A kind of mildew-proof sponge material and preparation method thereof

A sponge and material technology, which is applied in the field of mildew-proof sponge materials and its preparation, can solve the problems of low safety, high cost, poor heat resistance, etc., and achieve the effects of improving internal structure, good resilience performance, and reducing side reactions

Active Publication Date: 2019-04-05
秦皇岛高鹏泡沫塑料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, antibacterial agents can be added to improve the antibacterial performance. The commonly used antibacterial agents can be divided into two categories: inorganic antibacterial agents and organic antibacterial agents. The former has higher heat resistance, but the cost is high, and the latter has higher sterilization efficiency. , the amount of addition is small, but there are disadvantages such as poor heat resistance and low safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A preparation method of mildew-proof sponge material, comprising the following steps:

[0032] (1) Add melamine to the formaldehyde solution, add sodium acetate and sodium borate, and react with 300W intermittent microwave for 4 minutes to obtain melamine formaldehyde resin. Add polyvinyl butyral, polyvinyl alcohol and ethylene glycol dimethacrylate while stirring Alcohol ester, nitrogen gas, 300W intermittent microwave reaction for 8 minutes, adjust pH to neutral, dehydrate to obtain modified resin;

[0033] (2) Mix and stir the modified resin obtained in step (1) with surfactant and foaming agent evenly to obtain the first material, which is set aside;

[0034] (3) Mix glutaraldehyde, imidazoline biguanide sulfate and liquid curing agent evenly, slowly add isooctyl mercaptopropionate dropwise while stirring, and continue stirring for 2 hours after the dropwise addition to obtain the second material;

[0035] (4) Preheat the first material obtained in step (2) to 30°C...

Embodiment 2

[0043] A preparation method of mildew-proof sponge material, comprising the following steps:

[0044] (1) Add melamine to the formaldehyde solution, add sodium acetate and sodium borate, and react with 450W intermittent microwave for 5 minutes to obtain melamine formaldehyde resin. Add polyvinyl butyral, polyvinyl alcohol and ethylene dimethacrylate while stirring Alcohol ester, feed nitrogen, 450W intermittent microwave reaction for 10 minutes, adjust pH to neutral, dehydrate to obtain modified resin;

[0045] (2) Mix and stir the modified resin obtained in step (1) with surfactant and foaming agent evenly to obtain the first material, which is set aside;

[0046] (3) Mix glutaraldehyde, imidazoline biguanide sulfate and liquid curing agent evenly, slowly add isooctyl mercaptopropionate dropwise while stirring, and continue stirring for 3 hours after the dropwise addition to obtain the second material;

[0047](4) Preheat the first material obtained in step (2) to 40°C, then...

Embodiment 3

[0055] A preparation method of mildew-proof sponge material, comprising the following steps:

[0056] (1) Add melamine to the formaldehyde solution, add sodium acetate and sodium borate, react in 450W intermittent microwave for 4 minutes to obtain melamine formaldehyde resin, add polyvinyl butyral, polyvinyl alcohol and ethylene glycol dimethacrylate while stirring Alcohol ester, feed nitrogen, 450W intermittent microwave reaction for 9 minutes, adjust pH to neutral, dehydrate to obtain modified resin;

[0057] (2) Mix and stir the modified resin obtained in step (1) with surfactant and foaming agent evenly to obtain the first material, which is set aside;

[0058] (3) Mix glutaraldehyde, imidazoline biguanide sulfate and liquid curing agent evenly, slowly add isooctyl mercaptopropionate dropwise while stirring, and continue stirring for 2 hours after the dropwise addition to obtain the second material;

[0059] (4) Preheat the first material obtained in step (2) to 35°C, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a mold-proof sponge material and a preparation method thereof. The method comprises the following steps: firstly, preparing a first material by adopting modified resin, surfactant and foaming agent; preparing a second material by adopting glutaraldehyde, imidazoline biguanide sulfate, liquid curing agent and isooctyl sulfhydrate; slowly adding the preheated first material into the second material and preparing into a mixture; and foaming, thereby acquiring the mold-proof sponge material. The foaming is sufficient, the elasticity is excellent, the molecular chains of glutaraldehyde and imidazoline biguanide sulfate are mutually intertwined and penetrate into the holes of the sponge material and a mold-proof effect is achieved. The sponge material provided by the invention has excellent mechanical property and anti-mold property.

Description

technical field [0001] The invention relates to the technical field of sponge materials, in particular to a mildew-resistant sponge material and a preparation method thereof. Background technique [0002] Sponge has good water absorption and is a porous material, usually used for cushioning materials or cleaning items. Commonly used sponges are made of wood cellulose fibers or expanded plastic polymers, and there are a few natural sponges made of sponge animals that can be used for body cleaning or painting. In addition, there are three types of synthetic sponges, namely low-density polyether (non-absorbent sponge), polyvinyl alcohol (highly absorbent material, no obvious pores) and polyester. [0003] Under suitable temperature and humidity conditions, microorganisms (bacteria and mold) will proliferate in the pores of the sponge, and the secretion of the mold will cause the biodegradation of the sponge material. Higher requirements are put forward for the hygienic perfor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L61/28C08L29/14C08L29/04C08K13/02C08K5/07C08K5/3445C08K5/103C08K5/098C08K3/38C08J9/10C08J9/00
CPCC08J9/00C08J9/105C08J2203/04C08J2361/28C08J2429/04C08J2429/14C08K2003/387C08L61/28C08L2203/14C08L2205/025C08L2205/035C08L29/14C08L29/04C08K13/02C08K5/07C08K5/3445C08K5/103C08K5/098C08K3/38
Inventor 李忠
Owner 秦皇岛高鹏泡沫塑料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More