Glass powder, positive electrode silver paste prepared therefrom and solar battery

A technology of glass powder and positive electrode, applied in the field of solar cells, can solve the problems of photoelectric conversion efficiency and pulling force contradiction

Inactive Publication Date: 2017-03-08
KANGZHUN ELECTRONICS TECH KUNSHAN +5
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, one of the main problems faced by the existing positive electrode silver paste is the contradiction between photoelectric conversion efficiency and tensile force. How to develop a solar positive electrode silver paste with excellent performance, high photoelectric conversion efficiency and high tensile force, is currently the focus of the industry's attention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass powder, positive electrode silver paste prepared therefrom and solar battery

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] A kind of preparation method of above-mentioned glass powder, it comprises the steps:

[0026] Step S1: PbO, Bi 2 o 3 , TeO 2 , SiO 2 、WO 3 , ZnO, CaO, MgO, Al 2 o 3 , Li 2 O, Na 2 O, Fe 2 o 3 , B 2 o 3 and BaO and other oxides are mixed evenly according to the predetermined ratio and added to the platinum crucible.

[0027] Step S2: Put the above-mentioned platinum crucible filled with oxides into a high-temperature sintering furnace, sinter at a temperature of 800-1200° C., and keep it warm for 0.5-2 hours to obtain molten glass.

[0028] Step S3: Quenching the molten glass to form amorphous glass particles.

[0029] Step S4: Put the above glass particles in a ball mill for ball milling to obtain glass powder with a median particle size ranging from 0.5 μm to 3 μm.

[0030] It can be understood that in the step S1, various salts or fluorides that can be decomposed into corresponding oxides can also be used instead of the oxides.

[0031] A positive elec...

Embodiment 1

[0048] In the present embodiment, glass frit is made of PbO, Bi 2 o 3 , TeO 2 , SiO 2 、WO 3 , ZnO, CaO, MgO, Al 2 o 3 , Li 2 O, Na 2 O, Fe 2 o 3 , B 2 o 3 And BaO prepared.

[0049] Among them, the mass percentage of PbO is 30%, TeO 2 The mass percentage content is 31%, Bi 2 o 3 The mass percentage content is 22%, SiO 2 The mass percentage content of ZnO is 7%, the mass percentage content of ZnO is 2%, Na 2 The mass percentage of O is 1%, Li 2 The mass percentage of O is 1.5%, Al 2 o 3 The mass percentage of CaO is 1%, the mass percentage of CaO is 0.5%, B 2 o 3 The mass percentage content is 1%, Fe 2 o 3 The mass percentage content of BaO is 0.5%, the mass percentage content of BaO is 0.5%, the mass percentage content of MgO is 0.5%, WO 3 The mass percent content is 1.5%.

Embodiment 2

[0051] In the present embodiment, glass frit is made of PbO, Bi 2 o 3 , TeO 2 , SiO 2 、WO 3 , ZnO, CaO, MgO, Al 2 o 3 , Li 2 O, Na 2 O, Fe 2 o 3 , B 2 o 3 And BaO prepared.

[0052] Among them, the mass percentage of PbO is 27%, TeO 2 The mass percentage content is 28%, Bi 2 o 3 The mass percentage content is 26%, SiO 2 The mass percentage content of ZnO is 7.5%, the mass percentage content of ZnO is 2.5%, Na 2 The mass percentage of O is 1%, Li 2 The mass percentage of O is 1.5%, Al 2 o 3 The mass percentage of CaO is 1%, the mass percentage of CaO is 0.5%, B 2 o 3 The mass percentage content is 1%, Fe 2 o 3 The mass percentage content of BaO is 0.5%, the mass percentage content of BaO is 0.5%, the mass percentage content of MgO is 0.5%, WO 3 The mass percent content is 2.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to glass powder. The glass powder contains the ingredients in percentage by mass: 20% to 60% of PbO, 10% to 50% of Bi2O3, 20% to 60% of TeO2 and 5% to 15% of SiO2. According to the glass powder, through adjusting and optimizing chemical composition, electrodes prepared from positive electrode silver paste prepared from the glass powder can have relatively high photoelectric conversion efficiency and relatively good tension property, and thus the service life of a solar battery is guaranteed. In addition, the invention further provides the positive electrode silver paste prepared from the glass powder and the solar battery prepared from the positive electrode silver paste.

Description

technical field [0001] The invention relates to a glass powder, a positive electrode silver paste prepared by using the glass powder, and a solar cell prepared by using the positive electrode silver paste. Background technique [0002] With the increasingly prominent contradiction between human beings and the environment, as well as the increasing shortage of traditional energy sources, solar energy, as a sustainable, non-polluting green new energy, has received widespread attention. The proportion of the structure will become heavier and heavier. [0003] A crystalline silicon solar cell is a solar power generation device that converts light energy into electrical energy and stores it. Conventional P-type substrate solar cells have a negative electrode on the front (illuminated surface) and a positive electrode structure on the back (backlit surface). Sunlight shines on the front of the cell to form electron-hole pairs, and the carriers are formed in the PN junction. Dire...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C12/00H01B1/16H01B1/22H01L31/0224
CPCC03C12/00H01B1/16H01B1/22H01L31/022425Y02E10/50
Inventor 张顾耀许迪张楚鑫
Owner KANGZHUN ELECTRONICS TECH KUNSHAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com