PVC (Polyvinyl Chloride) modifying material for curtains and preparation method thereof
A modified material, PVC resin technology, applied in the field of PVC modified material for curtains and its preparation, can solve the problems of poor fluidity, easy discoloration, poor thermal stability, etc., to improve bending strength, bending modulus of elasticity and thermal deformation Temperature and dimensional stability, compatibility improvement, and stability improvement effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0059] A PVC modified material for curtains, comprising the following raw materials in parts by weight:
[0060] High degree of polymerization PVC resin 80 parts
[0061] 45 parts plasticizer
[0062] 5 parts heavy calcium carbonate
[0063] Light calcium carbonate 10 parts
[0064] Stabilizer 2 parts
[0065] 1 part waterproofing agent
[0066] Modifier 0.5 parts
[0067] Anti-ultraviolet agent 0.6 parts
[0068] Antioxidant 0.3 parts
[0069] Anti-tarnish agent 0.3 parts
[0070] 0.4 parts of external lubricant.
[0071] The high degree of polymerization PVC resin is a SG-0 type PVC resin with a degree of polymerization of 1800; the plasticizer is composed of epoxy soybean oil, synthetic vegetable ester and cyclohexane 1,2-diisononyl dicarboxylate A mixture composed of a weight ratio of 1:0.8:1.
[0072] The heavy calcium carbonate has a particle size of 100nm and has been modified by maleic anhydride grafting; the light calcium carbonate has a particle size of 10n...
Embodiment 2
[0092] A PVC modified material for curtains, comprising the following raw materials in parts by weight:
[0093] High degree of polymerization PVC resin 90 parts
[0094] Plasticizer 50 parts
[0095] 8 parts of heavy calcium carbonate
[0096] Light calcium carbonate 11 parts
[0097] Stabilizer 2.5 parts
[0098] Waterproofing agent 1.5 parts
[0099] Modifier 0.8 parts
[0100] Anti-ultraviolet agent 0.7 parts
[0101] Antioxidant 0.4 parts
[0102] Anti-tarnish agent 0.4 parts
[0103] 0.5 parts of external lubricant.
[0104] The high degree of polymerization PVC resin is a SG-0 type PVC resin with a degree of polymerization of 1850; the plasticizer is made of epoxy soybean oil, synthetic vegetable ester and cyclohexane 1,2-diisononyl dicarboxylate A mixture composed of a weight ratio of 1.2:0.9:1.
[0105] The heavy calcium carbonate has a particle size of 200nm and has been modified by maleic anhydride grafting; the light calcium carbonate has a particle size ...
Embodiment 3
[0125] A PVC modified material for curtains, comprising the following raw materials in parts by weight:
[0126] High degree of polymerization PVC resin 100 parts
[0127] Plasticizer 55 parts
[0128] 10 parts of heavy calcium carbonate
[0129] Light calcium carbonate 12 parts
[0130] Stabilizer 3 parts
[0131] Waterproofing agent 2 parts
[0132] Modifier 1 part
[0133] Anti-ultraviolet agent 0.8 parts
[0134] Antioxidant 0.5 part
[0135] Anti-tarnish agent 0.5 parts
[0136] 0.6 parts of external lubricant.
[0137] The high degree of polymerization PVC resin is a SG-0 type PVC resin with a degree of polymerization of 1900; the plasticizer is composed of epoxy soybean oil, synthetic vegetable ester and cyclohexane 1,2-diisononyl dicarboxylate A mixture composed in a weight ratio of 1.5:1:1.
[0138] The heavy calcium carbonate has a particle size of 300nm and has been modified by maleic anhydride grafting; the light calcium carbonate has a particle size of 5...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com