Environment-friendly glazed composite tile for buildings as well as manufacturing method thereof

A construction and environmental protection technology, applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve problems such as the failure of composite tiles to meet environmental protection requirements, save energy and energy consumption, increase aesthetics, reduce The effect of raw material cost

Inactive Publication Date: 2018-05-25
董浩
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] As people's awareness of environmental protection becomes stronger, traditional composite tiles cannot meet people's environmental protection requirements. With the development of new ecological composite tiles, color steel tiles with waste utilization, energy saving, environmental protection and beautiful appearance are becoming more and more important

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An environmentally friendly glazed composite tile for buildings made of rice husk and talcum powder, the manufacturing method is as follows:

[0034] Step 1. Put the rice husks into an ultraviolet light disinfection cabinet for disinfection, then dry them, heat them at 60°C for 5 hours to dry the rice husks, and then use a crusher to crush the dried rice husks into granules to obtain rice husk granules;

[0035] Step 2, after weighing 3 parts by weight of rice husk particles, add 1.5 parts by weight of talcum powder and mix evenly to obtain a mixture;

[0036] Step 3. Add 0.3 parts by weight of titanate coupling agent NDZ-401 to the above mixture, stir evenly, and let stand for 20 minutes to obtain the glue-added mixture;

[0037] Step 4, inject the above-mentioned glue-adding mixture into the composite tile mould, close the mould, and get rid of air bubbles;

[0038] Step 5. Carry out hot pressing treatment on the mold, the pressure is 3.5MPa, the temperature is 150°C...

Embodiment 2

[0042] An environmentally friendly glazed composite tile for construction made of corn stalks and putty powder, the manufacturing method is as follows:

[0043] Step 1. Put the corn stalks into an ultraviolet light disinfection cabinet for disinfection, then dry them, heat them at 60°C for 5 hours, dry the corn stalks, and then use a crusher to crush the dried corn stalks into granules to obtain corn stalk granules;

[0044] Step 2, after weighing 3 parts by weight of corn stalk particles, add 2 parts by weight of putty powder and mix evenly to obtain a mixture;

[0045] Step 3. Add 0.3 parts by weight of titanate coupling agent NDZ-401 to the above mixture, stir evenly, and let stand for 20 minutes to obtain the glue-added mixture;

[0046] Step 4, inject the above-mentioned glue-adding mixture into the composite tile mould, close the mould, and get rid of air bubbles;

[0047] Step 5. Carry out hot pressing treatment on the mold, the pressure is 3.5MPa, the temperature is 1...

Embodiment 3

[0051] An environmentally friendly glazed composite tile for construction made of bagasse and heavy calcium powder, the manufacturing method is as follows:

[0052] Step 1. Put the bagasse into an ultraviolet lamp disinfection cabinet for disinfection, then dry it, heat it at 60° C. for 8 hours to dry the bagasse, and then use a crusher to crush the dried bagasse into granules to obtain bagasse granules;

[0053] Step 2, after weighing 3 parts by weight of bagasse particles, add 2.5 parts by weight of heavy calcium powder and mix evenly to obtain a mixture;

[0054] Step 3. Add 0.4 parts by weight of titanate coupling agent NDZ-401 to the above mixture, stir evenly, and let stand for 30 minutes to obtain the glue-added mixture;

[0055] Step 4, inject the above-mentioned glue-adding mixture into the composite tile mould, close the mould, and get rid of air bubbles;

[0056]Step 5. Carry out hot pressing treatment on the mold, the pressure is 3.5MPa, the temperature is 180°C, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly glazed composite tile for buildings as well as a manufacturing method thereof. The environment-friendly glazed composite tile is manufactured by the following steps: pulverizing 3 parts by weight of crop waste, adding 1.5 to 2.5 parts by weight of stone powder and 0.3 to 0.4 part by weight of titanate coupling agent NDZ-401, mixing and stirring uniformly, injecting into a mold, performing hot-pressing and cooling treatment under 3.5 MPa and at 150 to 180 DEG C and demolding to obtain an environment-friendly composite tile; and spray-coating the surface of the composite tile with glaze, putting into an oven and solidifying to form the environment-friendly glazed composite tile, wherein the crop waste is one or more of rice husk, wheatgrass, cotton stalks, bagasse, saw dust, cornstalks, hemp stalks and wheat straws; and the stone powder is one or more of medical stone powder, coarse whiting powder, talcum powder, dolomite powder and putty powder. The environment-friendly glazed composite tile for buildings has the characteristics of waste utilization, energy saving, environmental friendliness and beautiful appearance.

Description

technical field [0001] The invention relates to an environmentally friendly glazed composite tile for buildings and a manufacturing method thereof, in particular to an environmentally friendly glazed composite tile for buildings with waste utilization, energy saving, environmental protection and beautiful appearance. Background technique [0002] With the continuous development of my country's economy in recent years, it has promoted the development of the construction industry. Modern buildings are gradually developing towards high quality and high grade, and their functional requirements are constantly improving. Traditional roofing materials can no longer meet the requirements of the development of the construction industry, and various new materials have emerged as the times require. [0003] The commonly used roofing materials are: asbestos tiles, cement tiles, composite tiles, etc. Among them, asbestos tiles not only contain carcinogenic ingredients, but also have a s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B30/02C04B41/65C04B18/24C04B18/26
CPCC04B18/24C04B18/26C04B30/02C04B41/009C04B41/5022C04B41/65C04B14/28C04B14/042C04B14/26C04B14/14C04B14/02C04B24/40C04B41/4543Y02W30/91
Inventor 李涌泉
Owner 董浩
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com