Resin composition and prepreg, metal foil laminate and interlayer insulation film produced using same

A technology of resin composition and prepreg, which is applied to metal layered products, synthetic resin layered products, layered products, etc., can solve the problems of difficulty in key technical points, mastering, and reducing the ring-opening temperature of benzoxazine resins.

Active Publication Date: 2019-10-01
SHENGYI TECH SUZHOU
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Bismaleimide triazine resin (BT resin) of Mitsubishi Gas can be said to be a model for the application of bismaleimide and cyanate ester. Although it has successfully solved the problem of water absorption in the application of bismaleimide resin, And the patented technology has been disclosed, but its key technical points are still difficult for domestic technicians to grasp
Amines are epoxy resin curing agents. After the amine reacts with the epoxy resin, the epoxy resin ring-opens to produce a large number of hydroxyl groups, and the hydroxyl groups will reduce the ring-opening temperature of the benzoxazine resin and accelerate the opening of the benzoxazine. Ring reaction, so that a large number of hydroxyl groups and amino groups are rapidly generated in the system, which leads to the acceleration of the curing reaction of the entire system and narrows the rheological window

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin composition and prepreg, metal foil laminate and interlayer insulation film produced using same
  • Resin composition and prepreg, metal foil laminate and interlayer insulation film produced using same
  • Resin composition and prepreg, metal foil laminate and interlayer insulation film produced using same

Examples

Experimental program
Comparison scheme
Effect test

Synthetic example 1

[0089] In a 500ml three-neck flask equipped with a stirrer, a reflux condenser and a thermometer, place it in an oil bath, add bisphenol A: 91.2g, p-phenylenediamine: 94.4g, formaldehyde: 48.0g; then add 80ml of ethanol and 20ml of toluene was used as a solvent, and the temperature was slowly raised to 75° C. and kept for 3 hours. During the process, the stirring state was kept continuously, and nitrogen was bubbled into the three-necked flask for protection. Above-mentioned reaction finishes, and after the product is cooled to room temperature, keep stirring and dropwise add methanol solution in the flask, to no longer having precipitate to separate out, stop stirring, leave standstill 24hr under room temperature, filter supernatant liquid, collect precipitate, will The precipitate was placed in a vacuum drying oven at 50°C and dried for 5 hours to obtain a diamine containing a benzoxazine structure, which was designated as N(BOZ)-1.

Synthetic example 2

[0091] In a 500ml three-neck flask equipped with a stirrer, a reflux condenser and a thermometer, place it in an oil bath, add bisphenol F: 79.2g, p-phenylenediamine: 94.4g, formaldehyde: 48.0g; then add 80ml of ethanol and 20ml of toluene was used as a solvent, and the temperature was slowly raised to 60° C. and kept for 5 hours. During the process, the stirring state was continuously maintained, and nitrogen was bubbled into the three-necked flask for protection. Above-mentioned reaction finishes, and after the product is cooled to room temperature, keep stirring and dropwise add methanol solution in the flask, to no longer having precipitate to separate out, stop stirring, leave standstill 24hr under room temperature, filter supernatant liquid, collect precipitate, will The precipitate was placed in a vacuum drying oven at 50°C and dried for 5 hours to obtain a diamine containing a benzoxazine structure, which was designated as N(BOZ)-2.

[0092] Modified resin example one ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a resin composition which is prepared from the following components (by weight based on solids): (a) 40-80 parts of benzoxazine structure-containing diamine modified bismaleimide resin; (b) 10-50 parts of epoxy resin; (c) 10-40 parts of active ester. As for the resin composition, through preferred pre-reaction of bismaleimide and benzoxazine-containing diamine resin at low temperature, benzoxazine almost does not perform ring-opening reaction at low temperature; by consuming a part of reactive groups through pre-reaction, a prepolymer with certain molecular weight is formed, steric hindrance of benzoxazine ring-opening reaction is improved, the reaction rate of a benzoxazine structure, which is in a resin structure, in a system is slowed down, a rheological reaction window of the resin composition is well regulated, and a risk that defects such as substrate white spots or white textures appear caused by too fast reaction of the resin composition in a pressing process is lowered.

Description

technical field [0001] The invention relates to a resin composition and a prepreg, a metal foil laminate and an interlayer insulating film made by using the resin composition, belonging to the technical field of electronic materials. Background technique [0002] The advancement of electronic technology is changing with each passing day. Portability and thinning have become the direction that electronic complete products have been pursuing. However, the thinning and thinning of complete electronic products requires the preparation of electronic products, including printed circuit boards, to be thinner. Therefore, it is necessary to The base material of copper clad laminate has high rigidity and anti-warping ability, so as to meet the structural support and processing requirements of printed circuit boards. [0003] In the prior art, the material prepared from the thermosetting resin composition with epoxy resin and its curing agent as essential components has the advantages ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L79/08C08L63/00C08G73/12C08K3/36B32B27/18B32B15/08B32B15/092B32B27/04
Inventor 崔春梅戴善凯肖升高陈诚黄荣辉季立富谌香秀任科秘
Owner SHENGYI TECH SUZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com