Smooth treatment agent for automobile processing materials
A technology for processing materials and smoothing treatment. It is applied in the direction of detergent compounding agent, detergent composition, polishing composition containing abrasive, etc. It can solve the problems of leaving traces and affecting the appearance, and achieves convenient use and high scrubbing efficiency. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] The automotive processing material smoothing agent in this embodiment is composed of the following components by mass: 5 parts of talc, 10 parts of sodium benzoate, 5 parts of softener, 10 parts of dodecyl polyoxyethylene, and 5 parts of sulfuric acid , 10 parts of nano copper borate, 5 parts of boric acid, 3 parts of anhydrous sodium metasilicate, 40 parts of deionized water.
[0015] Above-mentioned automobile processing material smooth treatment agent, its preparation steps are as follows:
[0016] (1) adding the above-mentioned talc, sodium benzoate, softener and dodecyl polyoxyethylene in deionized water to obtain A component solution;
[0017] (2) adding sulfuric acid, nano-copper borate, boric acid and anhydrous sodium metasilicate in the above-mentioned mass fractions into deionized water to obtain B component solution;
[0018] (3) Mix the A component solution and the B component solution evenly to obtain this product.
Embodiment 2
[0020] The automotive processing material smoothing agent in this embodiment is composed of the following components by mass: 18 parts of talc, 28 parts of sodium benzoate, 25 parts of softener, 20 parts of dodecyl polyoxyethylene, and 15 parts of sulfuric acid , 25 parts of nano copper borate, 10 parts of boric acid, 15 parts of anhydrous sodium metasilicate, 80 parts of deionized water.
[0021] Above-mentioned automobile processing material smooth treatment agent, its preparation steps are as follows:
[0022] (1) adding the above-mentioned talc, sodium benzoate, softener and dodecyl polyoxyethylene in deionized water to obtain A component solution;
[0023] (2) adding sulfuric acid, nano-copper borate, boric acid and anhydrous sodium metasilicate in the above-mentioned mass fractions into deionized water to obtain B component solution;
[0024] (3) Mix the A component solution and the B component solution evenly to obtain this product.
Embodiment 3
[0026] The automotive processing material smoothing agent in this embodiment is composed of the following components by mass: 10 parts of talcum powder, 14 parts of sodium benzoate, 15 parts of softener, 15 parts of dodecyl polyoxyethylene, and 10 parts of sulfuric acid , 12 parts of nano copper borate, 8 parts of boric acid, 9 parts of anhydrous sodium metasilicate, 60 parts of deionized water.
[0027] Above-mentioned automobile processing material smooth treatment agent, its preparation steps are as follows:
[0028] (1) adding the above-mentioned talc, sodium benzoate, softener and dodecyl polyoxyethylene in deionized water to obtain A component solution;
[0029] (2) adding sulfuric acid, nano-copper borate, boric acid and anhydrous sodium metasilicate in the above-mentioned mass fractions into deionized water to obtain B component solution;
[0030] (3) Mix the A component solution and the B component solution evenly to obtain this product.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com