Energy-saving thermal-insulation soundproof environment-friendly building mortar and preparation method thereof

A technology for thermal insulation, sound insulation and environmental protection, applied in the field of building materials, can solve the problems of inability to meet building construction, restrict the development of building construction, poor anti-cracking mortar effect, etc., to improve cleanliness and bondability, avoid high water absorption, good sound insulation

Inactive Publication Date: 2018-06-26
HEFEI YAKELI NEW BUILDING MATERIAL CO LTD
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of high-rise buildings, to reduce the weight of wall materials and improve their thermal insulation and energy-saving effects, thermal insulation mortar is usually coated on the wall. Thermal insulation mortar is a kind of thermal insulation building material used for interior and exterior walls. Insulation granules are used as lightweight aggregate, and dry powder mortar composed of other fillers and additives is added, but the insulation mortar is easy to absorb water and crack when exposed to space, which requires anti-cracking mortar on the insulation mortar layer, but the existing anti-crack The effect of cracking mortar is poor
In addition, the strength, impermeability, and water absorption of mortar on the market cannot meet the higher requirements of construction, thus limiting the development of construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] An energy-saving, heat-insulating, sound-insulating and environment-friendly building mortar of this embodiment comprises the following raw materials in parts by weight:

[0036] 20 parts of compound cement, 25 parts of modified ore filler, 4 parts of waterproof adhesion promoter, 20 parts of construction waste disposal, 8 parts of anti-crack additive, 2 parts of calcium stearate, 8 parts of hollow additive, water 20 servings.

[0037] The compound cement in this example is a mixture of Portland cement, aluminate cement and high alumina refractory cement in a weight ratio of 5:2:3.

[0038] The modified ore filler in this example is: send anorthite, vermiculite, and fish eye stone into the calciner according to the weight ratio of 2:1:3, calcined at 700°C for 30min, and then pulverized 100 mesh sieve, then add 4% polyvinyl alcohol and 4% silane coupling agent equivalent to the weight of the mixture, and stir for 15 minutes at a temperature of 65°C and a stirring speed ...

Embodiment 2

[0049] An energy-saving, heat-insulating, sound-insulating and environment-friendly building mortar of this embodiment comprises the following raw materials in parts by weight:

[0050] 30 parts of compound cement, 35 parts of modified ore filler, 8 parts of waterproof adhesion promoter, 30 parts of construction waste disposal, 10 parts of anti-crack additive, 4 parts of calcium stearate, 10 parts of hollow additive, water 30 servings.

[0051] The compound cement in this example is a mixture of Portland cement, aluminate cement and high alumina refractory cement in a weight ratio of 5:2:3.

[0052] The modified ore filler in this example is: send anorthite, vermiculite, and fish eye stone into the calciner according to the weight ratio of 2:1:3, calcinate for 40min at a temperature of 800°C, and then pulverize 100 mesh sieve, then add 6% polyvinyl alcohol and 6% silane coupling agent equivalent to the weight of the mixture, and stir for 25 minutes at a temperature of 75°C an...

Embodiment 3

[0063] An energy-saving, heat-insulating, sound-insulating and environment-friendly building mortar of this embodiment comprises the following raw materials in parts by weight:

[0064] 25 parts of compound cement, 30 parts of modified ore filler, 6 parts of waterproof adhesion promoter, 25 parts of construction waste disposal, 9 parts of anti-crack additive, 3 parts of calcium stearate, 9 parts of hollow additive, water 25 servings.

[0065] The compound cement in this example is a mixture of Portland cement, aluminate cement and high alumina refractory cement in a weight ratio of 5:2:3.

[0066] The modified ore filler in this example is: send anorthite, vermiculite, and fish eye stone into the calciner according to the weight ratio of 2:1:3, calcinate at a temperature of 750°C for 35min, and then pulverize 100 mesh sieve, then add 5% polyvinyl alcohol and 5% silane coupling agent equivalent to the weight of the mixture, and stir for 20 minutes at a temperature of 70°C and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses energy-saving thermal-insulation soundproof environment-friendly building mortar and a preparation method thereof. The energy-saving thermal-insulation soundproof environment-friendly building mortar is prepared from the following raw materials in parts by weight: 20-30 parts of compound cement, 25-35 parts of modified ore stuffing, 4-8 parts of a waterproof adhesion promoter, 20-30 parts of treated building waste, 8-10 parts of anti-cracking performance-enhancement additive, 2-4 parts of calcium stearate, 8-10 parts of hollow additive and 20-30 parts of water. The building mortar disclosed by the invention is low in heat conduction coefficient, is good in thermal insulation property, is outstanding in compactness, is resistant to water and seepage, further has excellent soundproof performance, adopts a great deal of building waste, and saves resources. The energy-saving thermal-insulation soundproof environment-friendly building mortar has the advantages of safe and reliable raw material component, relatively low cost, wide raw material source, relatively high practical value and good application prospect.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an energy-saving, heat-insulating, sound-insulating and environment-friendly building mortar and a preparation method thereof. Background technique [0002] The essence of building energy conservation is to scientifically and rationally improve the thermal performance of the outer envelope according to the characteristics of different climate zones. Building insulation is a measure to reduce the heat emitted from the building indoors to the outside, and plays an important role in creating a suitable indoor thermal environment and saving energy. [0003] Countries have done a lot of work in building design and construction, development and application of new building insulation materials, formulation and implementation of building energy-saving regulations, etc., while achieving considerable economic benefits, they have also improved the natural environment on which hum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B20/02C04B111/27C04B111/20C04B111/52
CPCC04B20/023C04B28/06C04B2111/00017C04B2111/20C04B2111/27C04B2111/52C04B7/02C04B14/041C04B14/202C04B14/04C04B2103/65C04B18/16C04B14/46C04B14/42C04B18/085C04B24/08C04B14/22C04B18/023C04B2103/44
Inventor 王磊
Owner HEFEI YAKELI NEW BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products