A plastering mortar and antibacterial agent technology, applied in the field of building materials, can solve the problems of endangering human health, short service life, high indoor humidity, etc., and achieve the effect of fast setting time, smooth surface and strong water absorption
Inactive Publication Date: 2017-04-26
新昌县永佳耐火材料厂
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, latex paint, wallpaper, and wall covering are generally used for interior decoration in our country. These materials have some shortcomings, such as the smooth and dense surface of latex paint, large echo, and poor water absorption, resulting in high indoor humidity; wallpaper and wall covering are used in production and pasting. Adhesives produce formaldehyde and other gases, which are harmful to human health and have a short service life. There are potential safety hazards and cannot meet modern people's requirements for environmental protection and health of building materials.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] An antibacterial plastering mortar in an embodiment of the present invention includes the following raw materials in parts by weight:
[0017] 20 parts of Portland cement, 1 part of nano titanium dioxide, 50 parts of quartz sand, 5 parts of montmorillonite powder, 1 part of polyanionic cellulose, 0.01 part of silicone modified polyester, 0.1 part of drier, 0.02 part of synergist part, 0.1 part of antibacterial agent.
[0018] The Portland cement is 42.5R.
[0019] The quartz sand is 200 mesh.
[0020] The montmorillonite powder is a 50 μm particle.
[0021] The drier includes a compound of cobalt naphthenate and manganese naphthenate, and its component ratio is 1:1.
[0022] The synergist includes a mixture of diethylaminosulfur trifluoride and bis(2-methoxyethyl)aminosulfur trifluoride, and the component ratio is 1:1.
[0023] The antibacterial agent comprises a compound of copper oxide, ammonium dihydrogen phosphate and lithium carbonate, and the ratio of its comp...
Embodiment 2
[0025] An antibacterial plastering mortar according to an embodiment of the present invention comprises the following raw materials in parts by weight:
[0026] 25 parts of Portland cement, 5 parts of nano titanium dioxide, 65 parts of quartz sand, 8 parts of montmorillonite powder, 2 parts of polyanion cellulose, 0.03 parts of silicone modified polyester, 0.2 parts of drier, 0.05 parts of synergist part, 0.15 part of antibacterial agent.
[0027] The Portland cement is 42.5R.
[0028] The quartz sand is 300 mesh.
[0029] The montmorillonite powder is a 100 μm particle.
[0030] The drier includes a compound of manganese naphthenate and lead naphthenate, and its component ratio is 1:1.
[0031] The synergist includes butyl triphenylphosphine fluoride and tetrabutyl phosphine fluoride, and the composition ratio thereof is 1:1.
[0032] The antibacterial agent comprises a compound of zinc oxide, copper oxide and ammonium dihydrogen phosphate, and its component ratio is 1:1:...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention belongs to the technical field of building materials and provides antibacterial finishing mortar. The antibacterial finishing mortar is prepared from the following raw materials in parts by weight: 20-25 parts of silicate cement, 1-5 parts of nano-titania, 50-65 parts of quartzite sand, 5-8 parts of montmorillonite powder, 1-2 parts of polyanionic cellulose, 0.01-0.03 part of organosilicone modified polyester, 0.1-0.2 part of drier, 0.02-0.05 part of synergist and 0.1-0.15 part of antibacterial agent. The antibacterial finishing mortar has the beneficial effects that the antibacterial finishing mortar is a special mortar material, which is developed for architectural decoration, and is smooth in surface, short in setting time, high in setting strength and high in water absorbency, so that the propagation of bacteria caused by high indoor humidity is avoided; and meanwhile, through adopting materials with antibacterial functions such as polyester modified siloxane, polyacrylate, polysiloxane and hydrophobic modified silicon dioxide, human health can be protected, and the requirements of modern people on environment-friendliness, safety and the like of the building materials are met.
Description
technical field [0001] The invention belongs to the technical field of building materials, in particular to an antibacterial plastering mortar. Background technique [0002] Plastering mortar refers to the mortar applied on the surface of buildings or building components, which can protect the base layer and increase the appearance. At present, latex paint, wallpaper, and wall covering are generally used for interior decoration in our country. These materials have some shortcomings, such as the smooth and dense surface of latex paint, large echo, and poor water absorption, resulting in high indoor humidity; wallpaper and wall covering are used in production and pasting. Adhesives produce formaldehyde and other gases, which are harmful to human health and have a short service life. There are potential safety hazards and cannot meet modern people's requirements for environmental protection and health of building materials. Contents of the invention [0003] Aiming at the de...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more