Manufacturing method of special bobbin cover paper for ultrafine chemical fiber filaments

A production method and ultra-fine technology, applied in the field of papermaking, can solve the problems of low covering power, easy thread hanging, and serious bottom penetration of the bobbin cover paper, so as to improve the characteristics of non-oil absorption and oil penetration, improve the quality of acidification, and prolong acidification the effect of time

Active Publication Date: 2017-02-08
济南欣易特种纸业有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Based on the above changes, the original tube cover paper has the following problems: 1. The colored tube cover paper is dark in color and fades seriously, causing the chemical fiber filaments near the bottom of the tube to be polluted by the color migration of the cover paper
As the bobbin storage time prolongs, the chemical fiber oil solution on the tow will be partially absorbed by the surface of the bobbin cover paper; part of it will permeate into the inner layer of the bobbin along the paper and the few fiber gaps, resulting in the bottom of the bobbin The fiber bundles of chemical fiber filaments are scattered due to the loss of the protection of the oil agent, which makes the bundling property of the superfine chemical fiber filaments not good, and it is easy to hang the filaments, and cannot be completely unwound, which seriously affects the automatic mass production of high-speed spinning machines
3. The cover paper of the bobbin tube has low covering power and serious see-through

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of special bobbin cover paper for ultrafine chemical fiber filaments
  • Manufacturing method of special bobbin cover paper for ultrafine chemical fiber filaments
  • Manufacturing method of special bobbin cover paper for ultrafine chemical fiber filaments

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A method for making a dark green bobbin cover paper specially used for superfine chemical fibers, which has the characteristics of no fading, no oil absorption, no oil penetration, good friction resistance, bright colors, strong hiding power, etc., comprising the following steps:

[0046] A. Prepare the slurry for the dark green winding base paper base paper specially used for superfine chemical fiber filaments with bright colors, strong hiding power and no fading effect, specifically:

[0047] A1, 70% softwood pulp and 30% hardwood pulp are mixed and beaten, the beating degree is 38 ° SR, and the beating concentration is 3%.

[0048] A2, 1.0% of the blue liquid organic pigment (relative to the total mass percentage of the absolute dry wood pulp), and 0.7% of the yellow liquid organic pigment (relative to the total mass percentage of the absolute dry wood pulp) are diluted with water in a stainless steel dispersion tank with stirring, The dilution concentration is 3%. ...

Embodiment 2

[0072] A method for making an orange-yellow bobbin cover paper specially used for superfine chemical fibers, which has the characteristics of no fading, no oil absorption, no oil penetration, good friction resistance, bright color, strong hiding power, etc., comprising the following steps:

[0073] A. Prepare the slurry for the base paper of the orange-yellow bobbin cover paper for ultra-fine chemical fiber filaments with bright colors, strong hiding power and non-fading effect, specifically:

[0074] A1, 80% softwood pulp and 20% hardwood pulp are mixed and beaten, the beating degree is 40°SR, and the beating concentration is 5%.

[0075] A2, 1.5% of orange liquid organic pigment (relative to the total mass percentage of absolute dry wood pulp) and 0.4% of yellow liquid organic pigment (relative to the total mass percentage of absolute dry wood pulp) are diluted with water in a stainless steel dispersion tank with stirring , the dilution concentration is 5%.

[0076] A3, 5% ...

Embodiment 3

[0099] A method for making a magenta bobbin cover paper specially used for superfine chemical fibers, which has the characteristics of no fading, no oil absorption, no oil penetration, good friction resistance, bright colors, strong hiding power, etc., comprising the following steps:

[0100] A. Prepare magenta bobbin cover paper base paper special for superfine chemical fiber filaments with non-fading, strong hiding power and bright colors, specifically:

[0101] A1, 80% softwood pulp and 20% hardwood pulp are mixed and beaten, the beating degree is 35 ° SR, and the beating concentration is 4%.

[0102] A2, 2.5% (relative to the total mass percentage of absolute dry wood pulp) of pink liquid organic pigment and 1.6% (relative to the total mass percentage of absolute dry wood pulp) of pink liquid organic pigment are added in a stainless steel dispersion tank with stirring Diluted, the diluted concentration is 4%.

[0103] A3, 4% of nano-scale silicon dioxide, white carbon bla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method of special bobbin cover paper for ultrafine chemical fiber filaments. The manufacturing method comprises: sufficiently mixing softwood pulp and hardwood pulp, a coloring material, a penetration assisting material, a covering material and a color fixing material to prepare pulp; carrying out papermaking to obtain raw paper of the bobbin cover paper; carrying out low-temperature acidification treatment on the raw paper by sulfuric acid to obtain the bobbin cover paper; after washing the acidified bobbin cover paper with water, neutralizing and plasticizing, carrying out surface modification treatment including oil prevention, abrasion resistance and the like; finally, drying, winding, cutting and packaging to obtain the bobbin cover paper. The bobbin cover paper prepared by the method has the characteristics of no fading, no oil absorption and no oil penetration, good surface wear-resisting performance, bright color and high covering capability, completely meets the requirements of users and has a good utilization effect.

Description

technical field [0001] The invention relates to a production method of bobbin cover paper wound with superfine chemical filaments, which is suitable for the chemical fiber industry, and belongs to the technical field of papermaking. Background technique [0002] In recent years, the chemical fiber industry has developed very rapidly. There are more and more types of chemical fiber filaments, and the chemical fiber filaments are becoming finer and finer. Changing from the original manual splicing to mechanized automatic splicing requires a very high tailing rate in spinning, that is to say, all the yarn at the bottom of the bobbin is required to be returned. Based on the above changes, the original tube cover paper has the following problems: 1. The colored tube cover paper is dark in color and fades seriously, causing the chemical fiber filaments near the bottom of the tube to be polluted by the color migration of the cover paper. 2. The cover paper of the bobbin is oil-abs...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/00D21D1/02D21F1/00D21H25/02
CPCD21D1/02D21F1/00D21H25/02D21H27/00
Inventor 孙翠霞殷立新孙建明柴正玲杨丽华刘亚青王毓
Owner 济南欣易特种纸业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap