Novel steel material for automobile rotation shaft
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of rotating shafts and steel materials, applied in the field of new steel materials, can solve the problems of low production cost and high manufacturing cost, and achieve the effects of increasing hardenability, reducing production cost and saving the amount of molybdenum used
Inactive Publication Date: 2018-04-27
重庆华厦新力新能源汽车有限公司
View PDF2 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] In order to solve the high manufacturing cost of the existing general-purpose W6Mo5Cr4V2 steel and maintain sufficient wear resistance and toughness of the steel, the purpose of the present invention is to provide a replacement for W6Mo5Cr4V2, which has sufficient toughness and wear resistance, and can be used as a car rotating shaft, and New steel for car shafts that can be produced cheaply
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] A new type of steel used for the rotating shaft of automobiles, the steel includes: carbon C0.9%-1.2%, silicon Si0.21%-0.5%, manganese Mn0.18%-0.3%, chromium Cr9.5 %~12.0%, tungsten W4%~4.8%, molybdenum Mo0.55%~2.2%, vanadium V0.5%~2.2%, nickel Ni0.05%~0.2%, cobalt Co0.25%~4.0%, niobium Nb0 .7~2%, sulfur S≤0.01%, phosphorus P≤0.01%, and the balance is iron Fe.
[0020] The heat treatment process for the above-mentioned novel chromium steel series steel includes the following steps:
[0021] (1), the first preheating, the temperature is 600 ℃, and the preheating time is 60 minutes;
[0022] (2), the second preheating, the temperature is 900 ℃, and the preheating time is 45 minutes;
[0023] (3) Quenching heating, the quenching heating temperature is 1150°C-1240°C, the quenching time is: (25+material thickness / 2) minutes, and then oil-cooled to 250°C-270°C;
[0024] (4) For the first tempering, the tempering temperature is 500°C to 550°C, the tempering time is 110 minu...
Embodiment 2
[0028] A new type of steel used for the rotating shaft of automobiles. The steel includes: carbon C0.95%~1.0%, silicon Si0.25%~0.35%, manganese Mn0.22%~0.3%, chromium Cr10%~ 11%, tungsten W4%~4.3%, molybdenum Mo0.6%~1%, vanadium V0.6%~1.5%, nickel Ni0.1%~0.15%, cobalt Co1%~1.4%, niobium Nb0.9~1.5% %, sulfur S≤0.005%, phosphorus P≤0.005%, and the balance is iron Fe.
[0029] The heat treatment process for the above-mentioned novel chromium steel series steel includes the following steps:
[0030] (1), the first preheating, the temperature is 600 ℃, and the preheating time is 60 minutes;
[0031] (2), the second preheating, the temperature is 900 ℃, and the preheating time is 45 minutes;
[0032] (3) Quenching heating, the quenching heating temperature is 1150℃~1240℃, the quenching time is: (25+material thickness / 2) minutes, then cooling in salt bath, grading heat preservation at 650℃, and then salt bath to 250℃~270℃ ;
[0033] (4) For the first tempering, the tempering temp...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
Compared with domestic steel W6Mo5Cr4V2, the steel material of the present invention replaces a large amount of molybdenum with chromium, which saves the usage of molybdenum, and also reduces the usage of vanadium and tungsten, thereby reducing the production cost of alloy steel; adding non-carbide elements Nickel improves the strength of steel through solid solution strengthening, and at the same time has high plasticity and toughness, and strongly increases the hardenability of steel, and the addition of cobalt greatly improves the hot hardness and cutting performance of alloy steel; adding The carbide forming element niobium increases the toughness of the steel and improves the processability of hot working. The content of P and S in the present invention is very low (especially P), so the purity of the steel is particularly good, and it plays a role in guaranteeing various properties of the steel. The annealed Brinell hardness of the steel reaches HB250. Therefore, the steel of the invention has high thermal hardness and cutting performance, and also has high toughness and wear resistance. However, the material cost is much lower than the domestic steel W6Mo5Cr4V2, which is suitable for making various vehicle shafts.
Description
technical field [0001] The invention relates to a new type of steel used for the rotating shaft of automobiles. Background technique [0002] The existing steel materials used for the rotating shaft of automobiles are generally made of domestic steel W6Mo5Cr4V2. The chemical composition of the alloy is (weight%): C0.80%~0.90%, Si≤0.45%, Mn≤0.40%, W5.50%~6.75 %, Mo4.50%~5.50%, Cr3.80%~4.40%, V1.75%~2.15%, S≤0.03%, P≤0.03%, and the rest is Fe. This steel contains a relatively high content of Mo. Now due to the lack of Mo in the international market, the price is relatively expensive, and the content of tungsten and vanadium in this steel is also high, so the cost of producing the alloy is also greatly increased. The Chinese invention patent (the notification number is CN1014081) discloses low-alloy high-performance steel, which is characterized in that the specific chemical composition of the steel is (weight %) C0.85% ~ 1.05%, W3.0% ~ 5.0%, Mo2. 0%~3.5%, Cr3.5%~5.0%, V1.15%...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).