480mpa grade galvanized steel strip and its production method

A production method, 480mpa technology, applied in hot-dip plating process, coating, metal material coating process, etc., can solve the problems of lack of applicability, extremely high requirements for rapid cooling capacity, high cost of precious alloys, and reduce inclusions The probability of defects, the effect of improving the solid solution strengthening effect, and reducing the difficulty of production control

Active Publication Date: 2019-01-25
HBIS COMPANY LIMITED HANDAN BRANCH COMPANY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

More importantly, in order to ensure the corrosion resistance of automobile sheets, the use of galvanized automobile sheets is also increasing year by year, especially the demand for galvanized automobile sheets with a tensile strength greater than or equal to 480MPa is increasing day by day; The method of galvanized automobile sheet greater than 480MPa is mainly a phase transformation strengthening method such as dual-phase steel, which is characterized by adding martensite forming elements such as Cr and Mo, and using phase transformation to improve the tensile strength of the steel; the cost of this process is expensive. At the same time, it has extremely high requirements on the rapid cooling capacity of galvanizing equipment, and it does not have the applicability for general promotion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 480mpa grade galvanized steel strip and its production method
  • 480mpa grade galvanized steel strip and its production method
  • 480mpa grade galvanized steel strip and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-13

[0016] Examples 1-13: The final chemical composition and process conditions of the production method of the 480MPa grade galvanized steel strip are as follows.

[0017] (1) The galvanized steel strip is prepared by converter smelting, LF refining, continuous casting, hot rolling, cold rolling, continuous annealing, and galvanizing. The chemical composition of the casting after the continuous casting process is shown in Table 1:

[0018] Table 1: Casting Chemical Composition

[0019]

[0020] (2) Hot rolling process:

[0021] During the hot rolling process, the solid solution and precipitation of the second phase particles, the deformation and recrystallization of austenite, and the transformation of ferrite will occur, so hot rolling is an important part of quality control; The joint setting of temperature and the control of the cooling in the front section after finishing rolling can lead to the precipitation of dispersed fine two-phase particles and realize grain refinem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses 480MPa-grade galvanized strip steel. The 480MPa-grade galvanized strip steel comprises, by mass, 0.05-0.09% of C, 0.05% or less of Si, 0.8-1.0% of Mn, 0.016% or less of P, 0.008% or less of S, 0.015-0.035% of Nb, 0.020-0.045% of Als, 0.007% or less of N, 0.015-0.035% of Ti, 0.0015-0.0030% of Ca, and the balance Fe. A production method comprises the steps that converter smelting and LF refining are conducted in a low-nitrogen mode; protective continuous casting is conducted, and nitrogen is controlled to be increased; and calcium treatment is conducted after refining is completed, wherein the mass percent of acid-insoluble aluminum in molten steel is smaller than or equal to 45 ppm, the ratio of the mass percent of the acid-insoluble aluminum to that of calcium is 0.5-1.5, and the ratio of the mass percent of the acid-insoluble aluminum to that of acid soluble aluminum is 0.05-0.20. According to the 480MPa-grade galvanized strip steel, the production cost is low, the overall mechanical performance of the product is superior, and the surface quality meets the requirements of FB surface levels in GB2518 and EN10346.

Description

technical field [0001] The invention belongs to the technical field of metallurgical plate production, in particular to a 480MPa grade galvanized steel strip and a production method thereof. Background technique [0002] With the growth of automobile production, people pay more and more attention to the emission of automobile exhaust. The application of high-strength steel in automobiles, on the one hand, is conducive to realizing the lightweight of automobiles and reducing automobile exhaust emissions; on the other hand, it also improves the safety of people in the car. More importantly, in order to ensure the corrosion resistance of automobile sheets, the use of galvanized automobile sheets is also increasing year by year, especially the demand for galvanized automobile sheets with a tensile strength greater than or equal to 480MPa is increasing day by day; The method of galvanized automobile sheet greater than 480MPa is mainly a phase transformation strengthening method ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/12C22C38/06C22C38/14C21D8/02C23C2/06C23C2/26C23C2/40
CPCC21D8/0226C21D8/0263C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C23C2/06C23C2/26C23C2/40
Inventor 许斌石建强赵渭良刘守显孙海燕蒋建朋李守华杨西鹏
Owner HBIS COMPANY LIMITED HANDAN BRANCH COMPANY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products