Whole-growing-season phosphorus and potassium compound fertilizer for tobaccos and preparation method thereof

A full growth period, compound fertilizer technology, applied in the field of tobacco chemical fertilizers, can solve the problems of low potassium content in soil phosphorus-enriched tobacco leaves, low utilization rate of phosphorus fertilizer and potassium fertilizer in flue-cured tobacco, etc., to prolong supply time, improve utilization rate, and reduce soil The effect on the risk of phosphorus pollution

Inactive Publication Date: 2018-07-27
HUNAN AGRICULTURAL UNIV
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of phosphorus-potassium compound fertilizer in the whole growth period of tobacco and its preparation method, so as to solve the problems of low utilization rate of phosphorus fertilizer and potassium fertilizer in flue-cured tobacco, enrichment of soil phosphorus and low content of potassium in tobacco leaves

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Whole-growing-season phosphorus and potassium compound fertilizer for tobaccos and preparation method thereof
  • Whole-growing-season phosphorus and potassium compound fertilizer for tobaccos and preparation method thereof
  • Whole-growing-season phosphorus and potassium compound fertilizer for tobaccos and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A preparation method of phosphorus and potassium compound fertilizer in the whole growth period of tobacco, comprising the following steps:

[0021] (1) Harvest the green scallops that have entered the full flowering stage, cut them into small sections of 5-8cm after drying, carry out low-temperature carbonization in a carbonization furnace at 350 degrees, crush them, and pass through a 150-mesh sieve to make potassium-rich green scallops Biochar;

[0022] (2) Harvest the plants that have entered the full flowering stage and cut them into small sections of 5-8cm. Mix the green pea and rapeseed cakes in a weight ratio of 2:3, add 0.1% fermented bacteria to ferment, ferment for 40 days, and crush 1. Pass through a 150-mesh sieve to make potassium-rich decomposed green scorpion-rapeseed cake fertilizer;

[0023] (3) After drying the tobacco rods from which the tobacco leaves have been removed, crush them into small pieces of 2-4 cm in length, carry out low-temperature car...

Embodiment 2

[0029] A preparation method of phosphorus and potassium compound fertilizer in the whole growth period of tobacco, wherein the first four steps are the same as in Example 1, and all the other steps are:

[0030] A. Preparation of organic components: Weigh 100kg of green beetroot biomass carbon, 300kg of decomposed green beetroot-rapeseed cake fertilizer, 100kg of tobacco stem biomass carbon, 10kg of phosphorus-solubilizing bacteria, 10kg of potassium-solubilizing bacteria, and 10kg of attapulgite soil, and mix well Granulate after uniformity, the particle size is 2-5mm;

[0031] B. Preparation of inorganic components: Weigh 50 kg of silicon-phosphate fertilizer, 150 kg of potassium sulfate, 80 kg of silicon-potassium fertilizer, and 5 kg of attapulgite, and granulate after fully mixing, with a particle size of 2-5 mm, to obtain inorganic component 1; Take 50kg of ammonium polyphosphate, 150kg of ammonium nitrate, 50kg of medical stone, and 10kg of attapulgite, mix them evenly,...

Embodiment 3

[0034] A preparation method of phosphorus and potassium compound fertilizer in the whole growth period of tobacco, wherein the first four steps are the same as in Example 1, and all the other steps are:

[0035] A. Preparation of organic components: Weigh 100kg of green beetroot biomass carbon, 300kg of decomposed green beetroot-rapeseed cake fertilizer, 100kg of tobacco stem biomass carbon, 10kg of phosphorus-solubilizing bacteria, 10kg of potassium-solubilizing bacteria, and 10kg of attapulgite soil, and mix well Granulate after uniformity, the particle size is 2-5mm;

[0036] B. Preparation of inorganic components: Weigh 50 kg of silicon-phosphate fertilizer, 150 kg of potassium sulfate, 80 kg of silicon-potassium fertilizer, and 5 kg of attapulgite, and granulate after fully mixing, with a particle size of 2-5 mm, to obtain inorganic component 1; Take 50kg of ammonium polyphosphate, 150kg of ammonium nitrate, 50kg of medical stone, and 10kg of attapulgite, mix them evenly,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides whole-growing-season phosphorus and potassium compound fertilizer for tobaccos. The whole-growing-season phosphorus and potassium compound fertilizer is prepared from an organiccomponent prepared from feather cockscomb biomass carbon, composted feather cockscomb-rapeseed cake fertilizer, tobacco stem biomass carbon, phosphorus-dissolving bacteria, potassium-dissolving bacteria and attapulgite, and three inorganic components according to the mass ratio of 1 to (1 to 3), wherein the mass ratio of the inorganic component 1 to the inorganic component 2 to the inorganic component 3 is 1 to (1 to 2) to (1 to 2); the inorganic component 1 is prepared from silicon-phosphorus fertilizer, potassium sulfate, phosphorus humate and the attapulgite; the inorganic component 2 is prepared from ammonium polyphosphate, ammonium nitrate, medical stones and the attapulgite; the inorganic component 3 is prepared from potassium humate, phosphorus humate and the attapulgite. Accordingto the whole-growing-season phosphorus and potassium compound fertilizer for the tobaccos, the problems that the utilization rate of phosphorus fertilizer and potassium fertilizer for baking the tobaccos is low, phosphorus is enriched in soil and the potassium content of tobacco leaves is low are solved.

Description

technical field [0001] The invention belongs to the field of tobacco chemical fertilizers, and in particular relates to a phosphorus and potassium compound fertilizer in the whole growth period of tobacco and a preparation method thereof. Background technique [0002] At present, the source of potassium fertilizer used for tobacco is mainly water-soluble potassium sulfate and potassium nitrate and other chemical potassium fertilizers, which will be lost with rainfall and fixed by the soil, resulting in low utilization rate of potassium fertilizer, insufficient soil potassium supply in the late growth period, and tobacco leaf potassium. The content cannot be improved; there are some patents on the formula of silicon potassium fertilizer, humic acid potassium fertilizer and potassium sulfate, and the compounding of organic potassium fertilizer can reduce potassium fixation, form multiple peaks of potassium supply, and provide partial slow release at the same time Potassium pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C05G3/00C05G3/04C05F17/00C05G3/80
CPCC05B7/00C05F17/00C05G3/80C05G5/12C05B17/00C05C1/00C05D1/00C05D1/02C05D9/00C05F5/002C05F11/02C05F11/08C05G3/00Y02W30/40
Inventor 李强张芸萍向德明黎娟蒲文宣周米良向铁军彭宇张明发孙旭滨周东波
Owner HUNAN AGRICULTURAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com