Polyethylene composition, foamed bead and preparation method thereof, and foamed bead molding body

A technology of polyethylene foaming and polyethylene, which is applied in the field of polyethylene compositions, and can solve the problems of high price of polyethylene foaming beads, limited application fields, and high equipment costs

Active Publication Date: 2017-11-03
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the process is intermittent and complex, with high equipment costs and technical barriers, so the price of the obtained polyethylene foam beads is relatively high, which limits its application field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene composition, foamed bead and preparation method thereof, and foamed bead molding body
  • Polyethylene composition, foamed bead and preparation method thereof, and foamed bead molding body
  • Polyethylene composition, foamed bead and preparation method thereof, and foamed bead molding body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0035] According to a preferred embodiment of the present invention, the polyethylene composition is figure 1 Prepared in the shown multi-reactor parallel device, described multi-reactor parallel device comprises first reactor 1, second reactor 2, third reactor 3, solid / liquid (gas) separator 4, homogenizer The silo 5 and the melt granulation system 6, wherein the first reactor 1, the second reactor 2 and the third reactor 3 are connected in parallel, and the number of the solid / liquid (gas) separator 4 is three One, communicated with the first reactor 1, the second reactor 2 and the third reactor 3 respectively, the component A produced by the first reactor 1, the component B produced by the second reactor 2 and the component B produced by the third reactor The component C prepared by the reactor 3 is phase-separated in different solid / liquid (gas) separators 4, and then the phase-separated component A, component B and component C are sent to the homogenizer in proportion si...

Embodiment 1

[0055] This example is used to illustrate the polyethylene composition, expanded beads and expanded bead molded body provided by the present invention and the preparation method thereof.

[0056] (1) Preparation of polyethylene composition:

[0057] The polyethylene composition provided in this embodiment contains component A, component B, component C, cell nucleating agent, lubricant and cell control agent. Wherein, component A, component B and component C are linear low density polyethylene (LLDPE) of ethylene / alpha olefin copolymerization, wherein, component A and component B adopt metallocene catalyst to prepare (the metallocene The catalyst system is the supported metallocene catalyst prepared by CN102453124A embodiment 1, the same below), and component C is prepared by using Ziegler-Natta catalyst (the Ziegler-Natta catalyst system is prepared by CN101838351A embodiment 1 prepared Ziegler-Natta catalyst system, the same below). Specific steps are as follows:

[0058] ...

Embodiment 2

[0076] This example is used to illustrate the polyethylene composition, expanded beads and expanded bead molded body provided by the present invention and the preparation method thereof.

[0077] (1) Preparation of polyethylene composition:

[0078] The polyethylene composition provided in this embodiment contains component A, component B, component C, cell nucleating agent, lubricant and cell control agent. Among them, component A, component B and component C are linear low-density polyethylene (LLDPE) copolymerized with ethylene / α olefin, wherein, component A and component B are prepared by metallocene catalyst, and component C is obtained by using Ziegler-Natta catalysts were prepared. Specific steps are as follows:

[0079] Add ethylene, alpha olefin, hydrogen and nitrogen into the fluidized bed gas phase reactor, then add the catalyst system, and then polymerize under the conditions of temperature 84-88°C and pressure 1.8-2.0MPa to obtain components A, Component B and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The present invention relates to the field of polymers, and particularly provides a polyethylene composition, a foamed bead and a preparation method thereof, and a foamed bead molding body. The polyethylene composition comprises a component A, a component B, a component C and a cell nucleating agent, wherein the component A is ethylene / alpha-olefin copolymerized linear low-density polyethylene, has the melt index MIA of 0.01-2 g / 10 min, and has the density [rho]A of 0.880-0.936 g / cm<3>, the component B is ethylene / alpha-olefin copolymerized linear low-density polyethylene, has the melt index MIB of 2.1-9.9 g / 10 min, and has the density [rho]B of 0.910-0.930 g / cm<3>, and the component C is ethylene / alpha-olefin copolymerized linear low-density polyethylene, has the melt index MIC of 10-80 g / 10 min, and has the density [rho]C of 0.880-0.930 g / cm<3>. The foamed bead prepared from the polyethylene composition has the uniform and compact cells, and the prepared foamed bead molding body has the high compressive strength.

Description

technical field [0001] The invention relates to a polyethylene composition, a polyethylene foam bead, a preparation method of the polyethylene foam bead and a molded polyethylene foam bead. Background technique [0002] Compared with polypropylene foamed beads, polyethylene foamed beads are softer due to their light weight, good mechanical properties including low-temperature impact resistance, higher closed cell ratio, and good resilience. Surface, and can be molded to obtain special shape products and other characteristics. Polyethylene foam beads are a polymer foam material with a wide range of uses. Compared with polystyrene series resin foamed bead molding products, polyethylene foamed bead molded products obtained by molding polyethylene foamed beads have chemical resistance, high toughness, high heat resistance, Good compression resilience and other excellent properties. However, polyethylene resin is a semi-crystalline polymer with a generally linear structure. Wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08J9/18C08J9/228
CPCC08J9/18C08J9/228C08J2323/08C08J2423/08C08L23/0815C08L2203/14C08L2205/025C08L2205/03
Inventor 郭鹏吕明福张师军徐耀辉高达利权慧邹浩邵静波杨庆泉初立秋
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com