Multifunctional bamboo cotton composite fabric

A composite fabric and multi-functional technology, applied in the textile field, can solve the problems of finding antibacterial and antistatic fabrics, and achieve the effect of quick drying and comfortable inner layer

Pending Publication Date: 2018-04-20
广东创时尚智能股份有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In addition, among the fabrics in the existing market, there are basically no fabrics with antibacterial and antistatic functions. With the improvement of living standards, people will have higher and higher requirements for the fabrics they wear. Functional fabrics will become the daily needs of ordinary people

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional bamboo cotton composite fabric
  • Multifunctional bamboo cotton composite fabric
  • Multifunctional bamboo cotton composite fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A multifunctional bamboo-cotton composite fabric, composed of an inner layer 1 and an outer layer 2, the inner layer 1 is an antistatic thermal layer, and the outer layer 2 is a hydrophobic layer, and the antistatic thermal layer is made of multifunctional composite yarn The hydrophobic layer is woven with hydrophobic yarn, the inner layer 1 and the outer layer 2 are connected together by low-denier yarn 3, and the low-denier yarn 3 runs through the inner layer 1 and the outer layer 2. The inner layer 1 and the outer layer 2 are connected together, and the surfaces of the inner layer 1 and the outer layer 2 are evenly arranged with connection points formed by low-denier yarns, and the multifunctional composite yarn is made of a single bamboo The fiber is twisted with a single cotton fiber to form a yarn, which is then scoured and treated with a composite finishing agent. The hydrophobic yarn is formed by twisting a single bamboo fiber and a single cotton fiber to form a ...

Embodiment 2

[0019] Washing Durability Test

[0020] With reference to the "GB / T8629-2001 Home Washing and Drying Program for Textile Tests" standard, a kind of multifunctional bamboo-cotton composite fabric of Example 1 is washed, repeated several times, and then the quick-drying test of the inner layer of the fabric and the outer surface are carried out. Water repellency test of the layer surface.

[0021] The quick-drying test of the inner layer of the fabric is as follows: (1) Cut out 5 samples from the sample, the size of each sample is 10cm×10cm, and the samples should be smooth and wrinkle-free. (2) Place the sample under standard atmospheric conditions to adjust the humidity balance. (3) Place the sample flat on the test bench (inner layer facing up), absorb about 0.2ml of water and gently drop it on the sample, the diameter of the dropper should not exceed 1cm from the surface of the sample. (4) Carefully observe the diffusion of water droplets, and record the time required for ...

Embodiment 3

[0031] Persistence test of antistatic ability

[0032] Refer to the standard of "GB / T8629-2001 Household Washing and Drying Procedures for Textile Tests", wash the samples 5, 10, and 20 times respectively, and then test them in YG(B) according to GB / T12703.2-2009 "Textile Electrostatic Test Method". The surface charge of the cloth sample is measured on the 403-type fabric friction electrification tester. The more the charge, the worse its antistatic property; the less the charge, the better its antistatic property.

[0033] Measure the electric charge of embodiment 1 of the present invention and common cloth on the market respectively, and the measurement results are as follows:

[0034] Table 3 Surface charge corresponding to each cloth sample

[0035]

[0036] It can be seen from the above table that the surface charge and the surface charge area density of Embodiment 1 of the present invention have obvious antistatic ability compared with the common cloth on the market,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of textiles, and particularly relates to a multifunctional bamboo cotton composite fabric. The multifunctional bamboo cotton composite fabric is compounded by an inner layer and an outer layer, wherein the inner layer is an antistatic warmth retention layer; the outer layer is a hydrophobic layer; the antistatic warmth retention layer is woven by multifunctionalcomposite yarns; the hydrophobic layer is woven by hydrophobic yarns; the inner layer is connected with the outer layer through low-denier yarns; the low-denier yarns pass through the inner layer andthe outer layer and are used for connecting the inner layer with the outer layer, and enabling connection points formed by the low-denier yarns to be uniformly distributed on the surfaces of the innerlayer and the outer layer. The multifunctional bamboo cotton composite fabric is a multifunctional composite fabric with an antistatic function, an antibacterial function and moisture transferring and quick drying functions, and is especially applicable to clothing fabrics; meanwhile, the functions of the multifunctional bamboo cotton composite fabric have lasting effects.

Description

technical field [0001] The invention belongs to the textile field, and in particular relates to a multifunctional bamboo-cotton composite fabric. technical background [0002] Patent CN102121161A discloses a kind of unidirectional moisture-wicking knitted fabric and its processing technology, which adopts synthetic fiber yarn and synthetic fiber waterproof yarn to weave, and the fabric is a four-layer layered structure. The principle of its invention is to realize the function of one-way moisture transfer through the distribution of synthetic fiber waterproof yarn and synthetic fiber yarn at different levels, so that the moisture in the fabric can quickly transfer and diffuse to the predetermined level. Although this method is suitable for fibers with the same linear density of a single component, synthetic fibers themselves have hydrophobic properties. The processing method is to build a moisture-conducting and quick-drying gradient structure through the weaving of synthe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B5/06B32B9/02B32B9/04B32B33/00D06M13/203D06M13/224D06M13/236D06M15/03D06M15/507D06M15/53D06M15/643
CPCD06M11/57D06M13/188D06M13/203D06M13/224D06M13/2246D06M13/236D06M15/03D06M15/507D06M15/53D06M15/6436D06M16/00B32B5/024B32B5/06B32B5/08B32B5/26B32B9/02B32B9/047B32B33/00D06M2200/12D06M2101/06B32B2307/304B32B2307/724B32B2307/7145B32B2307/73B32B2437/00
Inventor 钟汉文杨海裕唐汇贵黄芬芳钟永南钟永立
Owner 广东创时尚智能股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products