Low-reflection and high-transmittance glass and coating process thereof

A light-transmitting glass, low-reflection technology, applied in the coating and other directions, can solve the problems of high cost, glass reflection, low light transmittance, etc., to achieve the effect of strong light transmittance, guaranteed transmission, and simple process

Inactive Publication Date: 2018-04-06
ZHONGSHAN CHUANGKE RES TECH SERVICE
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to achieve the purpose in the background technology, the present invention proposes a low-reflection, high-transmittance glass and its coating process. The present invention can improve the deficiencies of the current production of coated glass, effectively improve glass reflection, low light transmittance, High cost and other issues, its coated glass can be widely used in military, national defense and other fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-reflection and high-transmittance glass and coating process thereof
  • Low-reflection and high-transmittance glass and coating process thereof
  • Low-reflection and high-transmittance glass and coating process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A low-reflection, high-transmittance glass and its coating process:

[0023] (1) When starting the coating preparation, thoroughly clean the working platform to ensure that there are no visible debris;

[0024] (2) Turn on the cooling circulating water pump to ensure that the working temperature of the instrument is in a constant state;

[0025] (3) Put various cleaning solutions in the cleaning tank, then put transparent silicon-based glass of the same size into the cleaning tank for cleaning, and use ultrasonic waves for ultrasonic cleaning, and the cleaning times are 3 times;

[0026] (4) Then transport the cleaned glass to a vacuum cleaning room for further cleaning. The water used in the cleaning process is deionized water, and special cleaning agents are used for cleaning, and ultrasonic cleaning is performed using ultrasound. The number of cleanings is 3 Second-rate;

[0027] (5) Transport the cleaned glass to a vacuum drying oven for drying at 80°C for 2 hours...

Embodiment 2

[0031] A low-reflection, high-transmittance glass and its coating process:

[0032] (1) When starting the coating preparation, thoroughly clean the working platform to ensure that there are no visible debris;

[0033] (2) Turn on the cooling circulating water pump to ensure that the working temperature of the instrument is in a constant state;

[0034] (3) Put various cleaning solutions in the cleaning tank, then put transparent silicon-based glass of the same size into the cleaning tank for cleaning, and use ultrasonic waves for ultrasonic cleaning, and the cleaning times are 5 times;

[0035] (4) Then transport the cleaned glass to a vacuum cleaning room for further cleaning. The water used in the cleaning process is deionized water, and special cleaning agents are used for cleaning, and ultrasonic cleaning is carried out, and the cleaning times are 5 Second-rate;

[0036] (5) Transport the cleaned glass to a vacuum drying oven for drying at 100°C for 1 hour;

[0037] (6)...

Embodiment 3

[0040] A low-reflection, high-transmittance glass and its coating process:

[0041] (1) When starting the coating preparation, thoroughly clean the working platform to ensure that there are no visible debris;

[0042] (2) Turn on the cooling circulating water pump to ensure that the working temperature of the instrument is in a constant state;

[0043] (3) Put various cleaning solutions in the cleaning tank, then put transparent silicon-based glass of the same size into the cleaning tank for cleaning, and use ultrasonic waves for ultrasonic cleaning, and the cleaning times are 5 times;

[0044] (4) Then transport the cleaned glass to a vacuum cleaning room for further cleaning. The water used in the cleaning process is deionized water, and special cleaning agents are used for cleaning, and ultrasonic cleaning is carried out, and the cleaning times are 5 Second-rate;

[0045] (5) Transport the cleaned glass to a vacuum drying oven for drying at 100°C for 2 hours;

[0046] (6) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of material preparation, and in particular relates to a low-reflection, high-transmittance glass and its coating process; a low-reflection, high-transparency glass and its coating process proposed by the present invention include the following steps: cleaning, coating and other processes , the coated glass prepared by it can well improve the problems of glass reflection, low light transmittance, high cost, etc., and its coated glass can be widely used in military, national defense and other fields.

Description

technical field [0001] The invention belongs to the technical field of material preparation, and in particular relates to a low-reflection, high-transmittance glass and its coating process. Background technique [0002] Glass coating is a surface treatment process for glass using polymer materials. Because polymer materials have chemical material properties such as high density and high sealing, they are widely used in the field of automotive glass beauty. At the same time, glass coating has It has the characteristics of high light transmission, anti-oxidation, acid and alkali resistance, and anti-ultraviolet radiation. In addition, it has a good anti-reflection effect. It has great value in military telescopes, aerospace and other fields, and is a good industrial product. But today's glass coating process is relatively complex and costly, which brings difficulties to product popularization. Contents of the invention [0003] In order to achieve the purpose in the backgro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/34
CPCC03C17/34C03C2217/734C03C2218/151
Inventor 陈路玉杜瑞婷杨永华
Owner ZHONGSHAN CHUANGKE RES TECH SERVICE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com