High and low temperature-resistant asphalt added with hexadecanol modifier and preparation method thereof

A technology of high and low temperature resistance and hexadecanol, which is used in building thermal insulation materials, building components, buildings, etc., can solve the problems of reduced asphalt performance, poor asphalt compatibility, and impact on use effects, and achieves easy large-scale production and process time. short effect

Inactive Publication Date: 2018-03-23
莫春妹
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Some modifiers added have poor compatibility with asphalt, resulting in reduced performance of asphalt and affecting the use effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The prepared asphalt contains the following components:

[0033] Petroleum asphalt 90%

[0034] SBR 2%

[0035] Powdered Sulfur Chloride 1%

[0036] Montmorillonite 0.5%

[0037] Linolenic Acid 4%

[0038] Glycerin in water 2%

[0039] Cetyl Alcohol 0.5%

[0040] The specific preparation method is as follows:

[0041] First take 9kg of No. 70 petroleum asphalt and pour it into the heating tank, heat it to 180°C, and quickly add 0.4kg of linolenic acid, 0.1kg of powdered sulfur chloride, 0.2kg of styrene-butadiene rubber, 0.05 kg montmorillonite, use a colloid mill to disperse the above mixture at high speed for 1 hour, finally add 0.2kg glycerol aqueous solution and 0.05k cetyl alcohol, raise the temperature to 220°C, continue grinding and dispersing for 1 hour, cool the system to 160°C, and develop After 1 hour, the processed modified asphalt can be obtained for use.

Embodiment 2

[0043] The prepared asphalt contains the following components:

[0044] Natural asphalt 91%

[0045] SBR 1%

[0046] Powdered Sulfur Chloride 2%

[0047] Montmorillonite 1.5%

[0048] Linolenic Acid 2%

[0049] Glycerin in water 1%

[0050] Cetyl Alcohol 1.5%

[0051] The specific preparation method is as follows:

[0052] First take 45.5kg of No. 90 natural asphalt and pour it into the heating tank, heat it to 190°C, and quickly add 1kg of linolenic acid, 1kg of powdered sulfur chloride, 0.5kg of styrene-butadiene rubber powder, 0.75kg montmorillonite, grind the above mixture at high speed for 2 hours with shearing machine dispersing equipment, finally add 0.5kg glycerol aqueous solution and 0.75kg cetyl alcohol, raise the temperature to 240°C, continue grinding and dispersing for 2h, cool down the system to 160°C, After 2 hours of late development, the processed modified asphalt can be obtained for use.

Embodiment 3

[0054] The prepared asphalt contains the following components:

[0055] Petroleum asphalt and natural asphalt mixture 97%

[0056] SBR 0.3%

[0057] Alkane powdered sulfur chloride 0.5%

[0058] Montmorillonite 0.5%

[0059] Linolenic Acid 1%

[0060] Glycerin aqueous solution 0.2%

[0061] Cetyl Alcohol 0.5%

[0062] The specific preparation method is as follows:

[0063] First take 194kg of No. 110 petroleum asphalt and natural asphalt mixture and pour it into the heating tank, heat it to 200°C, and quickly add 2kg of linolenic acid, 1kg of powdered sulfur chloride, and 0.6kg of styrene-butadiene rubber in a stirring state Powder, 1kg montmorillonite, grind the above mixture at high speed for 3 hours with a shearing machine dispersing equipment, finally add 0.4kg kg glycerin aqueous solution and 1kg cetyl alcohol, raise the temperature to 260°C, continue grinding and dispersing for 3 hours, and cool the system to 160°C ℃, after 3 hours of late development, the process...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high and low temperature resistant asphalt added with cetyl alcohol modifier and a processing method thereof. The high and low temperature resistant asphalt is made of base asphalt, styrene-butadiene rubber, powdered sulfur chloride, montmorillonite, linolenic acid, glycerin aqueous solution, and cetyl alcohol. First, the base asphalt is heated, and then linolenic acid and powdered chlorine are added. Sulfur, styrene-butadiene rubber, montmorillonite, and asphalt are modified, and then through a high-speed grinding process, after the dispersion is uniform, glycerin aqueous solution and cetyl alcohol modifier are added to further modify its stability. Finally, the product can be obtained after cooling down and developing in the later stage. The prepared modified asphalt product is not prone to delamination, and the processing flow is short, so it has a good application prospect.

Description

technical field [0001] The invention relates to a road asphalt, in particular to a high and low temperature resistant asphalt added with a modifier and a preparation method thereof, belonging to the field of asphalt processing. Background technique [0002] In recent years, bituminous compositions have been widely used in road paving. As the requirements for road surfaces are increasing, asphalt roads with excellent strength, flow resistance, and wear resistance are required. Therefore, it is necessary to prepare asphalt roads with higher softening points, Asphalt compositions with high mechanical strength such as elastic modulus need to be improved with various copolymer modifiers. [0003] Some modifiers added have poor compatibility with asphalt, resulting in reduced performance of asphalt and affecting the use effect. In terms of patents: CN201010522786.5 is a wide-area modified asphalt preparation technology, using powdered styrene-butadiene rubber as the first modifie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L9/06C08K13/02C08K5/09C08K3/34C08K5/053C08K5/05C08K3/30
CPCC08L95/005C08L2201/08C08L9/06C08K13/02C08K5/09C08K3/34C08K5/053C08K5/05C08K3/30
Inventor 莫春妹
Owner 莫春妹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap