Low-emission low-odor glass-fiber-reinforced polypropylene composite material and preparation method therefor

A technology of polypropylene material and low odor, which is applied in the field of polymer materials and can solve the problems of frosting and whitening on the surface of materials, low odor, etc.

Inactive Publication Date: 2018-06-15
CHONGQNG PRET NEW MATERIAL +4
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the problem of frosting and whitening on the surface of the material caused by the migration of antioxidants in the production process of glass fiber reinforced polypropylene composite materials, and at the same time provide a modification method for reducing the odor during the processing of glass fiber reinforced polypropylene materials, The invention can prepare glass fiber reinforced polypropylene material with low emission and low odor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-emission low-odor glass-fiber-reinforced polypropylene composite material and preparation method therefor
  • Low-emission low-odor glass-fiber-reinforced polypropylene composite material and preparation method therefor
  • Low-emission low-odor glass-fiber-reinforced polypropylene composite material and preparation method therefor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～2

[0024] This embodiment relates to a low emission and low odor glass fiber reinforced polypropylene composite material and its preparation method, the method is as follows:

[0025] Step 1, weighing the raw materials according to the weight ratio, each component and its data are shown in Table 1;

[0026] Step 2, the raw material polypropylene, glass fiber, compatibilizer and antioxidant weighed according to the weight ratio are added to the high-speed mixer in proportion and fully mixed, and then the above mixture is added to the extruder, and the extruder is passed through the extruder After plasticizing, extrude, draw, cool, and pelletize to 3-5mm long cylindrical particles, and finally obtain low-emission and low-odor glass fiber reinforced polypropylene composite materials. The temperature of the screw extruder is 100-220° C., and the rotation speed of the main engine is 300 rpm.

[0027] Among them, the polypropylene is provided by Sinopec Company, the brand is M60T; the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
diameteraaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-emission low-odor glass-fiber-reinforced polypropylene material and a preparation method therefor. The material is prepared from the following raw materials in parts by weight: 35-80 parts of polypropylene, 15-60 parts of glass fibers, 1.0-5 parts of compatibilizer and 0.1-1.5 parts of antioxidant. According to the material and the preparation method therefor, hindered phenol and hindered amine polymers are adopted as the antioxidant, an obtained sample has the same excellent aging resistance as that of a control sample, and the sample prepared by the method has alower odor level and lower emission performance.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a low-emission and low-odor glass fiber reinforced polypropylene material and a preparation method thereof. Background technique [0002] Compared with steel and other metals, the modulus strength of polypropylene material is much lower than that of steel and other metals. Therefore, in the field of automotive materials, polypropylene materials need to use glass fiber, talcum powder and other filler materials to improve the strength and modulus, so that they can be used in The field of automotive materials to replace steel, and ultimately achieve the purpose of reducing the weight of auto parts. [0003] Due to its high strength and high modulus, glass fiber reinforced polypropylene materials are generally used in stressed structural parts. During the long-term service life of automobiles, glass fiber reinforced polypropylene materials will degrade due to the influence ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L51/06C08J5/08
CPCC08J5/08C08J2323/12C08J2451/06
Inventor 张杨陈永东蔡青刘善华周文
Owner CHONGQNG PRET NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com