Safe and environment-friendly type abrasion-resistant self-cleaning latex paint and preparation method thereof

A safe, environmentally friendly, latex paint technology, used in latex paints, biocide-containing paints, coatings, etc., can solve problems such as poor dispersion, powder agglomeration and precipitation, poor stain resistance, etc. Solve the effect of poor stain resistance

Inactive Publication Date: 2017-06-23
BNSA NEW MATERIAL SHANGHAI CO LTD
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the technical solution disclosed in the above patent, the formula components of the latex paint contain a large amount of powder, which has poor dispersibility, and the paint film is prone to powder aggregation and precipitation, and its stain resistance is poor, which needs further improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Safe and environment-friendly type abrasion-resistant self-cleaning latex paint and preparation method thereof
  • Safe and environment-friendly type abrasion-resistant self-cleaning latex paint and preparation method thereof
  • Safe and environment-friendly type abrasion-resistant self-cleaning latex paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] In order to meet the requirements of "JB / T-9755-1995 Synthetic Emulsion Exterior Wall Paint Standard". The performance of the coating is mainly affected by the properties of the binder.

[0032] Firstly, screen and compare domestic binders suitable for latex paint coatings:

[0033]

[0034] Note: The water resistance shown in the above table is the data of the latex with 100um paint film coating paint on the glass plate, dried at 50℃ for 1 hour, and then soaked in water for 96 hours.

[0035] As can be seen from the above table, the performance requirements are compounded. Proceed to the next performance test.

[0036] The 4 emulsions were made into latex paint according to the following formulas:

[0037]

[0038]

[0039] Make a standard sample with the prepared latex paint, and conduct a performance test according to "JB / T-9755-1995 Standard for Synthetic Emulsion Exterior Wall Paint".

[0040] See the table below for the data:

[0041]

[0042] It ...

Embodiment 2

[0052] The safe and environment-friendly wear-resistant self-cleaning latex paint of this embodiment includes the following components and the content in parts by weight: 390 parts of emulsion, 20 parts of film-forming auxiliary agent, 5 parts of silica sol, 2 parts of multifunctional amine auxiliary agent, and 5 parts of hydrophobic agent , 2 parts of wetting agent, 7 parts of dispersant, 2 parts of defoamer, 1 part of cellulose, 2 parts of thickener, 240 parts of inorganic filler, 250 parts of water, 2 parts of preservative, 1 part of antifungal agent and propylene glycol 15 servings.

[0053] Among them, the emulsion is selected from commercially available BLJ838A-2 emulsion, the film-forming aid is 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, and the multifunctional amine auxiliary agent is selected from commercially available AMP-95, the hydrophobic agent is selected from the commercially available LC-808 lotus leaf additive, the wetting agent is selected from the com...

Embodiment 3

[0063] The safe and environment-friendly wear-resistant self-cleaning latex paint of this embodiment includes the following components and contents in parts by weight: 420 parts of emulsion, 30 parts of film-forming aids, 50 parts of silica sol, 4 parts of multifunctional amine additives, and 10 parts of hydrophobic agent , 5 parts of wetting agent, 8 parts of dispersant, 5 parts of defoamer, 3 parts of cellulose, 4 parts of thickener, 315 parts of inorganic filler, 270 parts of water, 4 parts of preservative, 2 parts of antifungal agent and propylene glycol 20 servings.

[0064] Among them, the emulsion is selected from the commercially available RS706T emulsion, the film-forming aid is 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, and the multifunctional amine auxiliary agent is selected from the commercially available AMP -95, the hydrophobic agent is selected from the commercially available LC-808 lotus leaf additive, the wetting agent is selected from the commercially ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a safe and environment-friendly type abrasion-resistant self-cleaning latex paint and a preparation method thereof. The latex paint is prepared from the following components in parts by weight: 390 to 420 parts of emulsion, 20 to 30 parts of film forming additive, 5 to 50 parts of silicon sol, 2 to 4 parts of multifunctional ammine additive, 5 to 10 parts of hydrophobic agent, 2 to 5 parts of wetting agent, 7 to 8 parts of dispersant, 2 to 5 parts of defoaming agent, 1 to 3 parts of cellulose, 2 to 4 parts of thickener, 240 to 260 parts of inorganic filler, 250 to 270 parts of water, 2 to 4 parts of preservative, 1 to 2 parts of anti-mildewing agent and 15 to 20 parts of propylene glycol. Compared with the prior art, the latex paint has the advantages that the compactness of a paint film is good, the hardness is high, the abrasion-resistant property is good, static electricity is not produced, and various dust in air is difficult to adhere; the preparation method is simple, the controllability is good, the green and environment-friendly effect is achieved, the technical defect of poor dirt resistance in a latex paint is effectively overcome, the service life of the latex paint is prolonged, the economy is good, the industrialized expanding production is easy, and the application prospect is good.

Description

technical field [0001] The invention belongs to the technical field of safe and environmentally friendly pigments and dyes, and relates to a safe and environmentally friendly wear-resistant self-cleaning latex paint and a preparation method thereof. Background technique [0002] Latex paint is a common name for latex paint. It was born in the middle and late seventies of the 20th century. It is a large class of thin-coated paint represented by acrylate copolymer emulsion. Latex paint is a water-dispersible paint. It is based on synthetic resin emulsion, and the filler is refined by adding various additives after grinding and dispersing. Latex paint has many advantages that are different from traditional wall paints, such as easy brushing, fast drying, and water-resistant paint film. [0003] However, as the formulations of the existing latex paints on the market become more and more transparent, the crazy price war has caused the performance of latex paints to continue to d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D133/04C09D5/02C09D5/16C09D7/12
CPCC09D5/024C09D5/1687C09D125/14C09D133/04C08L1/284C08K13/02C08K3/36C08K5/103C08K2003/2241C08K2003/265C08K3/34
Inventor 侯进全
Owner BNSA NEW MATERIAL SHANGHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com