Concrete reinforcement repair agent

A repairing agent and concrete technology, applied in the field of concrete admixtures, can solve problems such as heavy workload, and achieve the effects of enhancing compactness, avoiding secondary pollution, and enhancing surface strength

Inactive Publication Date: 2018-06-19
云南森博混凝土外加剂有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This surface enhancer is composed of two components. The obtained surface enhancer can significantly improve the surface strength of hardened concrete. It has the effects of filling, compacting, strengthening, and sealing. However, the surface reinforcement prepared by this patent The agent is divided into two components, AB, which need to be painted separately during use, so the workload of the project is relatively large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The concrete reinforcing and repairing agent of the present invention is composed of the following substances by weight percentage: methacrylic acid-methyl acrylate polymer 60%, deionized water: 20%, carboxylic acid: 0.4%, colloidal silica: 4% , magnesium stearate: 4%, fly ash: 10%, silicate: 0.6%, anhydrite: 1%. The methacrylic acid-methyl acrylate polymer is prepared from methacrylic acid, methyl acrylate, ethanol and ammonium persulfate. The consumption of described methacrylic acid is 30%, the consumption of methyl acrylate is 20%, the consumption of ethanol is 49.5%, and the consumption of ammonium persulfate is 0.5%.

Embodiment 2

[0030] The concrete reinforcing repair agent of the present invention is composed of the following substances by weight percentage: methacrylic acid-methyl acrylate polymer: 40%, deionized water: 40%, carboxylic acid: 0.6%, colloidal silica: 6% %, magnesium stearate: 3%, fly ash: 8%, silicate: 0.4%, anhydrite: 2%. The methacrylic acid-methyl acrylate polymer is prepared from methacrylic acid, methyl acrylate, ethanol and ammonium persulfate. The consumption of described methacrylic acid is 20%, the consumption of methyl acrylate is 20%, the consumption of ethanol is 58.5%, and the consumption of ammonium persulfate is 1.5%.

Embodiment 3

[0032] The concrete reinforcing repair agent is composed of the following substances by weight percentage: methacrylic acid-methyl acrylate polymer: 50%, deionized water: 30%, carboxylic acid: 0.5%, colloidal silica: 5%, Magnesium stearate: 3%, fly ash: 10%, silicate: 0.5%, anhydrite: 1%.

[0033] The methacrylic acid-methyl acrylate polymer is prepared from methacrylic acid, methyl acrylate, ethanol and ammonium persulfate. The consumption of described methacrylic acid is 26%, the consumption of methyl acrylate is 26%, the consumption of ethanol is 47%, and the consumption of ammonium persulfate is 1%.

[0034] The present invention prepares the surface strengthening restoration agent of concrete, and concrete preparation method is:

[0035] (1) Preparation of polymer macromonomer:

[0036] 1. Prepare materials, prepare weight component design: methacrylic acid: 50 parts; methyl acrylate: 50 parts; ethanol: 100 parts; ammonium persulfate: 3 parts;

[0037] 2. Preparation s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a concrete additive, in particular to a concrete surface reinforcement repair agent. The concrete surface reinforcement repair agent is composed of the following substances inpercentages by weight: 40% to 60% of methacrylic acid-methyl acrylate polymer, 20% to 40% of deionized water, 0.4% to 0.6% of carboxylic acid, 4% to 6% of colloid silicon oxide, 2% to 4% of magnesiumstearate, 8% to 12% of coal ash, 0.4% to 0.6% of silicate and 1% to 2% of anhydrite. The concrete surface reinforcement repair agent disclosed by the invention can be quickly permeated to the interior of concrete to reach the effect of effectively improving the using strength of concrete.

Description

technical field [0001] The invention relates to a concrete admixture, in particular to a repairing agent for surface reinforcement applied to concrete. Background technique [0002] In the actual construction process of concrete engineering, the type of cement, the water-cement ratio of concrete and even the use of some admixtures that affect the strength of concrete will affect the strength of concrete. For projects that also have clear requirements on the lightness of concrete, how to better maintain or even improve the strength of concrete requires the introduction of other additives to participate in the adjustment. Surface enhancers can play a very good role in increasing the strength of concrete. Therefore, in recent years, the research and use of surface enhancers have attracted more and more attention. [0003] Chinese Invention Patent Publication No. CN104557137A discloses the preparation of a concrete surface strengthening agent. This invention designs a two-comp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/85C04B24/26C08F220/14C08F220/06
CPCC04B41/5024C04B40/0039C04B41/85C08F220/06C08F220/14C04B24/2641C04B24/04C04B22/06C04B24/08C04B18/08C04B22/00C04B22/143C04B41/50C04B41/4857
Inventor 阿光强徐兴爱阿光城唐凯李金梅
Owner 云南森博混凝土外加剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com