Preparation method of cspb2br5 nanosheets

A technology of nanosheets and oleic acid, applied in the direction of nanotechnology, nanotechnology, chemical instruments and methods, etc., to achieve the effect of stable light response and wide application prospects

Active Publication Date: 2019-04-02
北京京通光能科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, none of the above reports involved the detection of CsPb 2 Br 5 Tuning the morphology of nanosheets to realize the regulation of their luminescent properties, and their applications in green LEDs and photodetection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of cspb2br5 nanosheets
  • Preparation method of cspb2br5 nanosheets
  • Preparation method of cspb2br5 nanosheets

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Example 1 CsPb 2 Br 5 preparation of

[0030] Preparation of CsPb by hot injection method 2 Br 5 Nanosheets, the preparation steps are:

[0031] (1) Mix 625mg of cesium stearate, 10ml of octadecene and 0.5ml of oleic acid under the environment of feeding nitrogen and maintaining mechanical magnetic stirring, heating to 140°C and stirring for 0.5h to obtain a cesium oleate solution;

[0032] (2) Mix 100mg of lead bromide, 7.5ml of octadecene, 0.5ml of octylamine and 0.5ml of oleic acid, heat to 100°C and mix and stir for 0.5h to obtain PbBr 2 Precursor solution;

[0033] (3) Add 0.375ml of cesium oleate solution to PbBr by hot injection method 2 Precursor solution, the two were mixed and stirred for 3 hours to obtain a crude product, which cannot be used directly because of the presence of ligands on the surface of the crude product, and must be purified. The purification method is to add the same amount of toluene as the crude product, centrifuge at 8000r for 5mi...

Embodiment 2

[0034] Example 2 CsPb 2 Br 5 preparation of

[0035] Preparation of CsPb by hot injection method 2 Br 5 Nanosheets, the preparation steps are:

[0036] (1) Mix 625mg of cesium stearate, 10ml of octadecene and 0.5ml of oleic acid under the environment of feeding nitrogen and maintaining mechanical magnetic stirring, heating to 140°C and stirring for 0.5h to obtain a cesium oleate solution;

[0037] (2) Mix 100mg of lead bromide, 7.5ml of octadecene, 0.5ml of octylamine and 0.5ml of oleic acid, heat to 120°C and mix and stir for 0.5h to obtain PbBr 2 Precursor solution;

[0038] (3) Add 0.375ml of cesium oleate solution to PbBr by hot injection method 2 Precursor solution, the two were mixed and stirred for 3h, and the crude product was purified to obtain CsPb 2 Br 5 Nanosheets.

Embodiment 3

[0039] Example 3 CsPb 2 Br 5 preparation of

[0040] Preparation of CsPb by hot injection method 2 Br 5 Nanosheets, the preparation steps are:

[0041] (1) Mix 625mg of cesium stearate, 10ml of octadecene and 0.5ml of oleic acid under the environment of feeding nitrogen and maintaining mechanical magnetic stirring, heating to 140°C and stirring for 0.5h to obtain a cesium oleate solution;

[0042] (2) Mix 100mg of lead bromide, 7.5ml of octadecene, 0.5ml of octylamine and 0.5ml of oleic acid, heat to 140°C and mix and stir for 1h to obtain PbBr 2 Precursor solution;

[0043] (3) Add 0.375ml of cesium oleate solution to PbBr by hot injection method 2 Precursor solution, the two were mixed and stirred for 3h, and the crude product was purified to obtain CsPb 2 Br 5 Nanosheets.

[0044] The CsPb prepared by embodiment 1-3 2 Br 5 Nanosheets were dispersed in toluene for preservation.

[0045] figure 1 Be the CsPb prepared under the different temperatures of embodiment 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
thicknessaaaaaaaaaa
luminous efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of an adjustable luminescent CsPb2Br5 nanosheet, a product and application thereof. The preparation method comprises the following steps: under nitrogen protection, mixing cesium stearate, octadecene and oleic acid to prepare a caesium oleate solution; additionally, mixing lead bromide, octadecene, octylame and oleic acid, heating and stirring to obtain a PbBr2 precursor solution; and then adding the caesium oleate solution into the PbBr2 precursor solution, mixing and stirring to obtain the CsPb2Br5 nanosheet. Different sizes of CsPb2Br5 nanosheets are obtained by regulating and controlling the reaction temperature of preparing the PbBr2 precursor solution to be 100 to 140 DEG C, and the photoluminescence gradually changes into green light from blue light. The obtained CsPb2Br5 nanosheets can be used for preparing light-emitting diodes, solar cells or photoelectric detectors, and the light-emitting efficiency of high-monochromaticity green light LEDs constructed by preparing the CsPb2Br5 nanosheets reaches 34.49 lm / W.

Description

technical field [0001] The invention belongs to the field of nanometer materials and relates to CsPb 2 Br 5 The preparation method of nanosheets also relates to the products and applications obtained by this preparation method. Background technique [0002] Inorganic perovskite nanomaterials (CsPb 2 x 5 , X=Cl, Br, I) is a new type of functional material, which has special properties in light-emitting diodes, solar cells, photodetectors, etc., and is widely used in the field of optoelectronic devices. In recent years, CsPb2X5 nanomaterials have attracted the attention of a large number of researchers, especially their morphology and applications. For example, "Applied Chemistry International Edition" (Angew.Chem.Int.Ed, 2016, 55, 8328) of the German Chemical Society reported a fast ion exchange method, which successfully prepared a large amount of highly efficient luminescent CsPb 2 Br 5 Nanosheets; American Chemical Society's "Advanced Optical Materials" (Adv.Opt.Mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G21/00C09K11/66B82Y40/00H01L33/50H01L31/08B82Y30/00
CPCB82Y30/00B82Y40/00C01G21/006C01P2002/72C01P2004/03C01P2004/04C01P2004/24C01P2004/62C01P2004/64C09K11/665H01L31/08H01L33/502
Inventor 臧志刚韩层李存龙唐孝生
Owner 北京京通光能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com