Flame-retardant thermoplastic elastic crash pad and preparation method thereof

A thermoplastic elastic and anti-vibration pad technology, which is applied in the field of anti-vibration materials, can solve the problems of poor elastic properties of TPI and cannot meet the requirements of wide use, etc., and achieve the effect of small compression set, excellent shock absorption effect and good protection

Inactive Publication Date: 2017-02-15
于桂菊
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, it is suitable for shock-absorbing rubber products, but because of the poor elastic properties of TPI, it cannot meet the requirements of its wide use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant thermoplastic elastic crash pad and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A flame-retardant thermoplastic elastic shockproof pad is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0024] 45 parts of hydrogenated styrene butadiene copolymer L606, 20 parts of polyisoprene resin, 30 parts of SIS resin, 6 parts of EPDM rubber-maleic anhydride graft, 3 parts of naphthenic rubber oil , 7 parts of flame retardant compounded with 30wt% dipentaerythritol alkane aluminum hypophosphite / polymelamine uric acid compound, 5 parts of mineral fillers composed of talcum powder and mica powder according to the weight ratio of 3:4, three ( 0.3 parts of 2,4-di-tert-butylphenyl) phosphite, and 0.6 parts of silicone powder.

Embodiment 2

[0026] A flame-retardant thermoplastic elastic shockproof pad is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0027] 50 parts of hydrogenated styrene butadiene copolymer L606, 22 parts of polyisoprene resin, 35 parts of SIS resin, 7 parts of EPDM rubber-maleic anhydride graft, 4 parts of naphthenic rubber oil , 8 parts of flame retardant compounded with 35wt% dipentaerythritol alkane-based aluminum hypophosphite / polymelamine uric acid salt, 7 parts of mineral fillers composed of talcum powder and mica powder according to the weight ratio of 3:4, three ( 0.4 parts of 2,4-di-tert-butylphenyl) phosphite, and 0.7 parts of silicone powder.

Embodiment 3

[0029] A flame-retardant thermoplastic elastic shockproof pad is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0030] 55 parts of hydrogenated styrene butadiene copolymer L606, 25 parts of polyisoprene resin, 40 parts of SIS resin, 8 parts of EPDM rubber-maleic anhydride graft, 5 parts of naphthenic rubber oil , 9 parts of flame retardant compounded with 40wt% dipentaerythritol alkane-based aluminum hypophosphite / polymelamine uric acid salt, 8 parts of mineral fillers composed of talcum powder and mica powder according to the weight ratio of 3:4, three ( 0.5 parts of 2,4-di-tert-butylphenyl) phosphite, and 0.8 parts of silicone powder.

[0031] The raw material of embodiment 1-3 is prepared according to the following preparation method

[0032] A preparation method of a flame-retardant thermoplastic elastic shockproof pad is characterized in that it specifically comprises the following steps:

[0033] (1) Carrier inte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retardant thermoplastic elastic crash pad and a preparation method thereof. The flame-retardant thermoplastic elastic crash pad is characterized by comprising the following raw materials by weight: 45 to 55 parts of hydrogenated styrene-butadiene copolymer L606, 20 to 25 parts of polyisoprene resin, 30 to 40 parts of SIS resin, 6 to 8 parts of EPDM-maleic anhydride graft, 3 to 5 parts of naphthenic rubber oil, 7 to 9 parts of a fire retardant, 5 to 8 parts of a mineral filler, 0.3 to 0.5 part of tris(2,4-di-tert-butylphenyl)phosphite and 0.6 to 0.8 part of silicone powder. According to the invention, the effective loading amount of a catalyst is easy to control; catalysis efficiency is high; good elasticity can be easier to maintain at a low temperature; and the prepared crash pad has high elasticity, permanent compression deformation and UL-94V-0-grade flame retardation effect, and is a highly damping material with low resilience.

Description

technical field [0001] The invention belongs to the technical field of shockproof materials, and in particular relates to a flame-retardant thermoplastic elastic shockproof pad and a preparation method thereof. Background technique [0002] Rubber is a relatively common shock-absorbing material. It has certain advantages due to its superior shock-absorbing performance and aging resistance. However, rubber has disadvantages such as long vulcanization cycle and difficult molding, which limit its large-scale use to a certain extent. Thermoplastic elastomers It has many advantages such as direct injection molding and recyclable utilization, so it has become a research hotspot. But at present, the main flame-retardant thermoplastic elastomer materials are halogen-containing materials, which do not conform to the environmental protection policies of many countries and are not conducive to the export of our products. [0003] Shockproof pads generally use butyl rubber. The biggest...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08L47/00C08L51/06C08L83/04C08K13/02C08K5/526C08K5/5313C08K5/3492C08F36/08C08F8/38B29B9/06B29C47/92B29C48/92
Inventor 于桂菊
Owner 于桂菊
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com