A kind of manufacturing method of bamboo fiber non-iron shirt

A production method and bamboo fiber technology, applied in the field of garment processing, can solve the problems of easy shrinkage, easy wrinkling, easy deformation, etc., and achieve the effect of not easy to shrink, not easy to yellow, and maintain strength

Active Publication Date: 2018-03-27
YUNNAN HAOXIANG CLOTHING CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But utilize the clothes that bamboo fiber is made, when wearing and washing, easily wrinkle, deform easily and shrink easily, bring a lot of inconvenience to consumer, all need ironing before washing at every turn

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacturing method of bamboo fiber non-iron shirt
  • A kind of manufacturing method of bamboo fiber non-iron shirt
  • A kind of manufacturing method of bamboo fiber non-iron shirt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The concrete steps of this embodiment are as follows:

[0023] 1. The processing of bamboo fiber fabrics: first put the bamboo fiber fabrics into the bleaching liquid and boil for 30min. Sodium acid sodium 5g / L, penetrating agent 5g / L, scouring agent 3g / L and oxygen bleaching stabilizer 5g / L, rinse twice with cold water after boiling and bleaching, and then wash with hot water at 100°C until the bamboo fiber fabric is boiled and bleached. The liquid is neutral, and then rinsed with cold water and dried for later use. The penetrating agent is JFC, the refining agent is ZJ-CH60 low-temperature refining agent, and the oxygen bleaching agent includes the following components by weight: ethylenediamine 5 parts of sodium tetraacetate, 8 parts of sodium hexametasulfate, 2 parts of hydroxyethylene diphosphate, 3 parts of boric acid, 2 parts of acrylic acid, 2 parts of magnesium sulfate, 2 parts of marmic acid, 0.5 parts of acrylamide, 100 parts of water;

[0024] 2. Garment ma...

Embodiment 2

[0036] The concrete steps of this embodiment are as follows:

[0037] 1. The processing of bamboo fiber fabrics: first put bamboo fiber fabrics into the bleaching liquid and boil for 45min, the bleaching temperature is 95°C, the bath ratio is 1:32, and the bleaching liquid contains 30% hydrogen peroxide 8g / L, silicon Sodium acid 7.5g / L, penetrating agent 6g / L, scouring agent 4g / L and oxygen bleaching stabilizer 6g / L, rinse with cold water for 2-3 times after boiling and bleaching, and then wash with hot water at 95℃ to the bamboo fiber fabric The decoction and bleaching liquid is neutral, and then rinsed with cold water and dried for later use. The penetrating agent is JFC, and the refining agent is ZJ-CH60 low-temperature refining agent. The oxygen bleaching agent includes the following components by weight: B 8 parts of sodium diamine tetraacetate, 3 parts of sodium hexametasulfate, 4 parts of hydroxyethylene diphosphate, 4 parts of boric acid, 2.5 parts of acrylic acid, 2.5...

Embodiment 3

[0050] The concrete steps of this embodiment are as follows:

[0051] 1. The processing of bamboo fiber fabrics: first put bamboo fiber fabrics into the bleaching liquid and boil for 60min, the bleaching temperature is 90°C, the bath ratio is 1:35, and the bleaching liquid contains 30% hydrogen peroxide 10g / L, silicon Sodium acid sodium 10g / L, penetrating agent 8g / L, scouring agent 5g / L and oxygen bleaching stabilizer 8g / L, rinse with cold water for 2 to 3 times after boiling and bleaching, and then wash with hot water at 90°C until the bamboo fiber fabric is clean. The bleaching liquid is neutral, and then rinsed with cold water and dried for later use. The penetrant is JFC, the refining agent is ZJ-CH60 low-temperature refining agent, and the oxygen bleaching agent includes the following components by weight: 10 parts of sodium amine tetraacetate, 3 parts of sodium hexametasulfate, 2 parts of hydroxyethylene diphosphate, 5 parts of boric acid, 3 parts of acrylic acid, 3 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for making a bamboo fiber no-ironing shirt. The method comprises the steps that first bamboo fiber fabric is placed into souring and bleaching liquid and is soured and bleached for 30-60min, wherein souring and bleaching temperature is 90-100 DEG C, a liquor ratio is 1: 30-35, the souring and bleaching liquid contains 30% of hydrogen peroxide with concentration being 6-10g / L, sodium silicate with the concentration being 5-10g / L, penetrating agents with the concentration being 5-8g / L, scouring agents with the concentration being 3-5g / L and oxygen bleaching stabilizer with the concentration being 5-8g / L; the bamboo fiber fabric is cleaned and dried after the scouring and bleaching, then the processed bamboo fiber fabric is tailored and sewed and a ready-made garment is obtained; then a no-ironing treatment is carried out on the manufactured garment, wherein according to the no-ironing treatment, bidirectional stereoscopic type atomization resin absorption, pre-drying, medium or high temperature micro-pressure stereoscopic shaping and finishing, washing, drying, cooling and re-shaping are conducted on the garment. The method for making the bamboo fiber no-ironing shirt can effectively improve the crease-resistant property of bamboo fiber and have a better shrink-proof and no-ironing effect, a manufactured shirt has the advantages of being not deformed easily, and not easy to shrink and the shirt is not easily deformed, not easy to shrink and yellowing, stable in size, soft in handle, uniform in color and lustre, and cool and comfortable to wear.

Description

technical field [0001] The invention belongs to the technical field of clothing processing, and in particular relates to a method for making a bamboo fiber non-ironing shirt. Background technique [0002] Bamboo fiber is cellulose fiber extracted from naturally growing bamboo. It is the fifth largest fiber after cotton, hemp, hemp, wool, and silk. Bamboo fiber has good air permeability, instant water absorption, and strong wear resistance. It has natural antibacterial, antibacterial, anti-mite, deodorant and anti-ultraviolet functions. One is a pure and environmentally friendly green fiber, which has been widely used in the textile field. At the same time, the use of bamboo fiber to produce bamboo fiber yarn is an extension of green fiber, which is also a green product. The knitted and woven fabrics and clothing produced by bamboo fiber yarn have a unique style that is obviously different from cotton and wood-type cellulose fibers. It has high strength, wear resistance, moi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A41B1/00A41B17/00D06L4/13D06L4/12D06L4/15D06L1/16D06M15/00D06M101/06
CPCA41B1/00A41B17/00D06B1/02D06C5/00D06L1/16D06M15/00D06M2101/06
Inventor 赵世近卢成军
Owner YUNNAN HAOXIANG CLOTHING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com