One-time forming pvc composite floor manufacturing process

A composite floor and manufacturing process technology, applied in building structures, other household appliances, floors, etc., can solve the problems of low production efficiency and cumbersome manufacturing process, and achieve the effect of simple manufacturing process and strong controllability

Active Publication Date: 2019-07-19
圣象实业(江苏)有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, after the surface layer, core layer and bottom layer of PVC composite floor are processed and formed, they are laminated by secondary pressing. The production process is cumbersome and the production efficiency is low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The manufacturing process of one-time molding PVC composite flooring comprises the following steps:

[0025] A. Mix the surface layer and the bottom layer according to the weight, put them into the upper layer of the corresponding co-extrusion double-cone machine, the temperature is 150 ° C, and the time is 10 minutes, and then enter the upper layer and the bottom layer of the calender molding machine;

[0026] B. The core layer is mixed according to the weight part, put into the lower layer of the co-extrusion double-cone machine, the temperature is 110°C, the time is 12min, and then it is foamed under the condition of 210-220°C, and then enters the middle layer of the calender molding machine;

[0027] C. The surface layer, core layer, and bottom layer enter the upper, middle, and lower layers of the calendering machine in turn, and perform a calendering composite molding. At the same time, the calendering machine calenders the polyvinyl chloride PVC heat transfer film...

Embodiment 2

[0033] The manufacturing process of one-time molding PVC composite flooring comprises the following steps:

[0034] A. Mix the surface layer and the bottom layer according to the weight parts, put them into the upper layer of the corresponding co-extrusion double cone machine, the temperature is 165 ° C, and the time is 18 minutes, and then enter the upper layer and the bottom layer of the calender molding machine;

[0035] B. The core layer is mixed according to the weight part, put into the lower layer of the co-extrusion double-cone machine, the temperature is 130°C, the time is 16min, and then it is foamed under the condition of 210-220°C, and then enters the middle layer of the calender molding machine;

[0036] C. The surface layer, core layer, and bottom layer enter the upper, middle, and lower layers of the calendering machine in turn, and perform a calendering composite molding. At the same time, the calendering machine calenders the polyvinyl chloride PVC heat transfe...

Embodiment 3

[0042] The manufacturing process of one-time molding PVC composite flooring comprises the following steps:

[0043] A. Mix the surface layer and the bottom layer according to the weight parts, put them into the upper layer of the corresponding co-extrusion double-cone machine, the temperature is 158 ° C, and the time is 14 minutes, and then enter the upper layer and the bottom layer of the calender molding machine;

[0044] B. The core layer is mixed according to the weight part, put into the lower layer of the co-extrusion double-cone machine, the temperature is 120°C, the time is 13min, and then it is foamed under the condition of 210-220°C, and then enters the middle layer of the calender molding machine;

[0045] C. The surface layer, core layer, and bottom layer enter the upper, middle, and lower layers of the calendering machine in turn, and perform a calendering composite molding. At the same time, the calendering machine calenders the polyvinyl chloride PVC heat transfe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of decorative sheet machining, and relates to PVC floors, in particular to a one-time forming type PVC composite floor manufacturing process. The manufacturing process comprises the following steps that parts of a surface layer and parts of a bottom layer are mixed by weight, put onto the upper layer of a co-extrusion double-cone machine and sequentially enter the upper layer and the bottom layer of a calendaring forming machine; parts of a core layer are mixed by weight, put onto the lower layer of the co-extrusion double-cone machine, then subjected to foaming at 210-220 DEG C and enter the middle layer of the calendaring forming machine; one-time calendaring composite forming is conducted, meanwhile, a polyvinyl chloride (PVC) heat transfer film, a polypropylene (PP) heat transfer film or a polyethylene (PE) heat transfer film veneer which is formed through calendaring of the calendaring forming machine is used as a decorative layer to bepasted on the upper surface of the surface layer, and one-time roll forming is conducted through a four-roller press or a five-roller press; and integral forming is achieved through die pressing andcompositing, and one-time forming, cooling and slitting are conducted. The one-time forming type PVC composite floor manufacturing process is simple and high in controllability, a manufactured PVC composite floor has the advantages of being free of formaldehyde, environmentally friendly, non-poisonous, safe, dampproof and the like and has certain anti-microbial and anti-mold effects.

Description

technical field [0001] The invention belongs to the technical field of decorative board processing, and relates to a PVC floor, in particular to a manufacturing process for one-time forming PVC composite floor. Background technique [0002] "PVC floor" refers to the floor made of polyvinyl chloride raw materials. It is made of polyvinyl chloride and its copolymer resin as the main raw material, and fillers, plasticizers, stabilizers, colorants and other auxiliary materials are added to the sheet continuous substrate. Produced by coating process or by calendering, extrusion or extruding process. The main products are: Coiled flooring, made of polyvinyl chloride resin as the main raw material, adding appropriate additives, on the sheet-like continuous substrate, produced by coating process, divided into foamed polyvinyl chloride rolls with substrate There are two types of flooring: PVC flooring and dense PVC coiled flooring with substrates; sheet flooring is made of polyvinyl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F15/10B29C48/00B29C69/00B29D99/00C08L27/06C08K13/02C08K3/26C08K5/12
Inventor 兴丰王素鹏黄玲玲
Owner 圣象实业(江苏)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com