cells not only have broad application prospects in automobiles and other vehicles, but also will be widely used in our daily life. Although there is still a long way to go before the maturity and large-scale popularization and application of fuel cell technology, there are reasons to believe that new energy fuel cell technology will bring earth-shaking changes to our social and economic life in the near future. [0003] The study of efficient and low-cost cathodic oxygen reduction (ORR) electrocatalysts in the development of fuel cells has been a long-stand...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/92B82Y30/00
CPCB82Y30/00H01M4/926Y02E60/50
Inventor 郭伟邢以晶李赏朱从懿潘牧
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com