Method for preparing micro-capsule containing high light-effect rare earth compounding matter

A rare earth complex and microcapsule technology is applied in the field of preparation of microcapsules containing rare earth complexes with high optical efficiency

Inactive Publication Date: 2007-10-03
SHANDONG UNIV
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, using LbL technology as an assembly method, different core template materials with a diameter of several microns are selected, the process parameters such as the chemical composition and ratio of the deposited polyelectrolyte and rare earth complexes are set, and the rare earth complexes are introduced at different stages of assembly. The method of obtaining microcapsules containing luminescent rare earth complexes in the shell with different shell layers has not been reported after searching

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing micro-capsule containing high light-effect rare earth compounding matter
  • Method for preparing micro-capsule containing high light-effect rare earth compounding matter
  • Method for preparing micro-capsule containing high light-effect rare earth compounding matter

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Embodiment 1. The preparation method of rare earth complex microcapsules containing high light efficiency, the steps are as follows:

[0051] (1) Select Europium(III) β-diketone complex Eu(DBM) 3 Phen;

[0052] (2) join the sodium chloride aqueous solution that concentration is 30mg / ml;

[0053] (3) With step (2) solution as solvent, select the anionic polyelectrolyte polystyrene sulfonate (PSS) that molecular weight is 70,000, mix its concentration and be the solution of 2.0mg / ml;

[0054] (4) select the cationic polyelectrolyte polyallyl ammonium chloride (PAH) that molecular weight is 70,000, take step (2) solution as solvent, mix its concentration and be the solution of 2.0mg / ml;

[0055] (5) by Eu(DBM) 3 Phen and PSS mass ratio are 1: 2 mixing the solution that step (1) obtains and the solution that step (3) obtains;

[0056] (6) by Eu(DBM) 3 Phen and PAH mass ratio are 1: 2 mixing the solution that step (1) obtains and the solution that step (4) obtains;

[...

Embodiment 2

[0066] Embodiment 2. The preparation method of rare earth complex microcapsules containing high light efficiency, the steps are as follows:

[0067] (1) Selection of rare earth complexes Eu(DBM) 3 Phen; with reference to embodiment 1 step (1)-(9) method, use MnCO 3 As template microspheres, make each milliliter solution contain 2.0×10 8 Microcapsules were deposited for 600 seconds, centrifuged at 3000rps for 600 seconds, and washed 3 times in ultrapure water to prepare Eu(DBM) 3 Solid Microcapsules of Phen {MnCO 3 [(Eu(DBM) 3 Phen / PAH)(Eu(DBM) 3 Phen / PSS)] 4} and hollow microcapsules [(Eu(DBM) 3 Phen / PAH)(Eu(DBM) 3 Phen / PSS)] 4 ;

[0068] (2) Containing Eu(DBM) 3 The microcapsule film of Phen is complete and the structure is intact; the fluorescence performance of the microcapsule is excellent, and only one layer of Eu(DBM) is deposited in the shell 3 When Phen, the microcapsules emit light visible to the naked eye under the excitation of ultraviolet light; hollow E...

Embodiment 3

[0069] Example 3. The preparation method of microcapsules containing rare earth complexes with high light efficiency, the steps are as follows:

[0070] (1) Select the rare earth complex Eu(TTA) 3 Phen; with reference to embodiment 1 step (1)-(9) method, make every milliliter solution contain 5.0 * 10 7 Microcapsules were deposited for 600 seconds, centrifuged at 3000rps for 600 seconds, washed 3 times in ultrapure water, and prepared containing Eu(TTA) 3 Phen Solid Microcapsules {MF[(Eu(TTA) 3 Phen / PSS)(Eu(TTA) 3 Phen / PAH)] 4} and hollow microcapsules [(Eu(TTA) 3 Phen / PSS)(Eu(TTA) 3 Phen / PAH)] 4 ;

[0071] (2) Containing Eu(TTA) 3 The microcapsule film of Phen is complete and the structure is intact; the fluorescence performance of the microcapsule is excellent, and only one layer of Eu(TTA) is deposited in the shell 3 When Phen, the microcapsules emit light visible to the naked eye under the excitation of ultraviolet light; the hollow Eu(TTA) 3 The fluorescent emis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

A process for preparing the RE match microcapsules with high optical effect includes such steps as choosing a main luminous body from Eu(III) beta-biketone matches Eu(acac)3Phen, Eu(TFA)3Phen, Eu(HFA)3Phen, Eu(TTA)3Phen, Eu(DBM)3Phen and Eu(PTA)3Phen, preparing the solid microcapsule whose shell layer contains said RE matches, and preparing the hollow microcapsules whose shell contains RE matches by dissolving the central core.

Description

technical field [0001] The invention relates to a method for preparing microcapsules containing rare earth complexes with high light efficiency, in particular to a method for preparing solid microcapsules and hollow microcapsules containing rare earth complexes with high light efficiency with a stable core-shell structure by using assembly technology at the molecular level new technology. Background technique [0002] The luminescence of rare earth complexes has the characteristics of high luminescence intensity of organic dyes and good monochromaticity of luminescence of rare earth ions. It has a large absorption coefficient for ultraviolet light and can efficiently transfer energy to rare earth ions. The dye molecules have luminescence peaks spanning tens of nanometers or even hundreds of nanometers. Therefore, rare earth complexes have an absolute advantage in luminescent monochromaticity over dyes, and are ideal luminescent substances for observing clear images of red,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J13/02C09K11/00
Inventor 张人杰林振广崔基炜路德明
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com