Matte finish-carving ink and preparation method thereof

An ink, fine carving technology, applied in the direction of ink, household appliances, applications, etc., can solve the problems of low gloss and can not meet the demand and so on

Inactive Publication Date: 2018-02-23
佛山市华力达材料科技有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the deficiencies of the above-mentioned prior art, the object of the present invention is to provide a matte engraving ink and its preparation method, aiming at solving the pattern or application of the matte effect of the ceramic glaze and ink in the prior art. The technical problem that cannot meet the demand when the substrate with relatively low gloss is required

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Matte finish-carving ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0082] The matte engraving ink, calculated in parts by weight, includes:

[0083] 15 parts of low-temperature high-boron frit,

[0084] 6 parts of bismuth vanadate,

[0085] Albite 10 parts,

[0086] Barium carbonate 5 parts,

[0087] 1 part fluorite,

[0088] 5 parts of ricinoleic acid polymer,

[0089] Fatty acid ethylhexyl ester 3 parts,

[0090] Fatty acid methyl ester 3 parts,

[0091] 45 parts of white oil.

[0092] Wherein, described albite feldspar comprises the component of following mass fraction:

[0093] Na 2 O 10~13%,

[0094] Al 2 o 3 16-20%,

[0095] SiO 2 65-70%.

[0096] The low-temperature high-boron frit includes the following components in mass fraction:

[0097] B 2 o 3 20%~40%,

[0098] SiO 2 35%~45%,

[0099] Al 2 o 3 2%~5%,

[0100] Na 2 O 10%~15%,

[0101] CaO 10% to 15%.

[0102] Described fluorspar comprises the component of following mass fraction:

[0103] CaF 2 93%~98%,

[0104] Fe2O 3 0.5~1%,

[0105] SiO ...

Embodiment 2

[0113] The matte engraving ink, calculated in parts by weight, includes:

[0114] 17 parts of low-temperature high-boron frit,

[0115] Bismuth vanadate 10 parts,

[0116] Albite 5 parts,

[0117] 8 parts of barium carbonate,

[0118] Lithium fluoride 1.5 parts,

[0119] 4 parts castor oil,

[0120] 3 parts of hydrogenated ricinoleic acid polymer,

[0121] 10 parts of diisobutyl succinate,

[0122] 55 parts of white oil.

[0123] Wherein, described albite feldspar comprises the component of following mass fraction:

[0124] Na 2 O 10~13%,

[0125] Al 2 o 3 16-20%,

[0126] SiO 2 65-70%.

[0127] The low-temperature high-boron frit includes the following components in mass fraction:

[0128] B 2 o 3 20%~40%,

[0129] SiO 2 35%~45%,

[0130] Al 2 o 3 2%~5%,

[0131] Na 2 O 10%~15%,

[0132] CaO 10% to 15%.

[0133] The preparation method of above-mentioned ink comprises the following steps:

[0134] A. Airflow pulverize low temperature high boron ...

Embodiment 3

[0140] The matte engraving ink, calculated in parts by weight, includes:

[0141] 20 parts of low-temperature high-boron frit,

[0142] Bismuth vanadate 5 parts,

[0143] Albite 7 parts,

[0144] 9 parts of barium carbonate,

[0145] Sodium fluorosilicate 2 parts,

[0146] 6 parts of hydrogenated ricinoleic acid polymer,

[0147] 3 parts fatty acid isopropyl ester,

[0148] 5 parts of diisobutyl adipate,

[0149] 40 parts of white oil.

[0150] Wherein, described albite feldspar comprises the component of following mass fraction:

[0151] Na 2 O 10~13%,

[0152] al 2 o 3 16-20%,

[0153] SiO 2 65-70%.

[0154] The low-temperature high-boron frit includes the following components in mass fraction:

[0155] B 2 o 3 20%~40%,

[0156] SiO 2 35%~45%,

[0157] al 2 o 3 2%~5%,

[0158] Na 2 O 10%~15%,

[0159] CaO 10% to 15%.

[0160] The preparation method of above-mentioned ink comprises the following steps:

[0161] A. The low-temperature high-boron...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a matte finish-carving ink and a preparation method thereof. The ink comprises the following components in parts by weight: 15-25 parts of low-temperature high-boron frit, 5-10parts of bismuth vanadate, 5-10 parts of sodium feldspar, 5-10 parts of barium carbonate, 1-3 parts of mineralizer, 5-7 parts of a dispersing agent, 5-15 parts of ester compound and 40-60 parts of solvent. The ink is high in abrasion resistance, the imitated materials are vivid, there is no color difference after ink-jet printing, the lines are matte, the applicable temperature range is wide, theweather resistance is high, and the ink is not easy to crack at low temperature and high temperature; the preparation method is simple in process and suitable for large-scale production.

Description

technical field [0001] The invention relates to the field of ceramic inks, in particular to a matte engraving ink and a preparation method thereof. Background technique [0002] Ceramic ink is used as a ceramic decorative material, and its application is becoming more and more extensive. With the improvement of people's quality of life, the requirements for living environment and quality are getting higher and higher, and the research on the simulation effect of ceramic tile patterns is getting more and more in-depth. Usually the simulation effect of the pattern of the ceramic tile is realized by the glaze or ink painted on the biscuit, but the glaze or ink with the simulation effect can only imitate the pattern with relatively high brightness. Patterns with a matte effect, such as cracks imitating stone, or substrates with relatively low brightness, such as stone, cement bricks, wood grain bricks, etc., the existing ink or glaze cannot meet the demand. [0003] It can be s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/36C09D11/322
CPCC09D11/322C09D11/36
Inventor 钟华龙黄道伟赵胜
Owner 佛山市华力达材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com