A kind of biological magnetic nano coating and preparation method thereof

A nano-coating and biomagnetic technology, applied in the field of coatings, can solve the problems of high cost and high density, and achieve the effects of wide absorption frequency band, improved water resistance and scrub resistance, and good anti-electromagnetic radiation function

Active Publication Date: 2019-07-26
炫杰复合材料(上海)有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Existing electromagnetic shielding coatings, some of which use metal powder, have high cost and high density

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of biological magnetic nano coating and preparation method thereof
  • A kind of biological magnetic nano coating and preparation method thereof
  • A kind of biological magnetic nano coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The raw material formula is shown in the following table:

[0027]

[0028]

[0029] Among them, the polymer emulsion is styrene-acrylic emulsion; the cationic block copolymer is P(MMA) 20 -b-P(METEA) 10 ; The particle size of nano ferric oxide is 10-20nm; the particle size of nano-lanthanum trioxide is 10-20nm; the defoamer is defoamer CF-16; The pore size of silica airgel is 80-100nm, the porosity is 90%-94%, and the dry density is 40-100kg / m 3 , The thermal conductivity is 0.010~0.025W / (m.K).

[0030] Preparation method: Add polymer emulsion, hyperbranched polyester alkyd resin, cationic block copolymer, ethylene glycol butyl ether, wetting and dispersing agent into a stirrer, stir evenly, then add graphene oxide and nano-ferric oxide , carbonyl iron, nano-lanthanum trioxide, silica aerogel, heavy calcium carbonate, defoamer, just stir evenly.

[0031] The performance of the coating that present embodiment obtains is shown in the table below:

[0032]

...

Embodiment 2

[0036] The raw material formula is shown in the following table:

[0037] serial number material name parts by weight 1 polymer emulsion 25 2 Hyperbranched Polyester Alkyd Resin 8 3 Graphene oxide 2 4 cationic block copolymer 7 5 Ethylene glycol butyl ether 20 6 Nano ferric oxide 2 7 carbonyl iron 0.6 8 Nano-lanthanum trioxide 0.6 9 Silica airgel 2 10 Wetting and dispersing agent 0.2 11 Ground calcium carbonate 24 12 Defoamer 0.3

[0038] Among them, the polymer emulsion is styrene-acrylic emulsion; the cationic block copolymer is P(MMA) 20 -b-P(METEA) 20 ; The particle size of nano ferric oxide is 10-20nm; the particle size of nano-lanthanum trioxide is 10-20nm; the defoamer is defoamer CF-16; The pore size of silica airgel is 80-100nm, the porosity is 90%-94%, and the dry density is 40-100kg / m 3 , The thermal conductivity is 0.010~0.025W / (m.K).

[0039] Preparation method:...

Embodiment 3

[0044] The raw material formula is shown in the following table:

[0045]

[0046]

[0047] Among them, the polymer emulsion is styrene-acrylic emulsion; the cationic block copolymer is P(MMA) 20 -b-P(METEA) 30 ; The particle size of nano ferric oxide is 10-20nm; the particle size of nano-lanthanum trioxide is 10-20nm; the defoamer is defoamer CF-16; The pore size of silica airgel is 80-100nm, the porosity is 90%-94%, and the dry density is 40-100kg / m 3 , The thermal conductivity is 0.010~0.025W / (m.K).

[0048] Preparation method: Add polymer emulsion, hyperbranched polyester alkyd resin, cationic block copolymer, ethylene glycol butyl ether, wetting and dispersing agent into a stirrer, stir evenly, then add graphene oxide and nano-ferric oxide , carbonyl iron, nano-lanthanum trioxide, silica aerogel, heavy calcium carbonate, defoamer, just stir evenly.

[0049] The performance of the coating that present embodiment obtains is shown in the table below:

[0050]

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
sizeaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses bio-magnetic nano-paint and a preparation method thereof. The bio-magnetic nano-paint comprises the following raw materials in parts by weight: 15-30 parts of polymer emulsion, 7-10 parts of hyperbranched polyester alkyd resin, 1-2 parts of graphene oxide, 5-8 parts of cationic segmented copolymers, 10-25 parts of butyl cellosolve, 1-2 parts of nano-ferroferric oxide, 0.5-0.8 parts of carbonyl iron, 0.5-0.8 parts of nano-lanthanum trioxide, 1-3 parts of silicon dioxide aerogel, 0.1-0.3 parts of a wetting and dispersing agent, 21-25 parts of ground calcium carbonate and 0.2-0.4 parts of a defoaming agent. The bio-magnetic nano-paint disclosed by the invention is environment-friendly paint with excellent water resistance and scrubbing resistance and has a good anti-electromagnetic radiation function, and the electromagnetic pollution to the environment is reduced; an absorption band of the paint is wider than that of a common metal shielding material.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a biomagnetic nano coating and a preparation method thereof. Background technique [0002] At present, with the continuous breakthrough and development of computer network technology worldwide, the network has spread all over every corner of our lives, such as mobile phones and laptops we use every day, but correspondingly, we have also pushed ourselves into a Go in an environment full of radiation and pollution. While modern equipment brings us convenience, it also continuously enhances the electromagnetic radiation around us. The pollution produced by electromagnetic radiation will not only interfere with the normal operation of electronic equipment, but also affect human health and ecological balance. The use of electromagnetic shielding materials for electromagnetic shielding protection is the most effective means of protection in daily work and life. [0003] Biomass energy is a k...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D125/14C09D5/23C09D7/61
CPCC08K2003/221C08K2003/2275C08K2003/265C08K2201/011C09D5/00C09D125/14C08L53/00C08K13/04C08K3/22C08K5/56C08K7/26C08K3/26C08K3/04
Inventor 张杰李齐侠顾广新
Owner 炫杰复合材料(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap