Mortar

A technology of mortar and parts by weight, applied in the field of concrete, can solve problems such as difficult operation, viscosity of mortar, and reduced strength, and achieve the effects of reducing difficulty, improving adhesion and good impermeability.

Inactive Publication Date: 2017-07-25
广州超力混凝土有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When using mortar to build walls, plaster floors, and plaster walls, the fluidity of the mortar will have a great impact on the above operations. If the fluidity is too large, although it can make the operation easier, it will cause a decrease in strength; and if the fluidity If the resistance is too small, although the strength is improved to a certain extent, it will cause the overall mortar to be relatively viscous and difficult to operate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mortar
  • Mortar
  • Mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Example 1: A mortar, wherein the components and their corresponding parts by weight are shown in Table 1. The mixture includes three materials: fly ash, admixture HT-TSA, and admixture HT-WRB. During construction, the mixing ratio of cement, sand, admixture, and water is cement, sand, admixture, and water. 1:7.37:0.89:0.97, the fineness modulus of sand is 2.7. And the mortar is prepared through the following steps:

[0050] S1, adding the admixture HT-TSA and the admixture HT-WRB into the water and mixing uniformly to form a first mixture;

[0051] S2, fully mixing cement, sand and fly ash to form a second mixture;

[0052] S3: The first mixture obtained in step S1 is slowly added to the second mixture obtained in step S2, and the mixture is fully stirred and mixed to prepare.

[0053] Table 1 Each component in Examples 1-4 and their corresponding parts by weight

[0054]

Embodiment 2

[0055] Example 2: A mortar. The difference from Example 1 is that the components and their corresponding parts by weight are shown in Table 1. The mixing ratio of cement, sand, admixture, and water is 1:5.27:0.43 : 0.76.

Embodiment 3

[0056] Example 3: A mortar, which is different from Example 1 in that the components and their corresponding parts by weight are shown in Table 1. The mixing ratio of cement, sand, admixture, and water is 1:5.08:0.27 : 0.65.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a mortar which contains the following components in parts by weight: 170-260 parts of cement, 1290-1320 parts of sand, 76.65-166.95 parts of mixed material and 170-185 parts of water; the fineness modulus of the sand is 2.5-2.7; the mixing ratio of cement to sand to mixed material to water is 1:(5.08-7.37):(0.27-0.89):(0.65-0.97); the mixed material contains at least one of coal ash, additive HT-TSA and additive HT-WRB. The mortar has the advantages of excellent liquidity and higher pressing resistance after final setting.

Description

Technical field [0001] The invention relates to the technical field of concrete, and more specifically, it relates to a mortar. Background technique [0002] Mortar refers to the bonding material used in building bricks, which is made by adding water to a certain proportion of sand and cementing materials (cement, lime paste, clay, etc.), also called mortar or mortar. [0003] When using mortar to build walls, wipe the ground, and wipe walls, the fluidity of the mortar will have a greater impact on the above operations. If the fluidity is too large, although the operation can be easier, it will reduce the strength; Too small, although the strength is improved to a certain extent, it will cause the overall mortar to be relatively viscous and difficult to handle. Therefore, a mortar with good fluidity and higher compressive strength after final setting has certain commercial value. Summary of the invention [0004] In view of the deficiencies in the prior art, the purpose of the pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B111/27
CPCC04B28/00C04B2111/00637C04B2111/27C04B2201/50C04B18/08C04B14/06C04B20/0076C04B2103/0068
Inventor 叶瑜
Owner 广州超力混凝土有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com