Preparation method of high-weather-resistance fluorescent coloring particles

A technology of colored particles and fluorescence, which is applied in the field of preparation of fluorescent colored particles, can solve problems such as poor weather resistance, achieve high weather resistance, protect bright colors, and improve weather resistance

Active Publication Date: 2017-09-15
ZHEJIANG JCOLOR TECH CO LTD
View PDF10 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] Although the fluorescent colored resin particles prepared by the technology provided by the current literature can meet the market demand in varying degrees in terms of hue, gloss, temperature resistance and solvent resistance, the common problem is poor weather resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037](1) Preparation of highly weather-resistant nano-scale polyacrylic resin particles: a four-necked flask equipped with a stirrer, condenser, thermometer, and nitrogen conduit is placed in a constant temperature water bath, and 220 parts of deionized water are added to the flask. Sodium dialkylbenzene sulfonate; then mix 17 parts of methyl acrylate, 40 parts of methyl methacrylate, and 3 parts of trimethylolpropane triacrylate and add them into the flask, start stirring, and raise the temperature of the mixture to At 75°C, add 0.35 parts of potassium persulfate, and then react under this condition for 6 hours to obtain nano-sized polyacrylic resin particles with high weather resistance.

[0038] (2) Preparation of highly weather-resistant fluorescent colored particles: In a reaction vessel equipped with a high-speed dispersion device, add 206 parts of deionized water, then add 90 parts of paraformaldehyde and 210 parts of benzomelamine in turn, and use soda ash to bring the...

Embodiment 2

[0040] (1) Preparation of highly weather-resistant nano-scale polyacrylic resin particles: a four-necked flask equipped with a stirrer, condenser, thermometer, and nitrogen conduit is placed in a constant temperature water bath, and 220 parts of deionized water are added to the flask. Sodium dialkylbenzene sulfonate; then mix 10 parts of tert-butyl acrylate, 40 parts of methyl methacrylate, 3 parts of methacrylic acid, and 7 parts of ethylene glycol dimethacrylate into the flask, start stirring , the temperature of the mixed solution was raised to 75°C, 0.35 parts of potassium persulfate was added, and then reacted under this condition for 6 hours to obtain nano-sized polyacrylic resin particles with high weather resistance.

[0041] (2) Preparation of highly weather-resistant fluorescent colored particles: In a reaction vessel equipped with a high-speed dispersion device, add 206 parts of deionized water, then add 90 parts of paraformaldehyde and 210 parts of benzomelamine in ...

Embodiment 3

[0043] (1) Preparation of highly weather-resistant nano-scale polyacrylic resin particles: a four-necked flask equipped with a stirrer, condenser, thermometer, and nitrogen conduit is placed in a constant temperature water bath, and 220 parts of deionized water are added to the flask. Sodium dialkylbenzene sulfonate; then mix 17 parts of methyl acrylate, 40 parts of methyl methacrylate, and 3 parts of trimethylolpropane triacrylate and add them into the flask, start stirring, and raise the temperature of the mixture to At 75°C, add 0.35 parts of potassium persulfate, and then react under this condition for 6 hours to obtain nano-sized polyacrylic resin particles with high weather resistance.

[0044] (2) Preparation of highly weather-resistant fluorescent colored particles: In a reaction vessel equipped with a high-speed dispersion device, add 206 parts of deionized water, then add 80 parts of paraformaldehyde, 10 parts of urea, 10 parts of melamine, and benzomelamine 200 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of fluorescent coloring particles, and aims to provide high-weather-resistance fluorescent coloring particles and a preparation method thereof. Compared with domestic and foreign products prepared by the prior art, the fluorescent coloring particles prepared by the method have high weather resistance, and can be taken as fluorescent pigments to be applied to the fields of plastics, plastic cement, coatings, ink and the like. According to the technical scheme, the preparation method of the high-weather-resistance fluorescent coloring particles comprises the following steps in sequence: (1) preparing high-weather-resistance nanoscale polyacrylic resin particles; (2) preparing a fluorescent coloring particle carrier resin prepolymer; (3) coloring and emulsifying the carrier resin; (4) curing fluorescent coloring resin particles.

Description

technical field [0001] The invention relates to a method for preparing fluorescent colored particles, in particular to a method for preparing highly weather-resistant fluorescent colored particles by using nano-scale highly weather-resistant polyacrylic resin modified amino resin particles. Background technique [0002] Fluorescent colored particles are widely used in the fields of plastics, plastics, coatings, inks and the like because of their bright colors. Compared with ordinary colorants, the products prepared by it are more eye-catching and favored by the market. Therefore, there are many literatures at home and abroad about the research on the preparation technology of this type of product; the basic preparation technology is obtained by dissolving organic fluorescent dyes in the carrier resin to form a solid solution, and the carrier resin is mainly polyester, polyamide , amino resins, polyacrylates or their composites. The technical methods mainly include polyconde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/02C08F220/14C08F222/14C08F220/18C08F220/06C08G12/30C08G12/38
CPCC09K11/025C08F220/14C08G12/30C08G12/38C08F222/103C08F220/1804C08F222/102C08F220/06
Inventor 杨少平李胜何建伟
Owner ZHEJIANG JCOLOR TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More