Graphene anticorrosion coating and preparation method thereof

A technology of anti-corrosion coatings and graphene, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problem that anti-corrosion coatings are difficult to meet high temperature and high humidity resistance, acid rain resistance, salt spray resistance, poor corrosion resistance, outdoor steel structures Problems such as poor use environment

Inactive Publication Date: 2018-04-17
SHENZHEN GUOCHUANG JIAWEI GRAPHENE TECH CO LTD
View PDF5 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the corrosion resistance of steel is poor, and protective measures must be taken to prevent steel from corroding and rusting, so as to ensure the safety of the steel structure during the design service period.
Outdoor steel structures are used in harsh environments, and ordinary anti-corrosion coatings are difficult to meet the requirements of high temperature and high humidity resistance, acid rain resistance, and salt spray resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene anticorrosion coating and preparation method thereof
  • Graphene anticorrosion coating and preparation method thereof
  • Graphene anticorrosion coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Embodiment 1: a kind of graphene anticorrosion coating, used raw material is as follows:

[0050] The graphene self-repairing anticorrosion primer includes the following raw materials in parts by weight: 6 parts of E44 epoxy resin, 16 parts of E20 epoxy resin, 14 parts of 650 polyamide curing agent, 0.5 part of graphene, 5 parts of 800 mesh zinc phosphate, 30 parts of 500 mesh zinc powder, 3.7 parts of 1000 mesh mica powder, nano-SiO 2 1.0 copies, BENGEL ® 1.0 parts of 828 organic bentonite, 4 parts of xylene, 8 parts of n-butanol, 6 parts of cyclohexanone, 1.5 parts of H-1400, 2.0 parts of BYK110, 1.0 parts of 6900-20X, 0.3 parts of 5500 defoamer. Among them, the diameter of graphene sheets is 5-30um, the number of graphene layers is less than 10 layers, and the specific surface area of ​​graphene is 30-200m 2 / g.

[0051] Paint preparation process: provide graphene slurry. Among them, the graphene slurry is prepared; the flake graphite with a purity of 97-99% is o...

Embodiment 2

[0056] Embodiment 2: The graphene anticorrosion coating comprises the following raw materials in parts by weight: 6 parts of E44 epoxy resin, 16 parts of E20 epoxy resin, 14 parts of 650 polyamide curing agent, 1 part of graphene, 5 parts of 800 mesh zinc phosphate , 30 parts of 500 mesh zinc powder, 3.2 parts of 1000 mesh mica powder, nano-SiO 2 1.0 copies, BENGEL ® 1.0 parts of 828 organic bentonite, 4 parts of xylene, 8 parts of n-butanol, 6 parts of cyclohexanone, 1.5 parts of H-1400, 2.0 parts of BYK110, 1.0 parts of 6900-20X, 0.3 parts of 5500 defoamer. Among them, the diameter of graphene sheets is 5-30um, the number of graphene layers is less than 10 layers, and the specific surface area of ​​graphene is 30-200m 2 / g.

[0057] Coating preparation technological process is with embodiment 1

Embodiment 3

[0059] The graphene anticorrosion coating includes the following raw materials in parts by weight: 6 parts of E44 epoxy resin, 16 parts of E20 epoxy resin, 14 parts of 650 polyamide curing agent, 3 parts of graphene, 5 parts of 800 mesh zinc phosphate, 500 mesh zinc 28 parts of powder, 3.2 parts of 1000 mesh mica powder, nano-SiO 2 1.0 copies, BENGEL ® 1.0 parts of 828 organic bentonite, 4 parts of xylene, 8 parts of n-butanol, 6 parts of cyclohexanone, 1.5 parts of H-1400, 2.0 parts of BYK110, 1.0 parts of 6900-20X, 0.3 parts of 5500 defoamer. Among them, the diameter of graphene sheets is 5-30um, the number of graphene layers is less than 10 layers, and the specific surface area of ​​graphene is 30-200m 2 / g.

[0060] Coating preparation technological process is with embodiment 1

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention provides graphene anticorrosion coating, prepared from, by weight, 20-60 parts of epoxy resin, 5.0-60 parts of a curing agent, 0.05-5.0 parts of graphene, 10-70 parts of an antirust filler, 5.0-30 parts of a solvent, and 1.0-10 parts of an aid, wherein graphene has sheet diameter of 5-30 mu m, thickness of less than 20 nanometers, the number of layers being less than 10 and specificsurface area of 30-200 m<2> / g. The graphene anticorrosion coating provided herein has good corrosion resistance, good tolerance to high temperature and high humidity, good resistance to acid rain andgood resistance to salt fog. The invention also provides a preparation method of the graphene anticorrosion coating.

Description

technical field [0001] The invention relates to the field of surface treatment, in particular to a graphene anticorrosion coating and a preparation method. Background technique [0002] With the development of social economy, my country's steel structure industry has shown a continuous and rapid growth momentum. The output of steel structure has increased from 8.5 million tons in 2002 to 22.94 million tons in 2009, with an average annual compound growth rate of 15.24%. According to relevant data estimates, in 2010, the output of steel structures reached 26 million tons. In 2011, the output of steel structure was about 29 million tons. my country's steel structure industry is in a period of rapid development. Steel structure materials are widely used in large stadiums, theaters, airports, railway stations, petroleum engineering equipment, steel structure residences, steel structure bridges, industrial plants, and offshore platforms. However, the corrosion resistance of ste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/10C09D7/61
CPCC09D163/00C08K2003/0893C08K2003/328C08K2201/011C08L2205/025C09D5/106C08L63/00C08K13/02C08K3/08C08K3/04C08K3/32C08K3/34C08K3/36
Inventor 文钟强王东卫丁显波
Owner SHENZHEN GUOCHUANG JIAWEI GRAPHENE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products