2a12 aluminum alloy casting process

A casting process, 2A12 technology, applied in the field of 2A12 aluminum alloy casting process, can solve the problems of unacceptable by users, high production cost, waste of high-load parts and component raw materials, etc., to achieve saving raw materials, high production efficiency, and good quality of workpieces Effect

Active Publication Date: 2019-07-12
喀左金牛机电设备科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using this method to process various high-load parts and components wastes a lot of raw materials, and the production cost is too high, which is difficult for users to accept

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] 1. Determine the group distribution ratio

[0043] The raw materials are formulated according to the following weight percentages, wherein the silicon content is 0.45%, the copper content is 3.8%, the manganese content is 09%, the titanium content is 0.12%, the magnesium content is 1.2%, the zinc content is 0.26%, the nickel content is 0.08%, and the iron content is 0.43%. , the balance is A00 pure aluminum;

[0044] 2. Preparation and smelting of master alloy

[0045] 1) copper aluminum alloy

[0046] Put copper and A00 pure aluminum into the crucible according to the weight ratio of 1:1, smelt, and make copper-aluminum alloy after standing;

[0047] 2) Al-Mn alloy

[0048] Add metal manganese and A00 pure aluminum into the crucible according to the weight ratio of 1:9, carry out melting, and make aluminum-manganese alloy after standing;

[0049] 3) Aluminum titanium alloy

[0050] Sponge titanium and A00 pure aluminum are added into the crucible according to the ...

Embodiment 2

[0072] 1. Determine the group distribution ratio

[0073]The raw materials are formulated according to the following weight percentages, wherein the silicon content is 0.48%, the copper content is 4.9%, the manganese content is 0.3%, the titanium content is 0.15%, the magnesium content is 1.8%, the zinc content is 0.28%, the nickel content is 0.09%, and the iron content is 0.44%. , the balance is A00 pure aluminum;

[0074] 2. Preparation and smelting of master alloy

[0075] 1) copper aluminum alloy

[0076] Put copper and A00 pure aluminum into the crucible according to the weight ratio of 1:1, smelt, and make copper-aluminum alloy after standing;

[0077] 2) Al-Mn alloy

[0078] Add metal manganese and A00 pure aluminum into the crucible according to the weight ratio of 1:9, carry out melting, and make aluminum-manganese alloy after standing;

[0079] 3) Aluminum titanium alloy

[0080] Sponge titanium and A00 pure aluminum are added into the crucible according to the ...

Embodiment 3

[0102] 1. Determine the group distribution ratio

[0103] The raw materials are formulated according to the following weight percentages, wherein the silicon content is 0.47%, the copper content is 4.2%, the manganese content is 0.6%, the titanium content is 0.11%, the magnesium content is 1.6%, the zinc content is 0.28%, the nickel content is 0.07%, and the iron content is 0.47%. , the balance is A00 pure aluminum;

[0104] 2. Preparation and smelting of master alloy

[0105] 1) copper aluminum alloy

[0106] Put copper and A00 pure aluminum into the crucible according to the weight ratio of 1:1, smelt, and make copper-aluminum alloy after standing;

[0107] 2) Al-Mn alloy

[0108] Add metal manganese and A00 pure aluminum into the crucible according to the weight ratio of 1:9, carry out melting, and make aluminum-manganese alloy after standing;

[0109] 3) Aluminum titanium alloy

[0110] Sponge titanium and A00 pure aluminum are added into the crucible according to the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a 2Al2 aluminum alloy casting process. Firstly, intermediate alloys including a copper-aluminum alloy, an aluminum-manganese alloy and an aluminum-titanium alloy are prepared and smelted; then pure aluminum is arranged in a crucible, the copper-aluminum alloy, the aluminum-manganese alloy and the aluminum-titanium alloy are added in batch and in sequence, and sufficient stirring while adding is carried out; magnesium metal is added into the crucible, and aluminum alloy liquid is prepared; the aluminum alloy liquid is subject to refining, slag removal and modification treatment; after sampling analysis is qualified, pouring is carried out, and crude workpieces are prepared; the crude workpieces are settled and corrected; and the crude workpieces are arranged in an aging oven to be subject to aging treatment, and a finished product is prepared through slinging treatment and machining. The 2Al2 aluminum alloy casting process has the beneficial effects that operation is convenient, the workpieces are molded through casting, raw materials can be saved, the production cost is reduced, the casting tissue density is good, the degree of finish is high, the workpiece quality is good, the size deformation is small, the finished product rate is high, and the production efficiency is high.

Description

technical field [0001] The invention relates to a 2A12 aluminum alloy casting process. Background technique [0002] 2A12 (that is, LY12 is equivalent to American Standard 2024) aluminum alloy is a high-strength duralumin. The traditional process is to use a power frequency induction furnace or a push-type resistance furnace to heat the 2A12 ingot to 480°C-495°C, and squeeze it through a hydraulic press to cool it. Extruded and heat-treated to produce qualified plates, bars, etc. Using this method to process various high-load parts and component materials wastes a lot of raw materials, and the production cost is too high, which is difficult for users to accept. Contents of the invention [0003] The present invention aims to solve the above-mentioned problems existing in the prior art, and provides a 2A12 aluminum alloy casting process that can save raw materials and reduce production costs. [0004] Technical scheme of the present invention is: [0005] A kind of 2A12 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D21/04C22C21/18C22C21/16C22C1/03
CPCB22D21/04C22C1/026C22C1/03C22C21/14C22C21/16C22C21/18
Inventor 唐文杰
Owner 喀左金牛机电设备科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com