High-temperature-resistant anti-aging resin anchoring agent

A resin anchoring agent and anti-aging technology, which is applied in the field of roadway support materials, can solve the problems of high temperature resistance and aging resistance that cannot meet the downhole function, so as to promote the function of fillers, improve high temperature resistance and aging resistance, and improve compatibility effect

Inactive Publication Date: 2017-12-01
常州瑞坦商贸有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main technical problem to be solved by the present invention is to provide a high temperature resistant and anti-aging resin anchoring agent in view of the inherent properties of the current common resin anchoring agent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant anti-aging resin anchoring agent

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0023]Weigh the montmorillonite and put it into a jet mill to crush for 10 minutes, screen out the montmorillonite particles with a particle size of 1mm, mix the montmorillonite particles with hydrochloric acid with a concentration of 0.5mol / L at a mass ratio of 1:5 and let it stand Immerse for 20 minutes, filter, and separate to obtain the filter residue. Put the alpine golden moss into a stone mortar and mash for 20 minutes to obtain moss slurry. Mix the filter residue and the moss slurry according to the mass ratio of 1:3 and put it in the cultivation room. The temperature is 23°C. 1. Under the condition of 50% relative air humidity, let it stand for cultivation for 8 days, moss grows on the filter residue, obtain the pre-modified filter residue, and the pre-modified filter residue and massfraction are 30% sodium silicate solution by mass ratio as 1: 5. After mixing, put it into an ultrasonic vibrator, and put it into an ultrasonic vibrator at a power of 200W and a frequency...

example 2

[0025] Weigh the montmorillonite and put it into the jet mill for 13 minutes to crush it, screen out the montmorillonite particles with a particle size of 2 mm, mix the montmorillonite particles with hydrochloric acid with a concentration of 0.5mol / L according to the mass ratio of 1:5 and let it stand Immerse for 25 minutes, filter, and separate to obtain the filter residue. Put the alpine golden moss into a stone mortar and mash for 25 minutes to obtain moss slurry. Mix the filter residue and the moss slurry according to the mass ratio of 1:3 and put it in the cultivation room. The temperature is 25°C 1. Under the condition of 55% relative air humidity, let it stand for cultivation for 9 days, moss grows on the filter residue, obtain the pre-modified filter residue, and the pre-modified filter residue and massfraction are 30% sodium silicate solution by mass ratio as 1: 5. After mixing, put it into an ultrasonic vibrator, and use ultrasonic vibration and impregnation for 25min...

example 3

[0027] Weigh the montmorillonite and put it into a jet mill for crushing for 15 minutes, screen out the montmorillonite particles with a particle size of 3mm, mix the montmorillonite particles with hydrochloric acid with a concentration of 0.5mol / L according to the mass ratio of 1:5 and let it stand Immerse for 30 minutes, filter, and separate to obtain the filter residue. Put the alpine golden moss into a stone mortar and mash for 30 minutes to obtain moss slurry. Mix the filter residue and the moss slurry according to the mass ratio of 1:3 and put it in the cultivation room. The temperature is 27°C 10 days under the condition of 60% relative air humidity, moss grows on the filter residue, and the pre-modified filter residue is obtained, and the pre-modified filter residue and mass fraction are 30% sodium silicate solution by mass ratio: 5. After mixing, put it into an ultrasonic vibrator, use ultrasonic vibration and impregnation for 30min under the condition of power of 300W...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature-resistant anti-aging resin anchoring agent, belonging to the technical field of roadway support materials. According to the invention, montmorillonite is crushed, then impregnated with hydrochloric acid and finally undergoes filtering and separation so as to obtain filter residues; the filter residues are mixed with moss pulp prepared from Polytrichum alpinum for culture, then the cultured filter residues undergo oscillation together with a sodium silicate solution, and the obtained mixture is subjected to filtering and separating so as to obtain a filter cake; the obtained filter cake and hydrochloric acid are subjected to oscillation, dipping and heating reaction, and then filtering and separating are carried out so as to obtain a pre-modified filter cake; the pre-modified filter cake is carbonized and then undergo mixing and grinding together with natural resin so as to obtain a modified self-made high-temperature-resistant anti-aging filling material; the filling material, bisphenol A type unsaturated polyester resin, dimethylaniline and tetrachlorobenzoquinone are uniformly mixed to obtain a component A; lauroyl peroxide, dibenzoyl peroxide and water are uniformly mixed to obtain a component B; and in use, the component A and the component B are mixed so as to obtain the high-temperature-resistant anti-aging resin anchoring agent. The high-temperature-resistant anti-aging resin anchoring agent has excellent ageing resistance, can maintain high compressive strength and anchoring force under a high temperature condition and exerts good supporting effect in a severe underground environment.

Description

technical field [0001] The invention discloses a high-temperature-resistant and anti-aging resin anchoring agent, which belongs to the technical field of roadway support materials. Background technique [0002] The method of firmly fixing metal bolts, deformed steel bars, and internal threaded pipes in concrete and rock foundation holes to replace embedded steel bars is called "anchor". Anchoring methods are generally divided into two types: the metal expansion bolt method and the chemical bonding method. Metal expansion bolts are fixed by mechanical force to expand the metal sheet and generate friction after squeezing the hole wall. They can only be used for anchoring non-structural parts under static loads, and their application range is narrow. The chemical bond anchoring is to use chemical adhesive to fix the metal rod. When the adhesive is cured, the matrix-adhesive layer-metal rod are firmly combined into a whole. Therefore, chemical anchoring is essentially an overa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/18C04B20/02C04B20/04C04B20/10C04B111/20
CPCC04B20/023C04B20/04C04B20/1055C04B26/18C04B2111/20C04B2201/50C04B24/121C04B24/005C04B24/00C04B22/002C04B14/104
Inventor 朱勇林茂兰潘宏梅
Owner 常州瑞坦商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com