Compound moisturizing maintenance film

A curing film and composite technology, which is applied in the direction of synthetic resin layered products, layered products, chemical instruments and methods, etc., can solve the problem of affecting the appearance and quality of concrete engineering, easily broken during the tearing process, and low strength of non-woven fabrics, etc. problem, to achieve the effect of good moisturizing and maintenance effect, good strength and fast construction speed

Inactive Publication Date: 2018-07-03
长沙水能量新材料有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The inner side of the existing concrete moisturizing and curing film is a hairy non-woven fabric. After the moisturizing and curing film is attached to the concrete surface to complete the curing, the non-woven fabric and the rough concrete surface penetrate into one body, which is not easy to tear off. The strength of the woven fabric is low, and it is easy to break during the tearing process after completion, forming mottled fragments on the surface of the concrete wall, which seriously affects the appearance and quality of the concrete project

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound moisturizing maintenance film
  • Compound moisturizing maintenance film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Such as figure 1 As shown, on the surface of the cement concrete 5, there is a composite moisture-retaining maintenance film pasted, and the composite moisture-retention maintenance film for anti-bonding and easy release is composed of an outer plastic film layer 11, a water-absorbing mixing layer 2, and a composite material layer 3. The inner side of the outer plastic film layer 11 is provided with a water-absorbing mixed layer 2 , and the inner side of the water-absorbed mixed layer 2 is provided with a composite material layer 3 .

[0019] The water-absorbing mixed layer 2 is composed of water-absorbing material 6 and viscous glue 7 . The water-absorbing material 6 can be graft copolymerized products of natural polymers such as starch and cellulose, or polymerized products such as sodium acrylate and methyl methacrylate. The polymer water-absorbing material 6 has super-strong water-absorbing and moisturizing properties, can absorb water hundreds to a thousand times ...

Embodiment 2

[0022] Such as figure 2 As shown, on the surface of the cement concrete 5, there is a composite moisture-retaining maintenance film pasted, and the composite moisture-retention maintenance film for anti-bonding and easy release is composed of an outer plastic film layer 11, a water-absorbing mixing layer 2, and a composite material layer 3. The inner side of the outer plastic film layer 11 is provided with a water-absorbing mixed layer 2 , and the inner side of the water-absorbed mixed layer 2 is provided with a composite material layer 3 .

[0023] The water-absorbing mixing layer 2 consists only of water-absorbing material 6 . The water-absorbing material 6 can be graft copolymerized products of natural polymers such as starch and cellulose, or polymerized products such as sodium acrylate and methyl methacrylate. The composite material layer 3 is composed of a multi-layer film 8 and a multi-layer non-woven fabric 9 by fusing, sewing, hot pressing, or gluing. The outer pla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a compound moisturizing maintenance film which is composed of an outer plastic thin film layer, a water absorbing and mixing layer and a composite material layer, wherein thewater absorbing and mixing layer is arranged on the inner side of the outer plastic thin film layer and is composed of a water absorbing material and sticky glue, the composite material layer is arranged on the inner side of the water absorbing material, and the composite material layer is formed by hot pressing the film and a non-woven fabric. The compound moisturizing maintenance film has the advantages of being stick-preventative, easy to release, good in moisturizing and maintaining effect, high in strength and high in construction speed.

Description

technical field [0001] The invention relates to the technical field of moisturizing and curing films, in particular to a composite moisturizing and curing film. Background technique [0002] The inner side of the existing concrete moisturizing and curing film is a hairy non-woven fabric. After the moisturizing and curing film is attached to the concrete surface to complete the curing, the non-woven fabric and the rough concrete surface penetrate into one body, which is not easy to tear off. The strength of the woven fabric is low, and it is easily broken during the tearing process after completion, forming mottled debris on the surface of the concrete wall, which seriously affects the appearance and quality of the concrete project. Contents of the invention [0003] The object of the present invention is to provide a composite moisturizing and maintenance film in order to overcome the deficiencies of the prior art. [0004] The present invention is achieved through the fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B40/04C04B40/02B32B7/12B32B27/12B32B5/02B32B3/24
CPCC04B40/04B32B3/266B32B5/02B32B7/12B32B27/12B32B2307/304B32B2307/50B32B2307/728C04B40/02
Inventor 袁江
Owner 长沙水能量新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap