Aqueous acrylic polyurethane aluminum powder paint and preparation method thereof

A technology of acrylic polyurethane and silver powder paint, applied in the field of coatings, can solve the problems that two-component water-based acrylic polyurethane silver powder paint has not been widely used, the gloss and vividness of the paint film cannot meet the requirements, and the orientation of water-based silver powder is poor. To achieve the effect of improving the flash effect, high gloss and vividness, and low VOC content

Inactive Publication Date: 2017-04-26
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Due to the slow volatilization of water in water-based acrylic polyurethane silver powder paint, a series of problems such as sag, silver powder sedimentation, and poor alignment of water-based silver powder appear in the water-based silver powder paint. Water-based acrylic polyurethane silver powder paint is not widely used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous acrylic polyurethane aluminum powder paint and preparation method thereof
  • Aqueous acrylic polyurethane aluminum powder paint and preparation method thereof
  • Aqueous acrylic polyurethane aluminum powder paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of waterborne acrylic polyurethane silver powder paint of the present invention, described waterborne acrylic polyurethane silver powder paint is made up of A component and B component,

[0031] The A component consists of the following components by weight percentage:

[0032]

[0033]

[0034] The B component is an isocyanate curing agent;

[0035] The weight ratio of the A component and the B component is 7:1.

[0036] The water-based hydroxyl acrylic emulsion is VSM 6299w of allnex resins.

[0037] The curing agent is Covestro's N3900.

[0038] The water-dispersible cellulose ester solution is an aqueous solution of water-dispersible cellulose ester with a mass fraction of 20%, and the water-dispersible cellulose ester is Eastman Solus 3050.

[0039] The ethylene-vinyl acetate copolymer wax emulsion is Bik AQUATIX 8421 from Germany.

[0040] The preparation method of waterborne acrylic polyurethane silver powder paint of the present invention, compr...

Embodiment 2

[0048] The difference between embodiment 2 and embodiment 1:

[0049] A kind of waterborne acrylic polyurethane silver powder paint of the present invention, described waterborne acrylic polyurethane silver powder paint is made up of A component and B component,

[0050] The A component consists of the following components by weight percentage:

[0051]

[0052] The B component is an isocyanate curing agent;

[0053] The weight ratio of the A component and the B component is 9:1.

[0054] The aqueous hydroxyacrylic emulsion is Setaqua 6516 of Nupace.

[0055] The preparation method of waterborne acrylic polyurethane silver powder paint of the present invention, comprises the steps:

[0056] Preparation method of component A:

[0057] (1) Add propylene glycol butyl ether into the paint mixing tank, add wetting and dispersing agent under stirring at 260r / min, then slowly add water-based silver powder, stir for 20min and then let stand for 2h to prepare water-based aluminu...

Embodiment 3

[0063] The difference between embodiment 3 and embodiment 1:

[0064] A kind of waterborne acrylic polyurethane silver powder paint of the present invention, described waterborne acrylic polyurethane silver powder paint is made up of A component and B component,

[0065] The A component consists of the following components by weight percentage:

[0066]

[0067]

[0068] The B component is an isocyanate curing agent;

[0069] The weight ratio of the A component and the B component is 8:1.

[0070] The water-based hydroxyl acrylic emulsion is a combination of two kinds of VSM 6299w of Allnex resin and Setaqua 6516 of New Pace.

[0071] The preparation method of waterborne acrylic polyurethane silver powder paint of the present invention, comprises the steps:

[0072] Preparation method of component A:

[0073] (1) Add propylene glycol butyl ether into the paint mixing tank, add wetting and dispersing agent under stirring at 300r / min, then slowly add water-based silver...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aqueous acrylic polyurethane aluminum powder paint, which is composed of a component A and a component B, wherein the component A is composed of, by weight, 35-45% of aqueous hydroxyl acrylic emulsion, 0.3-1% of a defoamer, 20-30% of deionized water, 0.3-1% of a wetting dispersant, 5-15% of a propylene glycol butyl ether, 6-8% of aqueous aluminum powder, 5-10% of an ethylene-vinyl acetate copolymer wax emulsion, 5-15% of water-dispersible cellulose ester solution, and 0.3-1% of a base material wetting agent; and the component B is an isocyanate curing agent. The weight ratio of the component A to the component B is 7-9:1. A paint film formed by the aqueous acrylic polyurethane aluminum powder paint is quick to dry, is glossy and has high brightness. Orientation of the aluminum powder is excellent.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to a water-based acrylic polyurethane silver powder paint and a preparation method thereof. Background technique [0002] With the continuous development of society, people have higher and higher requirements for the performance and environmental protection of coatings. Silver powder paint is widely favored by people for its rich colors, excellent color flop effect, and elegant decorative effect. Especially, new energy buses that advocate the concept of environmental protection often use silver powder and metal effect coatings. Most of the silver powder paints used in the painting of energy buses are solvent-based paints. Generally, single-component silver powder paints are used and then sprayed with varnishes. The organic solvent content is high, which seriously pollutes the environment and endangers the health of personnel. [0003] Using two-component waterborne acrylic polyurethane silv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/12C08G18/62
CPCC09D175/04C08G18/6216C08L2205/03C09D7/61C09D7/65
Inventor 王瑞宏郭晓峰周泽钱郭晓猛岳少哲
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com