Light weight thermal insulation dry-mixed mortar

A dry-mixed mortar and light-weight technology, applied in the field of dry-mixed mortar, can solve the problems of easy pulverization, flammability of polystyrene particles, and large water absorption of expanded perlite, so as to enhance the bonding force and improve the thermal insulation performance of the wall , good fire performance

Inactive Publication Date: 2018-07-24
福建三凯建筑材料有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a light-weight thermal insulation dry powder mortar, which can replace cement mortar and mixed mortar and apply it on the rod-shaped wall, so as to solve the problem of large water absorption of expanded perlite, easy pulverization, and easy powdering of polystyrene particles. burning problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light weight thermal insulation dry-mixed mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The lightweight thermal insulation dry powder mortar of the present embodiment includes the following raw materials in parts by weight: 20 parts of gel material, 60 parts of lightweight aggregate and 0.5 part of high-performance polymer additive; the gel material is composed of the following parts by weight of raw materials: powder 20 parts of coal ash and 60 parts of cement; the lightweight aggregate is turpentine vitrified microspheres; the high-performance polymer additive includes the following raw materials: organic silicon resin, hydroxypropyl methylcellulose ether, ethylene-acetic acid Ethylene copolymer dry powder, polycarboxylate superplasticizer dry powder and early strength agent. The weight ratio of the hydroxypropyl methylcellulose ether, ethylene-vinyl acetate copolymer dry powder and early strength agent is 1:2:1.

Embodiment 2

[0029] The lightweight thermal insulation dry powder mortar of the present embodiment includes the following raw materials in parts by weight: 40 parts of gel material, 80 parts of lightweight aggregate and 1.5 parts of high-performance polymer additive; the gel material is composed of the following raw materials in parts by weight: powder 40 parts of coal ash and 80 parts of cement; the lightweight aggregate is turpentine vitrified microspheres; the high-performance polymer additive includes the following raw materials: organic silicon resin, hydroxypropyl methylcellulose ether, ethylene-acetic acid Ethylene copolymer dry powder, polycarboxylate superplasticizer dry powder and early strength agent. The weight ratio of the hydroxypropyl methylcellulose ether, ethylene-vinyl acetate copolymer dry powder and early strength agent is 1:3:1.

Embodiment 3

[0031] The lightweight thermal insulation dry powder mortar of the present embodiment includes the following raw materials in parts by weight: 30 parts of gel material, 70 parts of lightweight aggregate and 1 part of high-performance polymer additive; the gel material is composed of the following parts by weight of raw materials: powder 30 parts of coal ash and 70 parts of cement; the lightweight aggregate is turpentine vitrified microspheres; the high-performance polymer additive includes the following raw materials: organic silicon resin, hydroxypropyl methylcellulose ether, ethylene-acetic acid Ethylene copolymer dry powder, polycarboxylate superplasticizer dry powder and early strength agent. The weight ratio of the hydroxypropyl methyl cellulose ether, ethylene-vinyl acetate copolymer dry powder and early strength agent is 1:2.5:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a light weight thermal insulation dry-mixed mortar, which comprises following raw materials in parts by weight: 20 to 40 parts of cementing material, 60 to 80 parts of light weight aggregate, and 0.5 to 1.5 parts of high performance polymer additive; wherein the cementing material comprises following raw materials in parts by weight: 20 to 40 parts of fly ash and 60 to 80parts of cement; the light weight aggregate is pitchstone vitrified micro beads; and the high performance polymer additive comprises following raw materials: organic silicone resin, hydroxypropyl methyl cellulose ether, VAE dry powder, polycarboxylic acid water reducer dry powder, and an early strength agent. The light weight thermal insulation dry-mixed mortar has the advantages of light weight,thermal insulation property, good fireproof performance, good caking property, good bleeding resistance, aging resistant property, green, environmental friendliness, resistance to biological biting, prolonged service life, high strength, high flexibility, and strong cracking resistant performance.

Description

technical field [0001] The invention relates to dry powder mortar, in particular to a light-weight thermal insulation dry powder mortar. Background technique [0002] Insulation mortar is a kind of pre-mixed dry powder mortar made of various light materials as aggregate, cement as cement, mixed with some modified additives, and mixed by the production enterprise. It is mainly used for building exterior wall insulation, and has the advantages of convenient construction and good durability. Inorganic thermal insulation mortar material thermal insulation system is fireproof and non-combustible. It can be widely used in dense residential buildings, public buildings, large public places, flammable and explosive places, and places with strict fire protection requirements. It can also be used as a fire barrier construction to improve building fire protection standards. There are two main types of thermal insulation mortar on the market: 1. Inorganic thermal insulation mortar (vi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B111/40C04B111/28C04B111/20C04B14/16
CPCC04B28/00C04B2111/20C04B2111/28C04B2111/40C04B2201/20C04B2201/32C04B2201/50C04B18/08C04B14/16C04B24/42C04B24/383C04B24/2623C04B2103/302C04B2103/12
Inventor 张平
Owner 福建三凯建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com