Water-based woodware lacquer coating capable of scavenging formaldehyde

A technology of water-based wood paint and formaldehyde, applied in the field of coatings, can solve the problems of water-based wood paint such as insufficient water resistance, strength, antibacterial property, wear resistance, etc., and achieve good formaldehyde purification performance, long service life and wear resistance good performance performance

Pending Publication Date: 2017-05-17
福建华夏蓝新材料科技有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with solvent-based wood coatings, water-based wood coatings still have insufficient water resistance, strength, antibacterial properties, and abrasion resistance, which cannot meet the requirements of society.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based woodware lacquer coating capable of scavenging formaldehyde

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A formaldehyde-removing water-based wood paint (inner chamber), which is composed of the following raw materials by weight: 10 parts of distilled water A, 34 parts of acrylic emulsion A (Wanhua Lacper4502), substrate wetting agent (TEGO® Wet 270) 0.3 parts, 0.3 parts of dispersing wetting agent (TEGO® Dispers651), 0.1 parts of defoamer (TEGO® Airex902W), 8.2 parts of acrylic emulsion B (Wanhua Lacper4318), 3 parts of distilled water B, PH regulator (DOW AMP -95) 0.5 parts, medium and high shear thickener (Wanhua VesmodyU505) 0.3 parts, titanium white paste (76wt% content R-996) 20.5 parts, 800 mesh heavy calcium 10 parts, 1250 mesh talc powder 3.5 parts, distilled water C2. 5 parts, 2.5 parts of dipropylene glycol butyl ether (DOW's DPnB), 2 parts of dipropylene glycol methyl ether (DOW's DPM), 1.5 parts of formaldehyde removal additive (commonly known as FA-7), 0.5 parts of propylene glycol (PG), fungicide (Kathon LXE by DOW) 0.3 parts.

[0019] The preparation method...

Embodiment 2

[0027] A formaldehyde-removing water-based wood lacquer (inner chamber), consisting of the following raw materials by weight: 6 parts of distilled water A, 30 parts of acrylic emulsion (Wanhua Lacper4502), 0.5 parts of substrate wetting agent (TEGO® Wet 270) 0.5 parts of dispersing wetting agent (TEGO® Dispers651), 0.5 parts of defoamer (TEGO® Airex902W), 15 parts of acrylic emulsion (Wanhua Lacper4318), 2 parts of distilled water B, PH regulator (DOW AMP-95 ) 0.5 parts, medium and high shear thickener (Wanhua VesmodyU505) 0.5 parts, titanium white paste (76wt% content R-996) 24.5 parts, 800 mesh heavy calcium 9.5 parts, 1250 mesh talcum powder 2.5 parts, distilled water C 1.5 parts, Dipropylene glycol butyl ether (DOW's DPnB) 1.5 parts, dipropylene glycol methyl ether (DOW's DPM) 2 parts, formaldehyde removal additive (commonly known as FA-7) 2 parts, propylene glycol (PG) 0.8 parts, fungicide (DOW's Kathon LXE) 0.2 parts.

[0028] The preparation method is:

[0029] (1) Pu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of coating, and particularly relates to water-based woodware lacquer coating capable of scavenging formaldehyde. The water-based woodware lacquer coating capable of scavenging formaldehyde is prepared from the following raw materials in parts by weight: 5-30 parts of distilled water A, 40-60 parts of polyacrylic emulsion A, 0.1-0.5 part of base material wetting agent, 0.5-2 parts of dispersing wetting agent, 0.1-1 part of deforming agent, 5-10 parts of polyacrylic emulsion B, 1-3 parts of distilled water B, 0.1-1 part of pH conditioning agent, 0.1-1 part of thickening agent, 10-30 parts of titanium dioxide slurry, 5-15 parts of heavy calcium powder, 1-10 parts of talcum powder, 1-5 parts of distilled water C, 1-5 parts of dipropylene glycol mono butyl ether, 1-5 parts of dipropylene glycol monomethyl ether, 0.5-3 parts of formaldehyde scavenging additive, 0.5-3 parts of propylene glycol and 0.1-1 part of bactericide. The water-based woodware lacquer coating capable of scavenging formaldehyde has high strength, good formaldehyde scavenging performance, good wear resistance and scratching resistance, an excellent antibacterial property, good water resistance and aging resistance, stain resistance and long service life.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to a water-based wood lacquer capable of removing formaldehyde. Background technique [0002] Wood coatings refer to the coatings used on wood products including solid wood and wood-based panels, including furniture, doors and windows, wall panels, floors, daily necessities, wooden musical instruments, sporting goods, stationery, children's toys, etc. Generally speaking, wood coatings are mainly furniture coatings. Wood coatings give wood and wood-based materials desired aesthetic characteristics such as color and luster, while also making wood resistant to damage caused by moisture, bacterial growth, biodegradation, chemical damage, etc. [0003] Water-based wood coatings have become a research hotspot due to their non-toxic, environmentally friendly, less volatile matter, and high safety. Compared with solvent-based wood coatings, water-based wood coatings still have deficiencies in wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/16C09D5/14C09D7/12
CPCC09D133/00C08L2205/025C09D5/14C09D5/16C09D7/61C09D7/63C08L33/00C08K13/02C08K2003/2241C08K2003/265C08K3/34C08K5/053
Inventor 饶长贵陈国栋
Owner 福建华夏蓝新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com