A method and application of polysilicate titanium flocculant prepared from cold-rolled titanium plate pickling waste liquid

A technology of pickling waste liquid and polysilicate titanium, which is applied in chemical instruments and methods, flocculation/sedimentation water/sewage treatment, water/sludge/sewage treatment, etc., can solve the problem of poor flocculation effect of flocculant and difficult treatment , toxicity and other issues, to achieve high turbidity removal rate, reduce preparation cost and obvious effect

Active Publication Date: 2021-05-14
KUNMING UNIV OF SCI & TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the problems that the existing cold-rolled titanium plate pickling waste liquid is not easy to handle and the existing flocculant has poor flocculation effect and is toxic, the present invention provides a method for preparing polysilicate titanium flocculant by using the cold-rolled titanium plate pickling waste liquid Method and application, the synthesis method of the polysilicate titanium flocculant of the present invention is simple and fast, does not need to add additional pure substances such as titanium salt to introduce Ti 4+ , and it can be prepared at normal temperature, and the preparation conditions are mild; and the present invention utilizes the Ti in the pickling waste liquid of cold-rolled titanium plate to the greatest extent 4+ At the same time, the acidity of titanium-containing waste liquid also improves the stability of activated silicic acid. The polysilicate titanium flocculant prepared by the invention is non-toxic, the flocs formed are large, and the sweeping effect is strong, and the turbidity removal effect when treating simulated river water Good and does not increase the color of the water

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method and application of polysilicate titanium flocculant prepared from cold-rolled titanium plate pickling waste liquid
  • A method and application of polysilicate titanium flocculant prepared from cold-rolled titanium plate pickling waste liquid
  • A method and application of polysilicate titanium flocculant prepared from cold-rolled titanium plate pickling waste liquid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1: A kind of method that utilizes cold-rolled titanium plate pickling waste liquor to prepare polysilicate titanium flocculant, concrete steps are as follows:

[0025] (1) Na 2 SiO 3 Dissolved in deionized water to make Na 2 SiO 3 solution; where Na 2 SiO 3 The mass fraction of silicon dioxide in the solution is 5.35%;

[0026] (2) Add the stabilizer (the stabilizer is acetic acid) to the dilute sulfuric acid solution and mix evenly to obtain the stabilizer-sulfuric acid solution; the mass percentage concentration of the dilute sulfuric acid solution is 15.0%, and the stabilizer (acetic acid) in the stabilizer-sulfuric acid solution The mass percentage concentration is 3.3%;

[0027] (3) Add the stabilizer-sulfuric acid solution obtained in step (2) dropwise to the Na obtained in step (1) 2 SiO 3 Solution, activated at room temperature and a stirring speed of 400 r / min for 4 hours to obtain a polysilicic acid solution; wherein the stabilizer-sulfuric ...

Embodiment 2

[0032] Embodiment 2: A kind of method that utilizes cold-rolled titanium plate pickling waste liquor to prepare polysilicate titanium flocculant, concrete steps are as follows:

[0033] (1) Na 2 SiO 3 Dissolved in deionized water to make Na 2 SiO 3 solution; where Na 2 SiO 3 The mass fraction of silicon dioxide in the solution is 1.95%;

[0034] (2) Add the stabilizer (the stabilizer is acetic acid) to the dilute sulfuric acid solution and mix evenly to obtain the stabilizer-sulfuric acid solution; the mass percentage concentration of the dilute sulfuric acid solution is 30.0%, and the stabilizer (acetic acid) in the stabilizer-sulfuric acid solution The mass percentage concentration is 1.3%;

[0035] (3) Add the stabilizer-sulfuric acid solution obtained in step (2) dropwise to the Na obtained in step (1) 2 SiO 3 Solution, activated at room temperature and a stirring speed of 200 r / min for 1 h to obtain a polysilicate solution; wherein the stabilizer-sulfuric acid sol...

Embodiment 3

[0040] Embodiment 3: A kind of method that utilizes cold-rolled titanium plate pickling waste liquor to prepare polysilicate titanium flocculant, concrete steps are as follows:

[0041] (1) Na 2 SiO 3 Dissolved in deionized water to make Na 2 SiO 3 solution; where Na 2 SiO 3 The mass fraction of silicon dioxide in the solution is 3.95%;

[0042] (2) Add the stabilizer (the stabilizer is acetic acid) to the dilute sulfuric acid solution and mix evenly to obtain the stabilizer-sulfuric acid solution; the mass percentage concentration of the dilute sulfuric acid solution is 20.0%, and the stabilizer (acetic acid) in the stabilizer-sulfuric acid solution The mass percentage concentration is 4.6%;

[0043] (3) Add the stabilizer-sulfuric acid solution obtained in step (2) dropwise to the Na obtained in step (1) 2 SiO 3 solution, at room temperature, the stirring speed is 300 r / min under the conditions of activation reaction 2h to obtain polysilicic acid solution; wherein th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method and application for preparing a polysilicate titanium flocculant by using waste pickling liquid of a cold-rolled titanium plate, and belongs to the fields of environmental science and safety science. The present invention will Na 2 SiO 3 Dissolved in deionized water to make Na 2 SiO 3 solution; Stabilizer is added to dilute sulfuric acid solution and mixed to obtain stabilizer-sulfuric acid solution; Na 2 SiO 3 Add the solution dropwise to the stabilizer-sulfuric acid solution, and react at room temperature and under stirring conditions for 1 to 5 hours to obtain a polysilicic acid solution; add the polysilicic acid solution to the cold-rolled titanium plate pickling waste solution, React for 0.1~3h to get polysilicate titanium flocculant. The polysilicate titanium flocculant prepared by the method of the invention can effectively trap and sink suspended solids in simulated rivers, and purify water quickly and efficiently; it can also be used for removing chromium from electroplating wastewater; and removing nitrogen, phosphorus and COD from organic wastewater.

Description

technical field [0001] The invention relates to a method and application for preparing a polysilicate titanium flocculant by using waste pickling liquid of a cold-rolled titanium plate, and belongs to the technical field of material synthesis and energy. Background technique [0002] Flocculation and sedimentation is a pretreatment method widely used in water treatment. The flocculant used in the early stage is activated silicic acid, which can produce adsorption bridging and net trapping and sweeping effects to adsorb destabilized micro colloidal particles, and finally gather into a net-like floc. The colloidal particles in a part of the water are swept by the coil to settle together, thereby purifying the water. But it has disadvantages such as easy to freeze and difficult to add. [0003] Cold-rolled titanium plate pickling waste liquid is highly acidic, Ti 4+ If the content is high, if it is discharged directly without treatment, it will pollute the environment and ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C02F1/52C02F101/16C02F101/22C02F101/30
CPCC02F1/5236C02F2101/16C02F2101/22C02F2101/30
Inventor 李雪张英杰许斌黄雪松王少鹏董鹏徐明丽林艳
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com