Aglaia odorata tea fragrant mulberry silk quilt
A Milanese flower and mulberry silk technology, applied to sleep or relaxation devices, home appliances, bedspreads, etc., to achieve the effects of increasing the added value, shortening the processing process, and enriching material life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0036] The following steps can be used to prepare the Milanese scented mulberry silk quilt:
[0037](1) Put the cooked silkworms that have been emptied of feces and urine on the silk spinning net, and the density of cooked silkworms is 800-900 / ㎡. The silk-spinning net is a flat-spinning silk-spinning net with a mesh width of 2-5 mm and a thickness of 1-2 mm.
[0038] (2) After the cooked silkworms have finished silk spinning, the silk is stripped from the spinning net to obtain a smooth fluffy sheet.
[0039] (3) Use a hydrogen peroxide solution with a temperature of 98-100°C and a concentration of 4% by mass for 30-40 minutes to degumming the wool sheet until the sericin content is 2.5-3.5%.
[0040] (4) Clean the degummed cotton sheet with clean water, and then place it in a dehydrator for dehydration.
[0041] (5) After the dehydrated cotton sheet is treated with impurity removal and shaping, it is dried to obtain a dry cotton sheet for later use; the drying temperature i...
Embodiment 2
[0055] The following steps can be used to prepare the Milanese scented mulberry silk quilt:
[0056] (1) Put the cooked silkworms that have been emptied of feces and urine on the silk spinning net, and the density of cooked silkworms is 800-900 / ㎡. The silk-spinning net is a flat-spinning silk-spinning net with a mesh width of 2-5 mm and a thickness of 1-2 mm.
[0057] (2) After the cooked silkworms have finished silk spinning, the silk is stripped from the spinning net to obtain a smooth fluffy sheet.
[0058] (3) Cook with a hydrogen peroxide solution with a temperature of 98-100°C and a mass percent concentration of 4% for 30-40 minutes, and degumming the wool sheet until the sericin content is 2.5-3.5%; Minutes, add hydrogen peroxide solution weight 1.5-2% ethylene glycol diglycidyl ether.
[0059] (4) Clean the degummed cotton sheet with clean water, and then place it in a dehydrator for dehydration.
[0060] (5) After the dehydrated cotton sheet is treated with impurit...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com