Sticky steel glue for bi-component anchor rod and preparation method of sticky steel glue

A two-component steel adhesive technology, applied in the direction of adhesives, epoxy resin adhesives, adhesive types, etc., can solve problems such as unscientific formula and processing technology, inability to guarantee the use effect, poor performance of steel adhesive, etc. Achieve the effects of scientific and standardized processing technology, anti-humidity and aging resistance, anti-freeze and thaw performance, and strong adhesive performance

Inactive Publication Date: 2018-05-04
ANHUI KUNDA CHEM ANCHORAGE
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When the bolt is in normal use, because it is directly in contact with concrete and other media, the corresponding steel glue must be used for routine use, so as to ensure the actual use effect. In normal use, steel glue is indispensable. However, the actual formula and processing technology of the impregnating glue on the existing market are not scientific, and the actual use effect cannot be guaranteed, resulting in poor performance and poor use effect of the steel glue, and it is impossible to obtain a relatively effective use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sticky steel glue for bi-component anchor rod and preparation method of sticky steel glue

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A two-component steel glue for anchor rods is prepared from the following raw materials in parts by mass:

[0030] Component A

[0031] Liquid polysulfide rubber 15, epoxy resin 125, fumed silica 3, coupling agent 2, diluent 10, nano silica 1, quartz powder 140;

[0032] Component B

[0033] Amino-terminated polyether 25, m-xylylenediamine 6, maleic anhydride 3, benzyl alcohol 1, glycerol 0.2;

[0034] The ratio of the A component to the B component is A:B=2.5:1 (parts by mass).

[0035] The method for preparing the above-mentioned two-component two-component anchor rod with steel glue, comprises the following steps:

[0036] 1) Combine the liquid polysulfide rubber and epoxy resin in the raw materials of component A, stir evenly, and set aside;

[0037] 2) Combine the fumed silica, nano-silica and quartz powder in the raw materials of component A to obtain a powder for use;

[0038] 3) Combine the materials in the above step 1 and step 2 and compound them evenly, ...

Embodiment 2

[0042] A two-component steel glue for anchor rods is prepared from the following raw materials in parts by mass:

[0043] Component A

[0044] Liquid polysulfide rubber 25, epoxy resin 135, fumed silica 5, coupling agent 4, diluent 14, nano silica 3, quartz powder 160;

[0045] Component B

[0046] Amino-terminated polyether 35, m-xylylenediamine 10, maleic anhydride 5, benzyl alcohol 3, glycerol 0.4;

[0047] The ratio of the A component to the B component is A:B=2.5:1 (parts by mass).

[0048] The method for preparing the above-mentioned two-component two-component anchor rod with steel glue, comprises the following steps:

[0049] 1) Combine the liquid polysulfide rubber and epoxy resin in the raw materials of component A, stir evenly, and set aside;

[0050] 2) Combine the fumed silica, nano-silica and quartz powder in the raw materials of component A to obtain a powder for use;

[0051] 3) Combine the materials in the above step 1 and step 2 and compound them evenly,...

Embodiment 3

[0055] A two-component steel glue for anchor rods is prepared from the following raw materials in parts by weight:

[0056] Component A

[0057] Liquid polysulfide rubber 20kg, E51 epoxy resin 100kg, 269# epoxy resin 30kg, fumed silica 4kg, KH5603kg, polypropylene glycol diglycidyl ether 12kg, nano silica 2kg, quartz powder 150kg;

[0058] Component B

[0059] Amino-terminated polyether 30kg, m-xylylenediamine 8kg, maleic anhydride 4kg, benzyl alcohol 2kg, glycerol 0.3kg;

[0060] The ratio of the A component to the B component is A:B=2.5:1 (parts by weight).

[0061] Described epoxy resin is by the composite mixture of E51 epoxy resin and 269# epoxy resin, and the mass ratio of described E51 epoxy resin and 269# epoxy resin is 10:3;

[0062] The coupling agent is KH560, and the diluent is polypropylene glycol diglycidyl ether.

[0063] The method for preparing the above-mentioned two-component two-component anchor bolt is characterized in that, comprises the steps:

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to sticky steel glue for a bi-component anchor rod. The sticky steel glue is prepared from the following components in parts by mass: a component A: 15-25 parts of liquid polysulfide rubber, 125-135 parts of epoxy resin, 3-5 parts of fumed silica, 2-4 parts of a coupling agent, 10-14 parts of a diluent, 1-3 parts of nano-silicon dioxide and 140-160 parts of quartz powder; a component B: 25-35 parts of amine-terminated polyether, 6-10 parts of m-xylylenediamine, 3-5 parts of maleic anhydride, 1-3 parts of benzyl alcohol and 0.2-0.4 parts of glycerol; and the ratio (parts by mass) of the component A to the component B is 2.5 to 1. The sticky steel glue has the beneficial effects that the formula is reasonable, the processing process is scientific and normative, and theprepared sticky steel glue is extremely high in strength and strong in damp-heat aging resistance and freeze thaw resistance and has very strong adhesive property aiming at waterproof, unclean and oil-carrying surfaces, so that great convenience is brought to the engineering construction.

Description

technical field [0001] The invention relates to the technical field of steel glue processing, in particular to a two-component steel glue for anchor rods and a preparation method thereof. Background technique [0002] Adhesive to steel, with super strong adhesive force, strong shearing force, anti-aging, good medium resistance (acid, alkali, water), strong impact resistance, normal temperature curing, small shrinkage during hardening, no flow during construction, no Volatile solvent, non-toxic and convenient construction, can be applied in a wide temperature range, no precipitation, almost suitable for all building substrates, steel structure adhesive is paste, with a relatively thin state, good thixotropy, mainly It is used for bonding reinforcement of concrete components, masonry components and steel components to steel plates, curtain wall installation; bonding installation of marble, granite, ceramic tiles, etc.; repair and bonding of concrete components and steel compon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/02C09J163/00C09J11/06C09J11/04C09J11/08
CPCC09J163/00C08K2201/011C08L2205/025C08L2205/035C09J11/04C09J11/06C09J11/08C08L63/00C08L81/04C08L71/00C08K13/02C08K3/36C08K5/5435
Inventor 朱国坤朱良坤赵庆
Owner ANHUI KUNDA CHEM ANCHORAGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com