A kind of preparation method of graphene modified residual stress sensitive coating

A graphene modification and residual stress technology, which is applied in coatings, chemical instruments and methods, metal material coating technology, etc., can solve problems such as the inability to obtain stress distribution, and achieve monitoring of coating integrity and safe service status Effect

Active Publication Date: 2020-06-30
AVIC BEIJING INST OF AERONAUTICAL MATERIALS
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ultrasonic testing technology is a non-destructive testing method, which has the advantages of strong penetrating power and good sound beam directionality. However, the result of ultrasonic testing stress is the average value of ultrasonic waves passing through a certain path inside the sample. Although it is not destructive, it cannot Get the stress distribution of the structure as a whole
Therefore, so far there is no technology suitable for non-destructive, online, real-time monitoring of coatings on remanufactured parts by thermal spraying.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of graphene modified residual stress sensitive coating
  • A kind of preparation method of graphene modified residual stress sensitive coating
  • A kind of preparation method of graphene modified residual stress sensitive coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The invention provides a method for preparing a graphene-modified residual stress-sensitive coating, comprising the following steps: Step (1) weighs 30g of strontium carbonate (SrCO 3 ), 20g of alumina (Al 2 o 3 ), 10g silicon dioxide (SiO 2 ), weighed 500ml of alcohol, and placed the mixed powder and alcohol in a planetary ball mill for ball milling and mixing for 70 minutes until the alcohol was completely volatilized. Then it was transferred to a corundum boat and treated in a high-temperature furnace at a temperature of 940°C for 4 hours.

[0038] Step (2) Weigh 1 g of graphene oxide and disperse it in 300 ml of absolute ethanol with ultrasonic vibration to prepare a graphene oxide dispersion. The ultrasonic dispersion time is 120min, and the ultrasonic frequency is 15Hz.

[0039] Step (3) takes by weighing 2g europium oxide (Eu 2 o 3 ) and 1g dysprosium oxide (Dy 2 o 3 ), add 300ml of dilute hydrochloric acid to dissolve, and add 300ml of distilled water at...

Embodiment 2

[0048] On the basis of the foregoing embodiments, the steps of this embodiment are: Step (1) weighs 60g of strontium carbonate (SrCO 3 ), 30g of alumina (Al 2 o 3 ), 20g silicon dioxide (SiO 2 ), weighed 1000ml of alcohol, and placed the mixed powder and alcohol in a planetary ball mill for ball milling and mixing for 80 minutes until the alcohol was completely volatilized. Then it was transferred to a corundum boat and treated in a high-temperature furnace at a temperature of 1000°C for 5 hours.

[0049] Step (2) Weigh 2 g of graphene oxide and disperse it in 600 ml of absolute ethanol with ultrasonic vibration to prepare graphene oxide dispersion. The ultrasonic dispersion time is 140min, and the ultrasonic frequency is 15Hz.

[0050] Step (3) takes by weighing 4g europium oxide (Eu 2 o 3 ) and 2g dysprosium oxide (Dy 2 o 3 ), add 600ml of dilute hydrochloric acid to dissolve, and add 600ml of distilled water at the same time, with a high-speed mixer at a rate of 500...

Embodiment 3

[0056] On the basis of the foregoing embodiments, the steps of the present embodiment are: step (1) takes by weighing 80g of strontium carbonate (SrCO 3 ), 60g of alumina (Al 2 o 3 ), 20g silicon dioxide (SiO 2 ), weigh 1000ml of alcohol, place the mixed powder and alcohol in a planetary ball mill for ball milling and mix for 90min until the alcohol is completely volatilized. Then it was transferred to a corundum boat, and the treatment temperature was 1040°C in a high-temperature furnace, and the treatment time was 7 hours.

[0057] Step (2) Weigh 4 g of graphene oxide and disperse it in 1000 ml of absolute ethanol with ultrasonic vibration to prepare graphene oxide dispersion. The ultrasonic dispersion time is 160min, and the ultrasonic frequency is 15Hz.

[0058] Step (3) takes by weighing 3g europium oxide (Eu 2 o 3 ) and 1.5g dysprosium oxide (Dy 2 o 3 ), add 600ml of dilute hydrochloric acid to dissolve, and add 600ml of distilled water at the same time, with a h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a residual stress sensitive coating modified through graphene. The preparation method comprises the steps that (1) strontium carbonate (CaCO3), aluminum oxide (Al2O3), silicon dioxide (SiO2) and alcohol are weighed and mixed; (2) graphene oxide is dispersed in absolute ethyl alcohol; (3) dilute hydrochloric acid is used for dissolution, and meanwhile, a certain amount of distilled water is added; (4) modification and element regulation and control of Dy3+ / Eu3+ are achieved through the graphene, and finally / Dy3+ / Eu3+ powder modified through the graphene is obtained through drying in the vacuum atmosphere; (5) CaAl2Si2O8:Eu3+, Dy3+ powder which has the powder particle size of about 1-3 [mu]m and modified through the graphene is obtained through screening; and (6) a graphene co-doped Dy3+ / Eu3+ WC-CO powder material with a certain particle size is obtained, and a visual SrAl2O4:Eu3+, Dy3+co-doped WC-CO abrasion-resistant coating is prepared through the thermal spraying technique. By the adoption of the scheme, the particle sizes of spraying materials are uniform, the purity is high, the graphene content in the powder is high, and the preparation method can be used for preparing the residual stress sensitive coating through the thermal spraying technique.

Description

technical field [0001] The invention belongs to the preparation of graphene-modified SrAl applied to thermal spraying technology 2 Si 2 o 8 :Eu 3+ , Dy 3+ The technical field of co-doped WC-Co residual stress-sensitive coating, especially relates to a method for preparing a graphene-modified residual stress-sensitive coating. Background technique [0002] The preparation of wear-resistant coatings by thermal spraying is one of the main technologies applied in remanufacturing engineering. It can be used not only to improve the surface wear resistance of new parts, but also to repair the geometric dimensions of failed parts, giving waste parts a new life cycle, It saves energy and material waste caused by manufacturing new products, and has wide application potential in high-tech engineering fields such as aerospace, petrochemical, and nuclear power plants. [0003] Wear-resistant coatings generally serve for a long time under harsh working conditions such as high loads a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C4/06C23C4/126C23C4/129C23C4/131C23C4/134C09K11/65C09K11/64
CPCC09K11/65C09K11/7792C23C4/06
Inventor 田浩亮张欢欢王长亮郭孟秋汤智慧崔永静高俊国周子民
Owner AVIC BEIJING INST OF AERONAUTICAL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com