Dispersed carbon-coated metal particles, articles and uses

A carbon coating and dispersion technology, used in coatings, applications, household appliances, etc., to achieve the effect of electroless plating activity improvement

Active Publication Date: 2020-10-30
EASTMAN KODAK CO
View PDF37 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, known dispersants have not been readily adapted to specific particles to minimize settling and interparticle interactions that can undesirably increase the viscosity of a given composition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dispersed carbon-coated metal particles, articles and uses
  • Dispersed carbon-coated metal particles, articles and uses
  • Dispersed carbon-coated metal particles, articles and uses

Examples

Experimental program
Comparison scheme
Effect test

example

[0355] Example of Article Invention: Use of Non-aqueous Photocurable Composition to Provide Patterned Article

[0356] The present examples demonstrate the use of the non-aqueous photocurable compositions of the present invention for the manufacture of precursor articles having photocurable patterns on suitable substrates.

[0357] To print the non-aqueous photocurable compositions of the present invention (as described below), a flexographic printing unit has been used with a resolution of 12,800 dpi using Kodak Square Spot (Kodak Square Spot) laser technology. A sample of a commercially available Kodak Flexcel NX flexographic printing plate precursor (Eastman Kodak Company) was imaged with a predetermined pattern written at a rate. The flexographic printing plate precursors were UV exposed and treated (developed) using known conditions recommended by the manufacturer for these flexographic printing parts. The resulting flexographic printing plate was 1.14 mm thick (includin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The present invention relates to a non-aqueous composition comprising dispersed carbon-coated metal particles in an organic diluent in an amount of at least 10% by weight. The dispersed carbon-coated metal particles have a median diameter equal to or less than 0.6 μm, and have a weight average molecular weight (M w ) and the particle dispersant comprising nitrogen-containing units is dispersed. The median diameter of the dispersed particles is measured using dynamic light scattering. Furthermore, when the non-aqueous composition contains up to and including 25% by weight of the dispersed carbon-coated metal particles, it exhibits no visual settling when subjected to a settling test at 20°C for at least 24 hours. Such non-aqueous compositions may include a photocurable component and are suitable for use in the preparation of photocurable and photocured conductive patterns and layers in a variety of articles, including touch screen devices having touch screen displays.

Description

technical field [0001] The present invention relates to non-aqueous compositions containing dispersed carbon-coated metal particles and a uniquely selected particle dispersant. The present invention also relates to non-aqueous photocurable compositions containing these dispersed carbon-coated metal particles and a particle dispersant. These non-aqueous photocurable compositions can be used to provide seed metal catalysts for electroless plating processes designed to provide patterns of conductive materials. Background technique [0002] Rapid progress is being made in various electronic devices, especially display devices for various communication, financial and archival purposes. Conductive films are necessary for applications such as touch screen panels, electrochromic devices, light emitting diodes, field effect transistors, and liquid crystal displays, and efforts are being made in the industry to improve the properties of these conductive films. [0003] In particular...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/03C09D11/38C09D11/037C09D179/02C09D133/14C09D179/04C09D179/08C09D4/02C08F222/10H05K1/00
CPCC08F222/10C09D4/00C09D11/03C09D11/037C09D11/38C09D133/14C09D179/02C09D179/04C09D179/08H05K1/00C09D7/20
Inventor 凯伦·M·柯西达盖瑞·L·史雷特玛莉·克里斯廷·布理克克里斯廷·乔安·蓝卓-考特兰詹姆斯·阿尔贝特·雷切克
Owner EASTMAN KODAK CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com