Aluminizing method of GH4049 ball

A technology of aluminizing and spheres, which is applied in the field of GH4049 sphere aluminizing, can solve the problems that the hardness is difficult to meet the design requirements, increase the difficulty of heat treatment, and difficult to guarantee the hardness value, etc., achieve good production verification results, reduce the risk of hardness, and shorten production the effect of time

Active Publication Date: 2017-05-31
CHINA HANGFA GUIZHOU LIYANG AVIATION POWER CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] GH4049 is a complex alloyed nickel-based hard-to-deform superalloy. After heat treatment using the heat treatment system corresponding to the hardness value range HB302-363 specified in the standard, it is difficult to guarantee the hardness value in this range, and often rework is still unqualified. Scrapped Parts Situation
The hardness value required by the design is HB285~352, which is more stringent than that specified in the standard, which increases the difficulty of heat treatment
In addition, the sphere needs to be aluminized after heat treatment. However, the hardness of the solid solution + aging treatment before aluminizing has always been difficult to meet the design requirements.
At present, there is no similar process in the same industry that can make it meet the design requirements, and a new method must be invented to meet the hardness requirements while satisfying the depth of the aluminized layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminizing method of GH4049 ball
  • Aluminizing method of GH4049 ball
  • Aluminizing method of GH4049 ball

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] Below in conjunction with accompanying drawing, the present invention is described in further detail:

[0021] Such as figure 1 and 2 As shown, the traditional heat treatment scheme is to first figure 1 The rough blank shown (the cross-sectional diameter of the round bar blank is Ф14mm, the length is 500mm, the chemical composition of the blank is as follows image 3 Shown) for solid solution + aging treatment, to ensure the hardness HB285 ~ 352, after the parts are processed to figure 2 When the shape is shown (the diameter of the spherical surface D is Ф10mm, and the distance between a pair of parallel planes is 6.4mm), then aluminized. The disadvantage is that the hardness of the parts and the depth of the aluminized layer will be affected during the subsequent aluminizing, and the required hardness value and depth of the aluminized layer will not be reached.

[0022] The heat treatment method of the present invention has broken the train of thought of tradition...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aluminizing method of a GH4049 ball. The aluminizing method comprises the steps of firstly, carrying out solid solution treatment on a GH4049 blank; then, processing the blank subjected to solid solution treatment into a semi-finished product with a spherical surface D; and finally, carrying out aging treatment on the entire semi-finished product while carrying out aluminizing on the spherical surface D of the semi-finished product at the aging temperature. According to the aluminizing method, the hardness is guaranteed to reach HB285 to HB352 while the depth of an aluminized layer is guaranteed to be 30 [mu]m to 50 [mu]m.

Description

technical field [0001] The invention belongs to the technical field of aluminizing, and in particular relates to a GH4049 sphere aluminizing method. Background technique [0002] Such as figure 1 and 2 As shown, in the development process of an aero-engine, the design drawing requires the hardness of the sphere (material GH4049) to be HB285-352, and the spherical surface D is aluminized to a depth of 30μm-50μm. [0003] GH4049 is a complex alloyed nickel-based hard-to-deform superalloy. After heat treatment using the heat treatment system corresponding to the hardness value range HB302-363 specified in the standard, it is difficult to guarantee the hardness value in this range, and often rework is still unqualified. The condition of scrapped parts. The hardness value required by the design is HB285-352, which is more stringent than that stipulated in the standard, which increases the difficulty of heat treatment. Moreover, aluminizing is required after the heat treatment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22F1/10C23C10/50
CPCC22F1/10C23C10/50
Inventor 韦芙丹林发仙翟辉赖道辉曹卫舒琴
Owner CHINA HANGFA GUIZHOU LIYANG AVIATION POWER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com