Anti-crack and anti-falling coating and preparation method

An anti-shedding and coating technology, which is applied in the direction of anti-corrosion coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as hidden dangers to people's life safety, inconvenience to people's lives, and unsatisfactory performance, so as to save emulsification production process and increase Anti-shedding performance, good waterproof and anti-corrosion effect

Inactive Publication Date: 2017-09-26
合肥市晨雷思建筑材料科技有限公司
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the improvement of people's living standards and the rapid development of the real estate industry, people's requirements for the decoration industry are getting higher and higher, and the performance requirements for building materials are getting higher and higher, which not only improves the quality, but also prolongs the durability of use. Necessary measures for energy saving and consumption reduction of buildings. Other performances of existing environmental protection materials for walls are not ideal. Shedding, anti-bubble coating material to meet the requirements of modern decoration
In recent years, a variety of inferior decoration materials have appeared on the market, and improper selection also poses hidden dangers to people's life safety
At present, most of the interior decoration coatings on the market are easy to fall off when they are used in a low-temperature and humid environment or for a long time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of anti-cracking, anti-shedding coating and preparation method of the preferred embodiment of the present invention;

[0033] The anti-cracking and anti-shedding coating is prepared from the following raw materials in parts by weight:

[0034] 30 parts of modified polyurethane, 20 parts of modified epoxy resin, 8 parts of glass fiber, 10 parts of aluminum oxide, 12 parts of sodium stearate, 15 parts of paste-like attapulgite clay, 20 parts of putty paste, 8 parts of diatomaceous earth , 5 parts of defoamer, 18 parts of filler, 7 parts of pigment, and appropriate amount of water;

[0035] The modified polyurethane is a graphene modified polyurethane, including the following raw materials in parts by weight: 35 parts of water-based polyurethane, 3 parts of graphene oxide, 12 parts of isophorone diisocyanate, 8 parts of hydrazine hydrate, and solvent N, An appropriate amount of N-dimethylformamide;

[0036] The preparation method includes: weighing 400mL of graphe...

Embodiment 2

[0050] A kind of anti-cracking, anti-shedding coating and preparation method of the preferred embodiment of the present invention;

[0051] The anti-cracking and anti-shedding coating is prepared from the following raw materials in parts by weight:

[0052] 20 parts of modified polyurethane, 15 parts of modified epoxy resin, 5 parts of glass fiber, 8 parts of aluminum oxide, 10 parts of sodium stearate, 10 parts of paste-like attapulgite clay, 15 parts of putty paste, 6 parts of diatomaceous earth , 3 parts of defoamer, 15 parts of filler, 5 parts of pigment, and appropriate amount of water;

[0053] The modified polyurethane is a graphene modified polyurethane, including the following raw materials in parts by weight: 20 parts of water-based polyurethane, 2 parts of graphene oxide, 10 parts of isophorone diisocyanate, 5 parts of hydrazine hydrate, and solvent N, An appropriate amount of N-dimethylformamide;

[0054] The preparation method includes: weighing graphene oxide a...

Embodiment 3

[0068] A kind of anti-cracking, anti-shedding coating and preparation method of the preferred embodiment of the present invention;

[0069] The anti-cracking and anti-shedding coating is prepared from the following raw materials in parts by weight:

[0070] 40 parts of modified polyurethane, 30 parts of modified epoxy resin, 12 parts of glass fiber, 15 parts of aluminum oxide, 15 parts of sodium stearate, 16 parts of paste-like attapulgite clay, 22 parts of putty paste, 10 parts of diatomaceous earth , 8 parts of defoamer, 20 parts of filler, 10 parts of pigment, and appropriate amount of water;

[0071] The modified polyurethane is a graphene modified polyurethane, including the following raw materials in parts by weight: 40 parts of water-based polyurethane, 5 parts of graphene oxide, 15 parts of isophorone diisocyanate, 10 parts of hydrazine hydrate, and solvent N, An appropriate amount of N-dimethylformamide;

[0072] The preparation method includes: weighing 500mL of gr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-crack and anti-falling coating and a preparation method, which belong to the technical field of coatings. The coating is prepared from the following components: modified polyurethane, modified epoxide resin, glass fiber, aluminum oxide, sodium stearate, paste attapulgite clay, putty cream, kieselguhr, a defoaming agent, a filling agent, pigment, and appropriate amount of water. The preparation method comprises the steps of weighing the modified polyurethane and the modified epoxide resin, adding into a reaction kettle, adding appropriate amount of water, and carrying out mixed reaction to obtain a mixture a1; adding the paste attapulgite clay, uniformly stirring, putting in an ultraphonic condition, and obtaining a mixture a2; adding the putty cream, the kieselguhr, the defoaming agent and the filling agent, stirring, shearing, adding a pigment, and uniformly mixing to obtain the coating. The coating provided by the invention not only has a better waterproof and anticorrosion effect, but also has a better anti-crack and anti-falling performance. In addition, the preparation method is simple and practicable, and has a better application value.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an anti-cracking and anti-shedding coating and a preparation method. Background technique [0002] Interior wall waterproof coatings are widely used in residential buildings, school office buildings, etc. At present, the types of interior wall waterproof coatings on the market include: synthetic resin emulsion coatings (commonly known as latex paints), water-soluble interior wall coatings, with polyvinyl alcohol and water glass as the main film-forming substances, including various modified economical coatings; colorful interior wall coatings Coatings include oil-in-water type and water-in-water type; in addition, there are fibrous coatings, imitation porcelain coatings, suede coatings, etc. [0003] With the improvement of people's living standards and the rapid development of the real estate industry, people's requirements for the decoration industry are getting higher and hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D187/00C09D7/12C09D5/08
CPCC09D175/04C08K2003/2227C08K2003/2241C08K2003/265C08K2201/011C08K2201/014C09D5/08C08L87/005C08K13/06C08K9/02C08K7/14C08K3/22C08K5/098C08K3/346C08K3/36C08K3/26C08K3/34C08K7/00C08K3/04
Inventor 史万玲
Owner 合肥市晨雷思建筑材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products