Hydrolysis-resistant white reflective polyester thin film and preparation method thereof

A polyester film, white reflection technology, used in chemical instruments and methods, layered products, synthetic resin layered products, etc., can solve the problems of poor hydrolysis resistance of reflective films, and achieve a wide range of applications and good hydrolysis resistance. , good hydrolysis resistance

Inactive Publication Date: 2017-06-30
NINGBO CHANGYANG TECH
View PDF1 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, most reflective films on the market have relatively poor hydrolysis resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrolysis-resistant white reflective polyester thin film and preparation method thereof
  • Hydrolysis-resistant white reflective polyester thin film and preparation method thereof
  • Hydrolysis-resistant white reflective polyester thin film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] In the hydrolysis-resistant white reflective film provided by the invention, the proportion of layer A is 89.5% of PET slices, 10% of silicon dioxide particles, and 0.5% of epoxy fatty acid glyceride. The proportion of layer B is 71% PET chips, intrinsic viscosity 0.68dL / g, 10% rutile titanium dioxide, 10% polymethylpentene, 5% MAH grafted SEBS (grafting rate ≥ 0.5%), 2% carbonization Diimine, 1% Millad3988 (Milliken Company), 1% PEG (molecular weight: 20,000), and the stated percentages are weight percentages. The thickness of layer A accounts for 12% of the total thickness, and the thickness of layer B accounts for 88% of the total thickness. The thickness of the obtained reflective film is 188 μm, and the relevant properties are shown in Table 1.

Embodiment 2

[0069] In the hydrolysis-resistant white reflective film provided by the invention, the proportion of layer A is 89.5% of PET slices, 10% of silicon dioxide particles, and 0.5% of epoxy fatty acid glyceride. The proportion of layer B is 66% PET chips, intrinsic viscosity 0.68dL / g, 10% rutile titanium dioxide, 15% polymethylpentene, 5% MAH grafted SEBS (grafting rate ≥ 0.5%), 2% carbonization Diimine, 1% Millad3988 (Milliken Company), 1% PEG (molecular weight: 20,000), and the stated percentages are weight percentages. The thickness of layer A accounts for 12% of the total thickness, and the thickness of layer B accounts for 88% of the total thickness. The thickness of the obtained reflective film is 188 μm, and the relevant properties are shown in Table 1.

Embodiment 3

[0071] In the hydrolysis-resistant white reflective film provided by the invention, the ratio of layer A is 89% of PET slices, 10% of silicon dioxide particles, and 1% of epoxy fatty acid glyceride. The proportion of layer B is 65.5% PET chips, intrinsic viscosity 0.68dL / g, 15% rutile titanium dioxide, 10% polymethylpentene, 5% MAH grafted SEBS (grafting rate ≥ 0.5%), 2% carbonization Diimine, 1.5% Millad3988 (Milliken Company), 1% PEG (molecular weight: 20,000), and the stated percentages are weight percentages. The thickness of layer A accounts for 12% of the total thickness, and the thickness of layer B accounts for 88% of the total thickness. The thickness of the obtained reflective film is 188 μm, and the relevant properties are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a hydrolysis-resistant white reflective film, more specifically, the invention relates to a hydrolysis-resistant white reflective polyester film. In order to improve the hydrolysis resistance of the existing white reflective film, the invention provides a hydrolysis-resistant white reflective polyester film and a preparation method thereof. The white reflective polyester film is an ABA three-layer structure; the A layer in the white reflective polyester film includes polyester resin, hydrolysis stabilizer and inorganic particles; the B layer in the white reflective polyester film includes polyester Resins, hydrolysis stabilizers, inorganic particles, incompatible resins, toughening resins, chain extenders, nucleating agents and dispersants. The reflectivity of the reflective film provided by the present invention is basically the same as that of the existing reflective film, and its hydrolysis resistance is very good. display device.

Description

technical field [0001] The invention relates to a hydrolysis-resistant white reflective film, more specifically, the invention relates to a hydrolysis-resistant white reflective polyester film. Background technique [0002] As the screen displays of mobile phones and TVs are developing towards large-screen displays, the demand for liquid crystal displays in the market is huge. These liquid crystal displays (LCD) provide illumination light by setting a surface light source called a backlight on the inside. to display. The backlight is mainly composed of light source, light guide plate, and backlight module. The reflective film plays an important role in gaining brightness in the entire backlight module. [0003] While the demand for display equipment is increasing sharply, people's demand for display performance is also becoming more and more diverse. Light and thin, flexible, high brightness, and wide color gamut are the mainstream. In addition, there are also requirements ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/06B32B27/08B32B27/36C08L67/02C08L23/20C08L51/00C08L71/02C08K3/22C08K5/29C08K3/36C08K5/1515
CPCB32B27/08B32B27/36C08K3/36C08K5/1515C08L67/02C08L2203/16C08L2205/035
Inventor 金亚东刘海波
Owner NINGBO CHANGYANG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com