Formula of anticorrosive paint

A technology for anti-corrosion coatings and formulations, applied in anti-corrosion coatings, coatings and other directions, can solve the problems of metal rust and corrosion, can not satisfy users, fall off, etc., and achieve the effects of low cost, improved safety, and simple structure

Inactive Publication Date: 2017-05-31
镇江程灿科技服务有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a formula for anti-corrosion coatings, which solves the phenomenon that most of the existing anti-corrosion coatings are prone to fall off after being eroded by wind and rain and impacted after long-term use, so that the metal to be protected will rust and corrode The phenomenon that cannot meet the needs of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: a kind of formula of anticorrosion coating, its composition is as follows by weight fraction:

[0028] 100 parts of water;

[0029] 5 parts of ethylene glycol;

[0030] 45 parts of titanium dioxide;

[0031] 15 parts of kaolin;

[0032] 9 parts of butyl ester;

[0033] 3 parts ethyl ester;

[0034] 1 part antifoaming agent;

[0035] 1 part of defoamer;

[0036] 1 part of dispersant;

[0037] Regulator 1 part;

[0038] Wetting agent 1 part.

[0039] The formula of above-mentioned a kind of anticorrosion coating, wherein, the weight fraction ratio of described butyl ester and ethyl ester is 3:1.

[0040] The formulation of the above anti-corrosion coating, wherein the particle size of the kaolin is 0.2mm.

[0041] The formulation of the above anti-corrosion coating, wherein the particle size of the titanium dioxide is 300nm.

[0042] The formula of the above-mentioned anti-corrosion coating, wherein the model of the anti-foaming agent is EFKA-526....

Embodiment 2

[0047] Embodiment 2: a kind of formula of anticorrosion coating, its composition is as follows by weight fraction:

[0048] 200 parts of water;

[0049] 10 parts of ethylene glycol;

[0050] 90 parts of titanium dioxide;

[0051] 35 parts of kaolin;

[0052] 18 parts of butyl ester;

[0053] 6 parts of ethyl ester;

[0054] 2 parts antifoaming agent;

[0055] 1 part of defoamer;

[0056] 2 parts of dispersant;

[0057] Regulator 2 parts;

[0058] Wetting agent 2 parts.

[0059] The formula of above-mentioned a kind of anticorrosion coating, wherein, the weight fraction ratio of described butyl ester and ethyl ester is 3:1.

[0060] The formulation of the above anti-corrosion coating, wherein the particle size of the kaolin is 0.3mm.

[0061] The formulation of the above anti-corrosion coating, wherein the particle size of the titanium dioxide is 400nm.

[0062] The formula of the above-mentioned anti-corrosion coating, wherein the model of the anti-foaming agent is ...

Embodiment 3

[0067] Embodiment 3: a kind of formula of anticorrosion coating, its composition is as follows by weight fraction:

[0068] 300 parts of water;

[0069] 15 parts of ethylene glycol;

[0070] 135 parts of titanium dioxide;

[0071] 45 parts of kaolin;

[0072] 27 parts of butyl ester;

[0073] 9 parts of ethyl ester;

[0074] 2 parts antifoaming agent;

[0075] 2 parts of defoamer;

[0076] 3 parts of dispersant;

[0077] Regulator 3 parts;

[0078] 3 parts of wetting agent.

[0079] The formula of above-mentioned a kind of anticorrosion coating, wherein, the weight fraction ratio of described butyl ester and ethyl ester is 3:1.

[0080] The formulation of the above anti-corrosion coating, wherein the particle size of the kaolin is 0.5mm.

[0081] The formulation of the above anti-corrosion coating, wherein the particle size of the titanium dioxide is 500nm.

[0082] The formula of the above-mentioned anti-corrosion coating, wherein the model of the anti-foaming agen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a formula of an anticorrosive paint. The anticorrosive paint is prepared by adopting water, ethylene glycol, titanium dioxide, kaolin, butyl ester and ethyl ester as main materials and adding a foam inhibitor, an antifoaming agent, a dispersing agent, a modifier and a wetting agent. The anticorrosive paint is simple in structure, convenient to prepare, relatively low in cost, free of harm, and good in anticorrosive effect; the phenomenon that the paint falls off does not easily appear, the overall security is effectively improved and the requirements of a manufacturer can be met.

Description

technical field [0001] The invention relates to the technical field of anti-corrosion coatings, in particular to a formula of anti-corrosion coatings. Background technique [0002] Anti-corrosion coatings, generally divided into conventional anti-corrosion coatings and heavy-duty anti-corrosion coatings, are an indispensable coating in paint coatings. Conventional anti-corrosion coatings play an anti-corrosion effect on metals under normal conditions and protect the service life of non-ferrous metals; A type of anti-corrosion coating that achieves a longer protection period than conventional anti-corrosion coatings. However, most of the existing anti-corrosion coatings are easy to fall off after being eroded by wind and rain and impacted after being used for a long time, so that the metal to be protected will rust and corrode, which cannot meet the needs of users. Contents of the invention [0003] The purpose of the present invention is to provide a formula for anti-cor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D5/08C09D7/12
CPCC09D1/00C09D5/08C09D7/63C09D7/65
Inventor 高扬陈章琴
Owner 镇江程灿科技服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap